Recycling thermally deactivated asbestos cement in mortar: A possible route towards a rapid conclusion of the "asbestos problem".

The "asbestos problem" arises from the fact that asbestos is still abundant in many buildings and represents a hazard for human health. Current strategies adopted by law aiming at mitigating this hazard are far from being ideal. A smarter solution would be an energy sustainable detoxification treatment followed by recycling. If adopted, it would preserve the environment from pollution, natural resources from depletion and human health from hazard. Asbestos-cement slates were thermally deactivated through a sustainable process and reused in mortar for plaster applications. We found that the addition up to 7 wt% of the deactivated product does not affect significantly the water demand; does not affect thixotropy, stickiness and spreadability of the plastic mixture; slightly increases the strength of the mortar; does not compromise mechanical properties after aging. Considering the huge amount of traditional mortar employed worldwide, a rapid end of the "asbestos problem" is envisaged.

Epoxy Resins for Flooring Applications, an Optimal Host for Recycling Deactivated Cement Asbestos.

Cement asbestos slates, commonly known as Eternit® and still abundant in private and public buildings, were deactivated through a thermal process. The resulting deactivated cement asbestos powder (DCAP), a mixture of Ca-Mg-Al silicates and glass, was compounded with Pavatekno Gold 200 (PT) and Pavafloor H200/E (PF), two different epoxy resins (bisphenol A epichlorohydrin) for flooring applications. The addition of the DCAP filler to the PF samples causes a slight but acceptable decrease in the relevant mechanical properties (compressive, tensile, and flexural strengths) upon increasing DCAP content. The addition of the DCAP filler to pure epoxy (PT resin) causes a slight decrease in the tensile and flexural strengths with increasing DCAP content, while the compressive strength is almost unaffected, and the Shore hardness increases. The main mechanical properties of the PT samples are significantly better than those of the filler-bearing sample of normal production. Overall, these results suggest that DCAP can be advantageously used as filler in addition to, or in substitution for, commercial barite. In particular, the sample with 20 wt% of DCAP is the best performing in terms of compressive, tensile, and flexural strengths, whereas the sample with 30 wt% of DCAP shows the highest Shore hardness, which is an important property to be considered in flooring applications.

Surface and bulk modifications of amphibole asbestos in mimicked gamble's solution at acidic PH.

This study aimed at investigating the surface modifications occurring on amphibole asbestos (crocidolite and tremolite) during leaching in a mimicked Gamble's solution at pH of 4.5 and T = 37 °C, from 1 h up to 720 h. Results showed that the fibre dissolution starts with the release of cations prevalently allocated at the various M- and (eventually) A-sites of the amphibole structure (incongruent dissolution). The amount of released silicon, normalized to fibre surface area, highlighted a leaching faster for the crocidolite sample, about twenty times higher than that of tremolite. Besides, the fast alteration of crocidolite promotes the occurrence of Fe centres in proximity of the fibre surface, or possibly even exposed, particularly in the form of Fe(II), of which the bulk is enriched with respect to the oxidized surface. Conversely, for tremolite fibres the very slow fibre dissolution prevents the underlying cations of the bulk to be exposed on the mineral surface, and the iron oxidation, faster than the leaching process, significantly depletes the surface Fe(II) centres initially present. Results of this work may contribute to unravel possible correlations between surface properties of amphibole asbestos and its long-term toxicity.