Tissue Bioengineering with Fibrin Scaffolds and Deproteinized Bone Matrix Associated or Not with the Transoperative Laser Photobiomodulation Protocol.

Extending the range of use of the heterologous fibrin biopolymer, this pre-clinical study showed a new proportionality of its components directed to the formation of scaffold with a lower density of the resulting mesh to facilitate the infiltration of bone cells, and combined with therapy by laser photobiomodulation, in order to accelerate the repair process and decrease the morphofunctional recovery time. Thus, a transoperative protocol of laser photobiomodulation (L) was evaluated in critical bone defects filled with deproteinized bovine bone particles (P) associated with heterologous fibrin biopolymer (HF). The groups were: BCL (blood clot + laser); HF; HFL; PHF (P+HF); PHFL (P+HF+L). Microtomographically, bone volume (BV) at 14 days, was higher in the PHF and PHFL groups (10.45 ± 3.31 mm3 and 9.94 ± 1.51 mm3), significantly increasing in the BCL, HFL and PHFL groups. Histologically, in all experimental groups, the defects were not reestablished either in the external cortical bone or in the epidural, occurring only in partial bone repair. At 42 days, the bone area (BA) increased in all groups, being significantly higher in the laser-treated groups. The quantification of bone collagen fibers showed that the percentage of collagen fibers in the bone tissue was similar between the groups for each experimental period, but significantly higher at 42 days (35.71 ± 6.89%) compared to 14 days (18.94 ± 6.86%). It can be concluded that the results of the present study denote potential effects of laser radiation capable of inducing functional bone regeneration, through the synergistic combination of biomaterials and the new ratio of heterologous fibrin biopolymer components (1:1:1) was able to make the resulting fibrin mesh less dense and susceptible to cellular permeability. Thus, the best fibrinogen concentration should be evaluated to find the ideal heterologous fibrin scaffold.

In vitro and in vivo assessment of CaP materials for bone regenerative therapy. The role of multinucleated giant cells/osteoclasts in bone regeneration.

In this work, bone formation/remodeling/maturation was correlated with the presence of multinucleated giant cells (MGCs)/osteoclasts (tartrate-resistant acid phosphatase [TRAP]-positive cells) on the surface of beta-tricalcium phosphate (ß-TCP), sintered deproteinized bovine bone (sDBB), and carbonated deproteinized bovine bone (cDBB) using a maxillary sinus augmentation (MSA) in a New Zealand rabbit model. Microtomographic, histomorphometric, and immunolabeling for TRAP-cells analyses were made at 15, 30, and 60 days after surgery. In all treatments, a faster bone formation/remodeling/maturation and TRAP-positive cells activity occurred in the osteotomy region of the MSA than in the middle and submucosa regions. In the ß-TCP, the granules were rapidly reabsorbed by TRAP-positive cells and replaced by bone tissue. ß-TCP enabled quick bone regeneration/remodeling and full bone and marrow restoration until 60 days, but with a significant reduction in MSA volume. In cDBB and sDBB, the quantity of TRAP-positive cells was smaller than in ß-TCP, and these cells were associated with granule surface preparation for osteoblast-mediated bone formation. After 30 days, more than 80% of granule surfaces were surrounded and integrated by bone tissue without signs of degradation, preserving the MSA volume. Overall, the materials tested in a standardized preclinical model led to different bone formation/remodeling/maturation within the same repair process influenced by different microenvironments and MGCs/osteoclasts. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 108B:282-297, 2020.