Novel germanium/polypyrrole composite for high power lithium-ion batteries.

Nano-Germanium/polypyrrole composite has been synthesized by chemical reduction method in aqueous solution. The Ge nanoparticles were directly coated on the surface of the polypyrrole. The morphology and structural properties of samples were determined by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Thermogravimetric analysis was carried out to determine the polypyrrole content. The electrochemical properties of the samples have been investigated and their suitability as anode materials for the lithium-ion battery was examined. The discharge capacity of the Ge nanoparticles calculated in the Ge-polypyrrole composite is 1014 mAh g(-1) after 50 cycles at 0.2 C rate, which is much higher than that of pristine germanium (439 mAh g(-1)). The composite also demonstrates high specific discharge capacities at different current rates (1318, 1032, 661, and 460 mAh g(-1) at 0.5, 1.0, 2.0, and 4.0 C, respectively). The superior electrochemical performance of Ge-polypyrrole composite could be attributed to the polypyrrole core, which provides an efficient transport pathway for electrons. SEM images of the electrodes have demonstrated that polypyrrole can also act as a conductive binder and alleviate the pulverization of electrode caused by the huge volume changes of the nanosized germanium particles during Li(+) intercalation/de-intercalation.

Tin/polypyrrole composite anode using sodium carboxymethyl cellulose binder for lithium-ion batteries.

A tin nanoparticle/polypyrrole (nano-Sn/PPy) composite was prepared by chemically reducing and coating Sn nanoparticles onto the PPy surface. The composite shows a much higher surface area than the pure nano-Sn reference sample, due to the porous higher surface area of PPy and the much smaller size of Sn in the nano-Sn/PPy composite than in the pure tin nanoparticle sample. Poly(vinylidene fluoride) (PVDF) and sodium carboxymethyl cellulose (CMC) were also used as binders, and the electrochemical performance was investigated. The electrochemical results show that both the capacity retention and the rate capability are in the same order of nano-Sn/PPy-CMC > nano-Sn/PPy-PVDF > nano-Sn-CMC > nano-Sn-PVDF. Scanning electronic microscopy (SEM) and electrochemical impedance spectroscopy (EIS) results show that CMC can prevent the formation of cracks in electrodes caused by the big volume changes during the charge-discharge process, and the PPy in the composite can provide a conducting matrix and alleviate the agglomeration of Sn nanoparticles. The present results indicate that the nano-Sn/PPy composite could be suitable for the next generation of anode materials with relatively good capacity retention and rate capability.