Multiple emission bands NIR-persistent luminescence mSiO2@Zn0.6Ca0.4Ga2O4:Cr3+,Yb3+ nanoparticles for biological applications.
J Mater Chem B
; 9(4): 1131-1137, 2021 01 28.
Article
en En
| MEDLINE
| ID: mdl-33432961
ABSTRACT
Persistent luminescence nanoparticles (PLNPs) emitting in the NIR window (700-1700 nm) have shown great promise in the field of fluorescence imaging due to their unique properties, including the absence of in situ excitation and low optical scattering in tissues. However, they are still facing some challenges, such as irregular shape, wide size distribution and poor persistent luminescence performance. Here, we report a facile mesoporous template method for synthesizing mSiO2@Zn0.6Ca0.4Ga2O4Cr3+,Yb3+ (mSiO2@ZCGO) persistent luminescent nanoparticles, which show a regular morphology and a size of about 69 nm. In addition, these nanocrystals exhibit persistent luminescence in multi-NIR windows, the first infrared window (â¼696 nm of Cr3+ emission) and second infrared window (â¼1000 nm of Yb3+ emission). Under illumination of a 254 nm UV lamp for 10 min, the persistent time of Cr3+ ions and Yb3+ ions lasted more than 120 min and 10 min, respectively. In particular, the NIR persistent emission of mSiO2@ZCGO could be stimulated by soft X-ray, which is beneficial to long-term imaging in deep tissues. The optical penetration length of Yb3+ ions persistent luminescence was evaluated to be 2.8 mm. These results demonstrate the great promise of mSiO2@ZCGO for deep-tissue bio-imaging.
Texto completo:
1
Banco de datos:
MEDLINE
Asunto principal:
Luminiscencia
/
Nanopartículas
/
Imagen Óptica
Idioma:
En
Revista:
J Mater Chem B
Año:
2021
Tipo del documento:
Article
País de afiliación:
China