Biodegradable ferroelectric molecular crystal with large piezoelectric response.

Transient implantable piezoelectric materials are desirable for biosensing, drug delivery, tissue regeneration, and antimicrobial and tumor therapy. For use in the human body, they must show flexibility, biocompatibility, and biodegradability. These requirements are challenging for conventional inorganic piezoelectric oxides and piezoelectric polymers. We discovered high piezoelectricity in a molecular crystal HOCH2(CF2)3CH2OH [2,2,3,3,4,4-hexafluoropentane-1,5-diol (HFPD)] with a large piezoelectric coefficient d33 of ~138 picocoulombs per newton and piezoelectric voltage constant g33 of ~2450 × 10-3 volt-meters per newton under no poling conditions, which also exhibits good biocompatibility toward biological cells and desirable biodegradation and biosafety in physiological environments. HFPD can be composite with polyvinyl alcohol to form flexible piezoelectric films with a d33 of 34.3 picocoulombs per newton. Our material demonstrates the ability for molecular crystals to have attractive piezoelectric properties and should be of interest for applications in transient implantable electromechanical devices.

A Poling-Free Supramolecular Crown Ether Compound with Large Piezoelectricity.

Supramolecular host-guest ferroelectrics based on solution processing are highly desirable because they are generally created with intrinsic piezoelectricity/ferroelectricity and do not need further poling. Poly(vinylidene fluoride) (PVDF) in the electric-active beta phase after stretching/annealing still shows no piezoelectric response unless poled. Although many supramolecular host-guest ferroelectrics have been discovered, their piezoelectricity is relatively small. Based on H/F substitution, we reported a supramolecular host-guest compound [(CF3-C6H4-NH3)(18-crown-6)][TFSA] (CF3-C6H4-NH3 = 4-trifluoromethylanilinium, TFSA = bis(trifluoromethanesulfonyl)ammonium) with a remarkable piezoelectric response of 42 pC/N under no poling condition. The introduction of F atoms increases phase transition temperature, polar axes, second harmonic generation (SHG) intensity, and piezoelectric coefficient d33. To our knowledge, such a large piezoelectric performance of [(CF3-C6H4-NH3)(18-crown-6)][TFSA] makes its d33, piezoelectric voltage coefficient g33, and mechanical quality factor Qm the highest among the reported supramolecular host-guest ferroelectric compounds and even larger than the values of PVDF. This work provides inspiration for optimizing piezoelectricity on molecular materials.