RESUMO
Nano-graphene materials have improved many thermal properties based on polymer systems. The additive polymers' thermal insulation cannot be significantly increased for use as a reinforcement in multifunctional thermally insulating polymer foam. Herein, we present the development of far-infrared emissivity and antistatic properties using multifunctional nano-graphene polyester fibers. Nano-graphene far-infrared thermal insulation polyester was synthesized with 2% nano-graphene and dispersant polypropylene wax-maleic anhydride (PP wax-MA) using the Taguchi method combined with grey relational analysis (GRA) to improve the thermal properties and the performance of the polymer composite. The thermogravimetric analysis (TGA) shows that the pyrolysis temperature of spinning-grade polyester was increased when the nano-graphene powder was added to the polyester. The differential scanning calorimeter (DSC) analysis confirmed the modification of polyester by nano-graphene, showing the effect of the nucleating agent, which ultimately improved the performance of the polyester. The physical properties of the optimized polyester fibers were improved with a yarn count of 76.5 d, tensile strength of 3.3 g/d, and an elongation at break increased from 23.5% to 26.7% compared with unmodified polymer yarn. These far-infrared emission rates increased from 78% to 83%, whereas the far-infrared temperature increased from 4.0 °C to 22 °C, and the surface resistance increased to 108 Ω. The performance of the optimized modified polyester yarn is far better than single-polypropylene-grafted maleic anhydride yarn. The performance of optimized modified polyester yarn, further confirmed using grey correlation analysis (GRA), can improve the yarns' mechanical properties and far-infrared functions. Our findings provide an alternative route for developing nano-graphene polyester fabrics suitable for the fabric industry.
RESUMO
This investigation aims at exploring the catalytic oxidation activity of iron-embedded activated carbon (FeAC) and the application for the degradation of phenol in the wet hydrogen peroxide catalytic oxidation (WHPCO). FeAC catalysts were prepared by pre-impregnating iron in coconut shell with various iron loadings in the range of 27.5 to 46.5% before they were activated. The FeAC catalysts were characterised by measuring their surface area, pore distribution, functional groups on the surface, and X-ray diffraction patterns. The effects of iron loading strongly inhibited the pore development of the catalyst but benefited the oxidation activity in WHPCO. It was found that the complete conversion of phenol was observed with all FeAC catalysts in oxidation. High level of chemical oxygen demand (COD) abatement can be achieved within the first 30 minutes of oxidation. The iron embedded in the activated carbon showed good performance in the degradation and mineralisation of phenol during the oxidation due to the active sites as iron oxides formed on the surface of the activated carbon. It was found that the embedding irons were presented in gamma-Fe(2)O(3), alpha-Fe(2)O(3), and alpha-FeCOOH forms on the activated carbon. The aging tests on FeAC catalysts showed less activity loss, and less iron leaching was found after four oxidation runs.