A Biomimetic Fibrous Composite Scaffold with Nanotopography-Regulated Mineralization for Bone Defect Repair.

The effective regeneration of large bone defects via bone tissue engineering is challenging due to the difficulty in creating an osteogenic microenvironment. Inspired by the fibrillar architecture of the natural extracellular matrix, we developed a nanoscale bioengineering strategy to produce bone fibril-like composite scaffolds with enhanced osteogenic capability. To activate the surface for biofunctionalization, self-adaptive ridge-like nanolamellae were constructed on poly(ε-caprolactone) (PCL) electrospinning scaffolds via surface-directed epitaxial crystallization. This unique nanotopography with a markedly increased specific surface area offered abundant nucleation sites for Ca2+ recruitment, leading to a 5-fold greater deposition weight of hydroxyapatite than that of the pristine PCL scaffold under stimulated physiological conditions. Bone marrow mesenchymal stem cells (BMSCs) cultured on bone fibril-like scaffolds exhibited enhanced adhesion, proliferation, and osteogenic differentiation in vitro. In a rat calvarial defect model, the bone fibril-like scaffold significantly accelerated bone regeneration, as evidenced by micro-CT, histological histological and immunofluorescence staining. This work provides the way for recapitulating the osteogenic microenvironment in tissue-engineered scaffolds for bone repair.

Designing Prepregnation and Fused Filament Fabrication Parameters for Recycled PP- and PA-Based Continuous Carbon Fiber Composites.

Continuous carbon fiber (cCF)-based 3D-printed polymer composites are known for their excellent flexural properties; however, the optimization of the overall process is still desired, depending on the material types involved. Here, the improved manufacturing of cCF-based composites is reported, considering virgin polyamide (PA) and postindustrial waste polypropylene (PP), and the parameters affecting the material properties are evaluated. Firstly, the prepregnation technique was optimized to manufacture cCF polymer filaments with various fiber-to-polymer ratios. Secondly, the fused filament fabrication (FFF) technique was optimized. It was observed that the layer height needs to be sufficiently low for proper interlayer adhesion. The influence of the printing temperature is more complicated, with filaments characterized by a lower fiber-to-polymer ratio requiring a higher nozzle diameter and higher temperatures for efficient printing; and for lower diameters, the best flexural properties are observed for parts printed at lower temperatures, maintaining a high interspace distance. Plasma treatment of the cCF was also explored, as was annealing of the produced parts to enhance the flexural properties, the latter being specifically interesting for the PP-based composite due to a lower wetting caused by a higher viscosity, despite supportive interfacial interactions. Eventually, overall guidelines were formulated for the successful production of cCF-based composites.

Impact of Multiple Reprocessing on Properties of Polyhydroxybutyrate and Polypropylene.

Biobased plastics have the potential to be sustainable, but to explore their circularity further, current end-of-life options need to be broadened. Mechanical recycling is one of the most accepted methods to bring back plastics into the loop. Polyhydroxybutyrates (PHBs) are biobased and biodegradable in nature with promising properties and varied applications in the market. This study focuses on their potential for mechanical recycling by multiple extrusion cycles (E1-E5) and multi-faceted characterization of the virgin (V) and reprocessed materials from E1 to E5. The behavior is compared to polypropylene (PP) as a reference with a similar property profile, which has also been reprocessed five times. The thermal properties of both series showed a stable melting point and thermal decomposition temperature from thermal analyses (differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA)). However, a steady increase in the degree of crystallinity was observed which could counterbalance the decrease in molecular weight due to repeated extrusion measured by gel permeation chromatography and resulted in similar values of tensile strength across the cycles. The strain at break was impacted after the first extrusion, but no significant change was observed thereafter; the same was observed for impact strength. Even in scanning electron microscopy (SEM) images, virgin and E5 samples appeared similar, showing the stability of morphological characteristics. Fourier transform infrared spectroscopy (FTIR) results revealed that no new groups are being formed even on repeated processing. The deviation between the PHB and PP series was more predominant in the melt mass flow rate (MFR) and rheology studies. There was a drastic drop in the MFR values in PHB from virgin to E5, whereas not much difference was observed for PP throughout the cycles. This observation was corroborated by frequency sweeps conducted with the parallel plate method. The viscosity dropped from virgin to E1 and E2, but from E3 to E5 it presented similar values. This was in contrast to PP, where all the samples from virgin to E5 had the same values of viscosity. This paper highlights the possibilities of mechanical recycling of PHB and explains why future work with the addition of virgin material and other additives is an area to be explored.

Connecting Gas-Phase Computational Chemistry to Condensed Phase Kinetic Modeling: The State-of-the-Art.

In recent decades, quantum chemical calculations (QCC) have increased in accuracy, not only providing the ranking of chemical reactivities and energy barriers (e.g., for optimal selectivities) but also delivering more reliable equilibrium and (intrinsic/chemical) rate coefficients. This increased reliability of kinetic parameters is relevant to support the predictive character of kinetic modeling studies that are addressing actual concentration changes during chemical processes, taking into account competitive reactions and mixing heterogeneities. In the present contribution, guidelines are formulated on how to bridge the fields of computational chemistry and chemical kinetics. It is explained how condensed phase systems can be described based on conventional gas phase computational chemistry calculations. Case studies are included on polymerization kinetics, considering free and controlled radical polymerization, ionic polymerization, and polymer degradation. It is also illustrated how QCC can be directly linked to material properties.