Hydrogenation of Carbon Dioxide to Dimethyl Ether on CuO-ZnO/ZSM-5 Catalysts: Comparison of Powder and Electrospun Structures.

The promising direct dimethyl ether (DME) production through CO2 hydrogenation was systematically analyzed in this research by synthesizing, characterizing, and testing several catalytic structures. In doing so, various combinations of precipitation and impregnation of copper- and zinc-oxides (CuO-ZnO) over a ZSM-5 zeolite structure were applied to synthesize the hybrid catalysts capable of hydrogenating carbon dioxide to methanol and dehydrating it to DME. The resulting catalytic structures, including the co-precipitated, sequentially precipitated, and sequentially impregnated CuO-ZnO/ZSM-5 catalysts, were prepared in the form of particle and electrospun fibers with distinguished chemical and structural features. They were then characterized using XRD, BET, XPS, ICP, TGA, SEM, and FIB-SEM/EDS analyses. Their catalytic performances were also tested and analyzed in light of their observed characteristics. It was observed that it is crucial to establish relatively small-size and well-distributed zeolite crystals across a hybrid catalytic structure to secure a distinguished DME selectivity and yield. This approach, along with other observed behaviors and the involved phenomena like catalyst particles and fibers, clusters of catalyst particles, or the whole catalytic bed, were analyzed and explained. In particular, the desired characteristics of a CuO-ZnO/ZSM-5 hybrid catalyst, synthesized in a single-pot processing of the precursors of all involved catalytically active elements, were found to be promising in guiding the future efforts in tailoring an efficient catalyst for this system.

Rapid wet chemical synthesis of bioactive glass with high yield by probe sonication.

Bioactive glasses (BGs) are inorganic biomaterials which possess favourable properties for bone repair and regeneration. The biological properties of the BGs depend on their physical features. This manuscript describes a simple methodology for rapid synthesis of BG nanoparticles (NPs) with tailored physical properties using ultrasonic disruption produced by an ultrasonic probe. The ultrasonic probe generates stable and transient cavitation which increases the mass transfer and accelerates the chemical reaction. This approach is relatively green as it evades the use of the drastic acidic conditions required for hydrolysis. The prepared BG NPs were characterized by Fourier transform infra-red (FTIR) spectroscopy, Raman spectroscopy, scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), particle size analysis (PSA), nitrogen adsorption/desorption and BET surface area analysis, X-ray photoelectron spectroscopy (XPS), inductively coupled plasma-optical emission spectrometry (ICP-OES), and in situ high temperature synchrotron XRD. The effects of ultrasonic irradiation time, and amplitude on the surface properties were investigated and the results confirmed that both parameters, especially amplitude, have significant effects on the physical properties of the prepared BG NPs. The XPS results showed that both, amplitude and time have a pronounced effect on the bridging and non-bridging oxygen atoms bonded to the Si centre in the BG samples, which play an important role in the bioactivity of the BG NPs. The in situ high temperature XRD patterns indicated a gradual phase transformation for the BG samples synthesized at different ultrasonic irradiation times and amplitudes. The TEM images showed that uniform nano-sized BG particles were obtained at 50% amplitude in only 10 minutes. A bimodal particle size distribution was observed with an increasing reaction time, up to 30 minutes, due to an increase in the formation of vortices at the interface where nucleation starts. All the prepared samples exhibited a glassy structure with the composition 70SiO2 : 25CaO : 5P2O5 and were highly bioactive. The proposed method would give a quick route for the synthesis of bioactive glasses and other ceramics with controlled physical properties.

Core-Sheath Pt-CeO2/Mesoporous SiO2 Electrospun Nanofibers as Catalysts for the Reverse Water Gas Shift Reaction.

One-dimensional (1D) core-sheath nanofibers, platinum (Pt)-loaded ceria (CeO2) sheath on mesoporous silica (SiO2) core were fabricated, characterized, and used as catalysts for the reverse water gas shift reaction (RWGS). CeO2 nanofibers (NFs) were first prepared by electrospinning (ES), and then Pt nanoparticles were loaded on the CeO2 NFs using two different deposition methods: wet impregnation and solvothermal. A mesoporous SiO2 sheath layer was then deposited by sol-gel process. The phase composition, structural, and morphological properties of synthesized materials were investigated by scanning electron microscope (SEM), scanning transmission electron microscopy (STEM), X-ray diffraction (XRD), nitrogen adsorption/desorption method, X-ray photoelectron spectroscopy (XPS), inductively coupled plasma-optical emission spectrometry (ICP-OES) analysis, and CO2 temperature programmed desorption (CO2-TPD). The results of these characterization techniques revealed that the core-sheath NFs with a core diameter between 100 and 300 nm and a sheath thickness of about 40-100 nm with a Pt loading of around 0.5 wt.% were successfully obtained. The impregnated catalyst, Pt-CeO2 NF@mesoporous SiO2, showed the best catalytic performance with a CO2 conversion of 8.9% at 350 °C, as compared to the sample prepared by the Solvothermal method. More than 99% selectivity of CO was achieved for all core-sheath NF-catalysts.

In Vivo Biocompatibility Investigation of an Injectable Calcium Carbonate (Vaterite) as a Bone Substitute including Compositional Analysis via SEM-EDX Technology.

Injectable bone substitutes (IBS) are increasingly being used in the fields of orthopedics and maxillofacial/oral surgery. The rheological properties of IBS allow for proper and less invasive filling of bony defects. Vaterite is the most unstable crystalline polymorph of calcium carbonate and is known to be able to transform into hydroxyapatite upon contact with an organic fluid (e.g., interstitial body fluid). Two different concentrations of hydrogels based on poly(ethylene glycol)-acetal-dimethacrylat (PEG-a-DMA), i.e., 8% (w/v) (VH-A) or 10% (w/v) (VH-B), were combined with vaterite nanoparticles and implanted in subcutaneous pockets of BALB/c mice for 15 and 30 days. Explants were prepared for histochemical staining and immunohistochemical detection methods to determine macrophage polarization, and energy-dispersive X-ray analysis (EDX) to analyze elemental composition was used for the analysis. The histopathological analysis revealed a comparable moderate tissue reaction to the hydrogels mainly involving macrophages. Moreover, the hydrogels underwent a slow cellular infiltration, revealing a different degradation behavior compared to other IBS. The immunohistochemical detection showed that M1 macrophages were mainly found at the material surfaces being involved in the cell-mediated degradation and tissue integration, while M2 macrophages were predominantly found within the reactive connective tissue. Furthermore, the histomorphometrical analysis revealed balanced numbers of pro- and anti-inflammatory macrophages, demonstrating that both hydrogels are favorable materials for bone tissue regeneration. Finally, the EDX analysis showed a stepwise transformation of the vaterite particle into hydroxyapatite. Overall, the results of the present study demonstrate that hydrogels including nano-vaterite particles are biocompatible and suitable for bone tissue regeneration applications.

In Vitro and In Vivo Biocompatibility Analysis of a New Transparent Collagen-based Wound Membrane for Tissue Regeneration in Different Clinical Indications.

BACKGROUND/AIM: For the treatment of different tissue defects such as jawbone defects, open wound defect, chronic ulcers, dura mater defects and corneal defects, different biomaterials are available. The use of collagen-based materials for these applications has been significantly increased over the past decades due to its excellent biocompatibility and degradability. However, no transparent collagen-based biomaterial is available until now. Thus, a newly developed transparent collagen membrane (TCM) based on natural derived porcine pericardium, which offers numerous application possibilities, was developed. The present study aimed to analyze the in vitro and in vivo biocompatibility using established methods. MATERIALS AND METHODS: The new TCM membrane and a commercially available collagen membrane (CM, Jason membrane, botiss biomaterials GmbH, Zossen, Germany) were tested for its in vitro cytocompatibility. Furthermore, the in vivo biocompatibility was analyzed using sham operations as control group. In vitro, cytocompatibility was tested in accordance with EN ISO 10993-5/-12 regulations and Live-Dead-stainings. In vivo, a subcutaneous implantation model in BALB/c mice was used and explants were prepared for analyses by established histological, immunohistochemical and histomorphometrical methods. RESULTS: In vitro, both membranes showed promising cytocompatibility with a slightly better direct cell response in the Live-Dead staining assay for the TCM. In vivo, TCM induced a comparable inflammatory immune response after 10 and 30 days with comparable numbers of M1- and M2-macrophages as also found in the control group without biomaterial insertion. CONCLUSION: The newly transparent collagen membrane is fully biocompatible and is supporting safe clinical application in tissue repair and surgery.

Ceria-Based Dual-Phase Membranes for High-Temperature Carbon Dioxide Separation: Effect of Iron Doping and Pore Generation with MgO Template.

Dual-phase membranes for high-temperature carbon dioxide separation have emerged as promising technology to mitigate anthropogenic greenhouse gases emissions, especially as a pre- and post-combustion separation technique in coal burning power plants. To implement these membranes industrially, the carbon dioxide permeability must be improved. In this study, Ce0.8Sm0.2O2-δ (SDC) and Ce0.8Sm0.19Fe0.01O2-δ (FSDC) ceramic powders were used to form the skeleton in dual-phase membranes. The use of MgO as an environmentally friendly pore generator allows control over the membrane porosity and microstructure in order to compare the effect of the membrane's ceramic phase. The ceramic powders and the resulting membranes were characterized using ICP-OES, HSM, gravimetric analysis, SEM/EDX, and XRD, and the carbon dioxide flux density was quantified using a high-temperature membrane permeation setup. The carbon dioxide permeability slightly increases with the addition of iron in the FSDC membranes compared to the SDC membranes mainly due to the reported scavenging effect of iron with the siliceous impurities, with an additional potential contribution of an increased crystallite size due to viscous flow sintering. The increased permeability of the FSDC system and the proper microstructure control by MgO can be further extended to optimize carbon dioxide permeability in this membrane system.