Proton is Essential or Not: A Fresh Look on Pseudocapacitive Energy Storage of PANI Composites.

Protonation has been considered essential for the pseudocapacitive energy storage of polyaniline (PANI) for years, as proton doping in PANI chains not only activates electron transport pathways, but also promotes the proceeding of redox reactions. Rarely has the ability for PANI of storing energy without protonation been investigated, and it remains uncertain whether PANI has pseudocapacitive charge storage properties in an alkaline electrolyte. Here, this work first demonstrates the pseudocapacitive energy storage for PANI without protonation using a PANI/graphene composite as a model material in an alkaline electrolyte. Using in situ Raman spectroscopy coupled with electrochemical quartz crystal microbalance (EQCM) measurements, this work determines the formation of -N= group over potential on a PANI chain and demonstrates the direct contribution of OH- in the nonprotonation type of oxidation reactions. This work finds that the PANI/graphene composite in an alkaline electrolyte has excellent cycling stability with a wider operation voltage of 1 V as well as a slightly higher specific capacitance than that in an acidic electrolyte. The findings provide a new perspective on pseudocapacitive energy storage of PANI-based composites, which will influence the selection of electrolytes for PANI materials and expand their application in energy storage fields.

Pseudocapacitance-Induced Synaptic Plasticity of Tribo-Phototronic Effect Between Ionic Liquid and 2D MoS2.

Contact-induced electrification, commonly referred to as triboelectrification, is the subject of extensive investigation at liquid-solid interfaces due to its wide range of applications in electrochemistry, energy harvesting, and sensors. This study examines the triboelectric between an ionic liquid and 2D MoS2 under light illumination. Notably, when a liquid droplet slides across the MoS2 surface, an increase in the generated current and voltage is observed in the forward direction, while a decrease is observed in the reverse direction. This suggests a memory-like tribo-phototronic effect between ionic liquid and 2D MoS2 . The underlying mechanism behind this tribo-phototronic synaptic plasticity is proposed to be ion adsorption/desorption processes resulting from pseudocapacitive deionization/ionization at the liquid-MoS2  interface. This explanation is supported by the equivalent electrical circuit modeling, contact angle measurements, and electronic band diagrams. Furthermore, the influence of various factors such as velocity, step size, light wavelength and intensity, ion concentration, and bias voltage is thoroughly investigated. The artificial synaptic plasticity arising from this phenomenon exhibits significant synaptic features, including potentiation/inhibition, paired-pulse facilitation/depression, and short-term memory (STM) to long-term memory (LTM) transition. This research opens up promising avenues for the development of synaptic memory systems and intelligent sensing applications based on liquid-solid interfaces.

N-Terminalized Ti3 C2 Tx MXene for Supercapacitor with Extraordinary Pseudocapacitance Performance.

MXenes have demonstrated significant potential in electrochemical energy storage, particularly in supercapacitors, owing to their exceptional properties. The surface terminal groups of MXene play a pivotal role in pseudocapacitive mechanism. Considering the hindered electrolyte ion transport caused by -F terminal groups and the limited ion binding sites associated with -O terminal groups, this study proposes a novel strategy of replacing -F with -N terminal groups. The modulated MXene-N electrode, featuring a substantial number of -N terminal groups, demonstrates an exceptionally high gravimetric capacitance of 566 F g-1 (at a scan rate of 2 mV s-1 ) or 588 F g-1 (at a discharge rate of 1 A g-1 ) in 1 м H2 SO4 electrolyte, and the potential window is significantly increased. Furthermore, subsequent spectra analysis and density functional theory calculations are employed to investigate the mechanism associated with -N terminal groups. This work exemplifies the significance of terminal modulation in the context of electrochemical energy storage.

A Highly Robust and Conducting Ultramicroporous 3D Fe(II)-Based Metal-Organic Framework for Efficient Energy Storage.

Exploitation of metal-organic framework (MOF) materials as active electrodes for energy storage or conversion is reasonably challenging owing to their poor robustness against various acidic/basic conditions and conventionally low electric conductivity. Keeping this in perspective, herein, a 3D ultramicroporous triazolate Fe-MOF (abbreviated as Fe-MET) is judiciously employed using cheap and commercially available starting materials. Fe-MET possesses ultra-stability against various chemical environments (pH-1 to pH-14 with varied organic solvents) and is highly electrically conductive (σ = 0.19 S m-1) in one fell swoop. By taking advantage of the properties mentioned above, Fe-MET electrodes give prominence to electrochemical capacitor (EC) performance by delivering an astounding gravimetric (304 F g-1) and areal (181 mF cm-2) capacitance at 0.5 A g-1 current density with exceptionally high cycling stability. Implementation of Fe-MET as an exclusive (by not using any conductive additives) EC electrode in solid-state energy storage devices outperforms most of the reported MOF-based EC materials and even surpasses certain porous carbon and graphene materials, showcasing superior capabilities and great promise compared to various other alternatives as energy storage materials.

Supramolecular Engineering of Ti3C2Tx MXene -Perylene Diimide Hybrid Electrodes for the Pseudocapacitive Electrochemical Storage of Calcium Ions.

The rare combination of metallic conductivity and surface redox activity enables 2D MXenes as versatile charge storage hosts for the design of high-rate electrochemical energy storage devices. However, high charge density metal ions including but not limited to Ca+2 and Mg+2 pose challenges such as sluggish solid-state diffusion and also inhibiting the charge transfer across electrode-electrolyte interfaces. In this work, free-standing hybrid electrode architectures based on 2D titanium carbide-cationic perylene diimide (Ti3C2Tx@cPDI) via supramolecular self-assembly are developed. Secondary bonding interactions such as dipole-dipole and hydrogen bonding between Ti3C2Tx and cPDI are investigated by zeta potential and Fourier-transformed infrared (FTIR) spectroscopy . Ti3C2Tx@cPDI free-standing electrodes show typical volumetric capacitance up to 260 F cm-3 in Mg2+ and Ca2+ aqueous electrolytes at charging times scales from 3 minutes to a few seconds. Three-dimensional (3D) Bode maps are constructed to understand the charge storage dynamics of Ti3C2Tx@cPDI hybrid electrode in an aqueous Ca-ion electrolyte. ,Pseudocapacitance is solely contributed by the nanoscale distribution of redox-active cPDI supramolecular polymers across 2D Ti3C2Tx. This study opens avenues for the design of a wide variety of MXene@redox active organic charge hosts for high-rate pseudocapacitive energy storage devices.

Unraveling the Role of Metal Vacancy Sites and Doped Nitrogen in Enhancing Pseudocapacitance Performance of Defective MXene.

Nitrogen-doped titanium carbides (MXene) films exhibit extraordinary volumetric capacitance when high-concentration sulfuric acid electrolyte is utilized owing to the enhancement of pseudocapacitance. However, the energy storage mechanism of nitrogen-doped MXene is unclear due to the complex electrode structure and electrolyte ions' behavior. Here, based on pristine MXene (Ti3C2O2), three different MXene structures are constructed by introducing metal vacancy sites and doped nitrogen atoms, namely, defective MXene (Ti2.9C2O2), nitrogen-doped MXene (Ti3C2O1.9N0.1), and nitrogen-doped MXene with metal vacancy sites (Ti2.9C2O1.9N0.1). Then, the density functional theory (DFT)-based calculations coupled with the effective screening medium reference interaction site method (ESM-RISM) are applied to reveal the electrochemical behavior at the electrode/electrolyte interfacial area. Through analyzing the electronic structure, electrical double-layer capacitance (EDLC), and equilibrium potential of the pseudocapacitance reaction, the specific effect of structural changes on their performance can be clarified: metal vacancy sites can reduce the potential difference of gap layer (Outer Helmholtz plane) at charged state and increase the electronic capacity of Ti, which can be used to explain the high pseudocapacitance, low charge transfer resistance and high-rate capacity properties of nitrogen-doped MXene observed in experiments.

Hydrogen-Bonded Organic Framework Derived 2D N, O Co-Doped Carbon Nanobelt with Tunable Pseudocapacitive Contribution for Efficient Capacitive Deionization.

Defect engineering is recognized as an attractive method for modulating the electronic structure and physicochemical characteristics of carbon materials. Exploiting heteroatom-doped porous carbon with copious active sites has attracted great attention for capacitive deionization (CDI). However, traditional methods often rely on the utilization of additional heteroatom sources and strong corrosive activators, suffering from low doping efficiency, insufficient doping level, and potential biotoxicity. Herein, hydrogen-bonded organic frameworks (HOFs) are employed as precursors to synthesize N, O co-doped porous carbon via a simple and green reverse defect engineering strategy, achieving controllable heavy doping of heteroatoms. The N, O co-doping triggers significant pseudocapacitive contribution and the surface pore structure supports the formation of the electric double layer. Therefore, when HOF-derived N, O co-doped carbon is used as CDI electrodes, a superior salt adsorption capacity of 32.29 ± 1.42 mg g-1 and an outstanding maximum salt adsorption rate of 10.58 ± 0.46 mg g-1 min-1 at 1.6 V in 500 mg L-1 NaCl solution are achieved, which are comparable to those of state-of-the-art carbonaceous electrodes. This work exemplifies the effectiveness of the reverse nitrogen-heavy doping strategy on improving the carbon structure, shedding light on the further development of rational designed electrode materials for CDI.

Elucidating High Initial Coulombic Efficiency, Pseudocapacitive Kinetics and Charge Storage Mechanism of Antiperovskite Carbide Ni3ZnC0.7@rGO Anode for Fast Sodium Storage in Ether Electrolyte.

To explore novel electrode materials with in-depth elucidation of initial coulombic efficiency (ICE), kinetics, and charge storage mechanisms is of great challenge for Na-ion storage. Herein, a novel 3D antiperovskite carbide Ni3ZnC0.7@rGO anode coupled with ether-based electrolyte is reported for fast Na-ion storage, exhibiting superior performance than ester-based electrolyte. Electrochemical tests and density functional theory (DFT) calculations show that Ni3ZnC0.7@rGO anode with ether-based electrolyte can promote charge/ion transport and lower Na+ diffusion energy barrier, thereby improving ICE, reversible capacity, rate, and cycling performance. Cross-sectional-morphology and depth profiling surface chemistry demonstrate that not only a thinner and more homogeneous reaction interface layer with less side effects but also a superior solid electrolyte interface (SEI) film with a high proportion of inorganic components are formed in the ether-based electrolyte, which accelerates Na+ transport and is the significant reason for the improvement of ICE and other electrochemical properties. Meanwhile, electrochemical and ex situ measurements have revealed conversion, alloying, and co-intercalation hybrid mechanisms of the Ni3ZnC0.7@rGO anode based on ether electrolyte. Interestingly, the Na-ion capacitors (SICs) designed by pairing with activated carbon (AC) cathode exhibit favorable electrochemical performance. Overall, this work provides deep insights on developing advanced materials for fast Na-ion storage.

Ultrafast and Durable Sodium-Ion Storage of Pseudocapacitive VN@C Hybrid Nanorods from Metal-Organic Framework.

Vanadium nitride (VN) is a promising electrode material for sodium-ion storage due to its multivalent states and high electrical conductivity. However, its electrochemical performance has not been fully explored and the storage mechanism remains to be clarified up to date. Here, the possibility of VN/carbon hybrid nanorods synthesized from a metal-organic framework for ultrafast and durable sodium-ion storage is demonstrated. The VN/carbon electrode delivers a high specific capacity (352 mA h g-1), fast-charging capability (within 47.5 s), and ultralong cycling stability (10 000 cycles) for sodium-ion storage. In situ XRD characterization and density functional theory (DFT) calculations reveal that surface-redox reactions at vanadium sites are the dominant sodium-ion storage mechanism. An energy-power balanced hybrid capacitor device is verified by assembling the VN/carbon anode and active carbon cathode, and it shows a maximum energy density of 103 Wh kg-1 at a power density of 113 W kg-1.

Effect of annealing temperature on structural and electrochemical behaviour on MgFe2O4as electrode material in neutral aqueous electrolyte for supercapacitors.

Binary metal oxides possess unique structures and multiple oxidation states, making them highly valuable in electrochemical analysis. This study aims to determine the effect of annealing temperature on the electrochemical properties of magnesium ferrite when used as an electrode material in a neutral aqueous electrolyte. We utilized the sol-gel technique to synthesize the material and annealed it at various temperatures. Our analysis of the material using different characterization techniques reveals significant changes in its structural and electrochemical properties. We found that the material exhibited a range of phases, and higher annealing temperatures led to improved electrochemical properties. The electrochemical measurements showed reversible and redox pseudo-capacitance behavior, with the material annealed at 500 °C exhibiting the highest specific capacitance of 117 F g-1at a current density of 0.5 A g-1. Capacitive and diffusion-controlled processes govern the total charge storage mechanism, and their contribution changes significantly as the annealing temperature varies. The capacitance retention of 500 °C annealed sample was 58% and it remained stable. This work establishes a correlation between annealing temperature on structural, morphological, and electrochemical behavior, thereby opening up avenues for tailoring them effectively. These findings can be useful in the development of future electrode materials for electrochemical applications.

Selective Capacitive Recovery of Rare-Earth Ions from Wastewater over Phosphorus-Modified TiO2 Cathodes via an Electro-Adsorption Process.

Large amounts of wastewater containing low-concentration (<10 ppm) rare-earth ions (REIs) are discharged annually in China's rare-earth mining and processing industry, resulting in severe environmental pollution and economic losses. Hence, achieving efficient selective recovery of low-concentration REIs from REIs-containing wastewater is essential for environmental protection and resource recovery. In this study, a pseudocapacitance system was designed for highly efficient capacitive selective recovery of REIs from wastewater using the titanium dioxide/P/C (TiO2/P/C) composite electrode, which exhibited over 99% recovery efficiency for REIs, such as Eu3+, Dy3+, Tb3+, and Lu3+ in mixed solution. This system maintained high efficiency and more than 90 times the enrichment concentration of REIs even after 100 cycles. Ti4+ of TiO2 was reduced to Ti3+ of Ti3O5 under forward voltage in the system, which trapped the electrons of phosphorus site and caused it to be oxidized to phosphate with a strong affinity for REIs, thus improving the selectivity of REIs. Under reverse voltage, Ti3O5 was oxidized to TiO2, which transferred electrons to phosphate and transformed to the phosphorus site, resulting in the desorption and enrichment of REIs and the regeneration of the electrode. This study provides a promising method for the efficient recovery of REIs from wastewater.

Electrochemical Capacitance Traces with Interlayer Spacing in Two-dimensional Conductive Metal-Organic Frameworks.

Electrically conductive metal-organic frameworks (MOFs) are promising candidates for electrochemical capacitors (EC) for fast energy storage due to their high specific surface areas and potential for redox activity. To maximize energy density, traditional inorganic pseudocapacitors have utilized faradaic processes in addition to double-layer capacitance. Although conductive MOFs are usually comprised of redox active ligands which allow faradaic reactions upon electrochemical polarization, systematic studies providing deeper understanding of the charge storage processes and structure-function relationships have been scarce. Here, we investigate the charge storage mechanisms of a series of triazatruxene-based 2D layered conductive MOFs with variable alkyl functional groups, Ni3(HIR3-TAT)2 (TAT=triazatruxene; R=H, Et, n-Bu, n-Pent). Functionalization of the triazatruxene core allows for systematic variation of structural parameters while maintaining in-plane conjugation between ligands and metals. Specifically, R groups modulate interlayer spacing, which in turn shifts the charge storage mechanism from double-layer capacitance towards pseudocapacitance, leading to an increase in molar specific capacitance from Ni3(HIH3-TAT)2 to Ni3(HIBu3-TAT)2. Partial exfoliation of Ni3(HIBu3-TAT)2 renders redox active ligand moieties more accessible, and thus increases the dominance of faradaic processes. Our strategy of controlling charge storage mechanism through tuning the accessibility of redox-active sites may motivate further design and engineering of electrode materials for EC.

Role of Surface Terminations for Charge Storage of Ti3C2Tx MXene Electrodes in Aqueous Acidic Electrolyte.

In this study, we used 2-Dimmensionnal Ti3C2 MXene as model materials to understand how the surface groups affect their electrochemical performance. By adjusting the nature of the surface terminations (Cl-, N/O-, and O-) of Ti3C2 MXene through a molten salt approach, we could change the spacing between MXene layers and the level of water confinement, resulting in significant modifications of the electrochemical performance in acidic electrolyte. Using a combination of techniques including in-operando X-ray diffraction and electrochemical quartz crystal microbalance (EQCM) techniques, we found that the presence of confined water results in a drastic transition from an almost electrochemically inactive behavior for Cl-terminated Ti3C2 to an ideally fast pseudocapacitive signature for N,O-terminated Ti3C2 MXene. This experimental work not only demonstrates the strong connection between surface terminations and confined water but also reveals the importance of confined water on the charge storage mechanism and the reaction kinetics in MXene.

Dual Molecules Cooperatively Confined In-Between Edge-oxygen-rich Graphene Sheets as Ultrahigh Rate and Stable Electrodes for Supercapacitors.

Noncovalent modification of carbon materials with redox-active organic molecules has been considered as an effective strategy to improve the electrochemical performance of supercapacitors. However, their low loading mass, slow electron transfer rate, and easy dissolution into the electrolyte greatly limit further practical applications. Herein, this work reports dual molecules (1,5-dihydroxyanthraquinone (DHAQ) and 2,6-diamino anthraquinone (DAQ)) cooperatively confined in-between edge-oxygen-rich graphene sheets as high-performance electrodes for supercapacitors. Cooperative electrostatic-interaction on the edge-oxygen sites and π-π interaction in-between graphene sheets lead to the increased loading mass and structural stability of dual molecules. Moreover, the electron tunneling paths constructed between edge-oxygen groups and dual molecules can effectively boost the electron transfer rate and redox reaction kinetics, especially at ultrahigh current densities. As a result, the as-obtained electrode exhibits a high capacitance of 507 F g-1 at 0.5 A g-1 , and an unprecedented rate capability (203 F g-1 at 200 A g-1 ). Moreover, the assembled symmetrical supercapacitor achieves a high energy density of 17.1 Wh kg-1 and an ultrahigh power density of 140 kW kg-1 , as well as remarkable stability with a retention of 86% after 50 000 cycles. This work may open a new avenue for the efficient utilization of organic materials in energy storage and conversion.

Redox Electrolytes-Assisting Aqueous Zn-Based Batteries by Pseudocapacitive Multiple Perovskite Fluorides Cathode and Charge Storage Mechanisms.

Aqueous Zn-based batteries (AZBs) have attracted intensive attention. However, to explore advanced cathode materials with in-depth elucidation of their charge storage mechanisms, improve energy storage capacity, and construct novel cell systems remain a great challenge. Herein, a new pseudocapacitive multiple perovskite fluorides (ABF3 ) cathode is designed, represented by KMF-(IV, V, and VI; M = NiCoMnZn/-Mg/-MgFe), and constructed Zn//KMF-(IV, V, and VI) AZBs and their flexible devices. Ex situ tests have revealed a typical bulk phase conversion mechanism of KMF-VI electrode for charge storage in alkaline media dominated by redox-active Ni/Co/Mn species, with transformation of ABF3 nanocrystals into amorphous metal oxide/(oxy)hydroxide nanosheets. By employing single or bipolar redox electrolyte strategies of 20 mm [Fe(CN)6 ]3- or/and 10 mm SO3 2- /Cu[(NH3 )4 ]2+ acting on KMF-(IV, V, and VI) cathode and Zn anode, the AZBs show an improved energy storage owing to additional capacity contribution of redox electrolytes. The as-designed Zn//polyvinyl alcohol (PVA)-KOH-K3 [Fe(CN)6 ]//KMF-(IV, V, and VI) redox gel electrolytes-assisting flexible AZBs (RGE-FAZBs) exhibit remarkable performance under different bending angles because of slight dissolution corrosion of zinc anode compared with liquid electrolytes. Overall, the work demonstrates the novel idea of conversion-type multiple ABF3 cathode for redox electrolytes-assisting AZBs (RE-AZBs) and their flexible systems, showing great significance on electrochemical energy storage.

Conformal Coverage of ZnO Nanowire Arrays by ZnMnO3 : Room-temperature Photodeposition from Aqueous Solution.

Compositionally and structurally complex semiconductor oxide nanostructures gain importance in many energy-related applications. Simple and robust synthesis routes ideally complying with the principles of modern green chemistry are therefore urgently needed. Here we report on the one-step, room-temperature synthesis of a crystalline-amorphous biphasic ternary metal oxide at the ZnO surface using aqueous precursor solutions. More specifically, conformal and porous ZnMnO3 shells are photodeposited from KMnO4 solution onto immobilized ZnO nanowires acting not only as the substrate but also as the Zn precursor. This water-based, low temperature process yields ZnMnO3 /ZnO composite electrodes featuring in 1 M Na2 SO4 aqueous solution capacitance values of 80-160 F g-1 (as referred to the total mass of the porous film i. e. the electroactive ZnMnO3 phase and the ZnO nanowire array). Our results highlight the suitability of photodeposition as a simple and green route towards complex functional materials.

Controlling phase transformation of La/Ni oxides by switching annealing conditions and their resultant pseudocapacitive behaviour.

Annealing step is a critical step in the hydrothermal assisted synthesis of La/Ni oxides such as LaNiO3-δ(LNOA) and La2NiO4+δ(LNON). In the current study, we have discovered the interlink between the atmosphere and temperature conditions which dictate the product formed. La/Ni nitrate precursors were subjected to a hydrothermal synthesis followed by an annealing step at appropriate temperature and varying atmosphere resulting in the synthesis of the corresponding oxides. The annealing temperature was varied in the range between 650 °C and 800 °C and also the annealing was carried out either in pure N2atmosphere or air. From the x-ray diffraction analysis, it was inferred that annealing in air invariably resulted in the rhombohedral LaNiO3(LNOA) perovskite phase, while annealing in N2atmosphere resulted in an orthorhombic Ruddlesden-Popper phase La2NiO4(LNON), a layered oxide containing traces of NiO phase. Typically, iodometric titrations substantiate the presence of Ni (III) which further can be correlated to the presence of oxygen vacancies (δ). Iodometric test results demarcated the difference between the two phases with absolutely minimal I2liberated from the LNON samples proving that negligible amount of Ni (III) was present in LNON Scanning electron microscopy (SEM) images showed an agglomeration of particles annealed at higher temperatures irrespective of the atmosphere. Temperature dependent oxygen non-stoichiometry (Δδ) was analyzed through thermogravimetric analysis, wherein Δδwas inversely proportional to the annealing temperature for all of the LNOA samples. Considering that largeδvalues favor pseudocapacitive behaviour, it was observed LNOA oxides showed excellent pseudocapacitive behaviour compared to the LNON oxides. Dunn deconvolution of the cyclic voltammograms of LNOA 800 °C at 5 m Vs-1indicated that diffusive contribution (66%) was predominant over capacitive contributions. The LNOA sample annealed at 800 °C displayed the highest specific capacitance of 100.3 F g-1at 1 A g-1current density.

Preparation of Carbon Dots@r-GO Nanocomposite with an Enhanced Pseudo-Capacitance.

Carbon materials with pseudocapacitive performance have attracted emerging interest in the energy storage and conversion field. Reduced graphene oxide (r-GO) with superior conductivity and electrochemical stability has been extensively investigated as an efficient capacitive electrode material. In this study, three-dimensional carbon dots (CDs)@r-GO hydrogel electrode was successfully in situ prepared by the one-pot method, where the CDs play a critical role in serving as both reduction agent and electrochemical active sites. With prolonged reaction time, the oxygen content of the CDs@r-GO nanocomposite material could be effectively reduced to ensure better electric conductivity, and the nitrogen content, which provides pseudocapacitance, was gradually increased. The representative two pairs of fast and reversible current peaks appeared in cyclic voltammetry curves, with around three times higher specific capacitance of CDs@r-GO hydrogel electrode (290 F g-1 at the current density of 1 A g-1 in 1 M H2SO4 electrolyte). This simple and mild approach is promising and it is believed it will shed more light on the preparation of high-efficiency and high-performance energy storage materials based on functional reductive CDs.

Phosphorus Doping Strategy-Induced Synergistic Modification of Interlayer Structure and Chemical State in Ti3C2Tx toward Enhancing Capacitance.

Heteroatom doping is considered an effective method to substantially improve the electrochemical performance of Ti3C2Tx MXene for supercapacitors. Herein, a facile and controllable strategy, which combines heat treatment with phosphorous (P) doping by using sodium phosphinate (NaH2PO2) as a phosphorus source, is used to modify Ti3C2Tx. The intercalated ions from NaH2PO2 act as "pillars" to expand the interlayer space of MXene, which is conducive to electrolyte ion diffusion. On the other hand, P doping tailors the surface electronic state of MXene, optimizing electronic conductivity and reducing the free energy of H+ diffusion on the MXene surface. Meanwhile, P sites with lower electronegativity owning good electron donor characteristics are easy to share electrons with H+, which is beneficial to charge storage. Moreover, the adopted heat treatment replaces -F terminations with O-containing groups, which enhances the hydrophilicity and provides sufficient active sites. The change in surface functional groups increases the content of high valence-stated Ti with a high electrochemical activity that can accommodate more electrons during discharge. Synergistic modification of interlayer structure and chemical state improves the possibility of Ti3C2Tx for accommodating more H+ ions. Consequently, the modified electrode delivers a specific capacitance of 510 F g-1 at 2 mV s-1, and a capacitance retention of 90.2% at 20 A g-1 after 10,000 cycles. The work provides a coordinated strategy for the rational design of high-capacitance Ti3C2Tx MXene electrodes.

Enhancement of Electrocatalytic and Pseudocapacitive Properties as a Function of Structural Order in A2Fe2O5 (A = Sr, Ba).

Significant enhancements of electrocatalytic activities for both half-reactions of water-electrolysis, i.e., oxygen evolution reaction (OER) and hydrogen evolution reaction (HER), as well as pseudocapacitive charge-storage properties are demonstrated upon changing the structural order in a perovskite-type system. The structural change is prompted by the increase in the ionic radius of the A-site ion in A2Fe2O5. The structure of Sr2Fe2O5 consists of alternating layers of FeO6 octahedra and FeO4 tetrahedra, whereas Ba2Fe2O5 comprises seven different coordination geometries for Fe. We note that the catalytically active metal, i.e., iron, and the oxygen stoichiometry are the same for both materials. Nevertheless, the change in the structural order results in significantly greater electrocatalytic activity of Ba2Fe2O5, manifested in smaller overpotentials, smaller charge-transfer resistance, greater electrocatalytic current, and faster reaction kinetics. In addition, this material shows significantly enhanced pseudocapacitive properties, with greater specific capacitance and energy density compared to Sr2Fe2O5. These findings indicate the important role of structural order in directing the electrochemical properties.