Organo-Mediated Ring-Opening Polymerization of Ethylene Brassylate from Cellulose Nanofibrils in Reactive Extrusion.

Ethylene brassylate is a renewable macrolactone from castor oil that can be polymerized via ring-opening polymerization (ROP) to obtain a fully biosourced biodegradable polyester. ROP mediated by organometallic catalysts leads to high molar mass poly(ethylene brassylate) (PEB). However, the use of metal-free organocatalysis has several advantages, such as the reduction of toxic and expensive metals. In this work, a novel cellulose nanofibril (CNF)/PEB nanocomposite fabrication process by organocatalysis and reactive extrusion (REx) is disclosed. Here, ROP was carried out via solvent-free REx in the presence of CNFs using organic 1,5,7-triazabicyclo[4.4.0]dec-5-ene as a catalyst. Neat or lactate-esterified CNFs (LACNF) were used as initiators to investigate the effect of surface topochemistry on the in situ polymerization and the properties of the nanocomposites. A molar mass of 9 kDa was achieved in the presence of both unmodified and LACNFs with high monomer conversion (>98%) after 30 min reaction in a microcompounder at 130 °C. Tensile analysis showed that both nanofibril types reinforce the matrix and increase its elasticity due to the efficient dispersion obtained through the grafting from polymerization achieved during the REx. Mechanical recycling of the neat polymer and the nanocomposites was proven as a circular solution for the materials' end-of-life and showed that lactate moieties induced some degradation.

Interface interactions driven antioxidant properties in olive leaf extract/cellulose nanocrystals/poly(butylene adipate-co-terephthalate) biomaterials.

Functional packaging represents a new frontier for research on food packaging materials. In this context, adding antioxidant properties to packaging films is of interest. In this study, poly(butylene adipate-co-terephthalate) (PBAT) and olive leaf extract (OLE) have been melt-compounded to obtain novel biomaterials suitable for applications which would benefit from the antioxidant activity. The effect of cellulose nanocrystals (CNC) on the PBAT/OLE system was investigated, considering the interface interactions between PBAT/OLE and OLE/CNC. The biomaterials' physical and antioxidant properties were characterized. Morphological analysis corroborates the full miscibility between OLE and PBAT and that OLE favours CNC dispersion into the polymer matrix. Tensile tests show a stable plasticizer effect of OLE for a month in line with good interface PBAT/OLE interactions. Simulant food tests indicate a delay of OLE release from the 20 wt% OLE-based materials. Antioxidant activity tests prove the antioxidant effect of OLE depending on the released polyphenols, prolonged in the system at 20 wt% of OLE. Fluorescence spectroscopy demonstrates the nature of the non-covalent PBAT/OLE interphase interactions in π-π stacking bonds. The presence of CNC in the biomaterials leads to strong hydrogen bonding interactions between CNC and OLE, accelerating OLE released from the PBAT matrix.

Tailoring Nanocellulose-Cellulose Triacetate Interfaces by Varying the Surface Grafting Density of Poly(ethylene glycol).

Careful design of the structures of interfaces between nanofillers and polymer matrices can significantly improve the mechanical and thermal properties of the overall nanocomposites. Here, we investigate how the grafting density on the surface of nanocelluloses influences the properties of nanocellulose/cellulose triacetate (CTA) composites. The surface of nanocellulose, which was prepared by 2,2,6,6-tetramethylpiperidine-1-oxyl oxidation, was modified with long poly(ethylene glycol) (PEG) chains at different grafting densities. The PEG-grafted nanocelluloses were homogeneously embedded in CTA matrices. The mechanical and thermal properties of the nanocomposites were characterized. Increasing the grafting density caused the soft PEG chains to form denser and thicker layers around the rigid nanocelluloses. The PEG layers were not completely miscible with the CTA matrix. This structure considerably enhanced the energy dissipation by allowing sliding at the interface, which increased the toughness of the nanocomposites. The thermal and mechanical properties of the composites could be tailored by controlling the grafting density. These findings provide a deeper understanding about interfacial design for nanocellulose-based composite materials.