[The antibacterial properties of Ca and Zn-containing coatings prepared with micro-arc oxidation].
Shanghai Kou Qiang Yi Xue
; 21(3): 266-9, 2012 Jun.
Article
en Zh
| MEDLINE
| ID: mdl-22885484
ABSTRACT
PURPOSE:
To prepare Ca and Zn-containing coatings using micro-arc oxidation on pure titanium surface and to investigate the coatings effect on S.mutans adhesion and morphology.METHODS:
Five groups including low Ca-containing (L-Ca), high Ca-containing (H-Ca), low Zn-containing (L-Zn), medium Zn-containing (M-Zn), high Zn-containing (H-Zn) were prepared with micro-arc oxidation on titanium surface and machined commercial pure titanium (CP) was used as control group. Antibacterial properties of S.mutans on samples surface were appraised by the paster method and the change of bacteria was observed by SEM. SPSS 13.0 software package was used for all statistical analysis.RESULTS:
The results showed that L-Ca and H-Ca groups had no significant difference in antibacterial property(P>0.05);Zn-containing groups had distinct antibacterial effect(P<0.01) compared with CP group,and there was significant difference between L-Zn and H-Zn group (P<0.05). Meanwhile,Zn-containing groups could affect adhesion and morphology of S.mutans by SEM.CONCLUSIONS:
Zn-containing coating prepared with micro-arc oxidation can effectively influence S.mutans adhesion and morphology, which shows better antibacterial effect with the increase of zinc content.
Buscar en Google
Banco de datos:
MEDLINE
Asunto principal:
Materiales Biocompatibles Revestidos
/
Antibacterianos
Límite:
Humans
Idioma:
Zh
Revista:
Shanghai Kou Qiang Yi Xue
Asunto de la revista:
ODONTOLOGIA
Año:
2012
Tipo del documento:
Article
País de afiliación:
China