Spatial Growth Factor Delivery for 3D Bioprinting of Vascularized Bone with Adipose-Derived Stem/Stromal Cells as a Single Cell Source.

Encapsulating multiple growth factors within a scaffold enhances the regenerative capacity of engineered bone grafts through their localization and controls the spatiotemporal release profile. In this study, we bioprinted hybrid bone grafts with an inherent built-in controlled growth factor delivery system, which would contribute to vascularized bone formation using a single stem cell source, human adipose-derived stem/stromal cells (ASCs) in vitro. The strategy was to provide precise control over the ASC-derived osteogenesis and angiogenesis at certain regions of the graft through the activity of spatially positioned microencapsulated BMP-2 and VEGF within the osteogenic and angiogenic bioink during bioprinting. The 3D-bioprinted vascularized bone grafts were cultured in a perfusion bioreactor. Results proved localized expression of osteopontin and CD31 by the ASCs, which was made possible through the localized delivery activity of the built-in delivery system. In conclusion, this approach provided a methodology for generating off-the-shelf constructs for vascularized bone regeneration and has the potential to enable single-step, in situ bioprinting procedures for creating vascularized bone implants when applied to bone defects.

3D printed hydrogel scaffold promotes the formation of hormone-active engineered parathyroid tissue.

The parathyroid glands are localized at the back of the thyroid glands in the cervical region and are responsible for regulation of the calcium level in the blood, through specialized cells that sense Ca2+and secrete parathyroid hormone (PTH) in response to a decline in its serum level. PTH stimulates the skeleton, kidneys and intestines and controls the level of Ca2+through specialized activities. Iatrogenic removal of the parathyroid gland, as well as damage to its vascular integrity during cauterization are some of the common complications of thyroid surgery. Therefore, regeneration and/or replacement of malfunctioning parathyroid tissue is required. Tissue engineering is an emerging and promising field for patients with organ failure with recent pioneering clinical applications. The success of tissue engineering strategy depends on the use of proper cells, bioactive factors that stimulate the activities of these cells and scaffolds that are produced to recapitulate the tissue structure and support the function of the engineered tissues. 3D printing is a developing strategy for the production of these scaffolds by providing a delicate control over their structure and properties. In this study, human primary parathyroid cells were successfully isolated and their viability and ability to secrete PTH upon stimulation with different levels of Ca2+were shownin vitro. These cells were then seeded onto 3D printed alginate scaffolds and 3D bioprinted within alginate bioink, and cell viability as well as the ability to secrete PTH upon stimulation were also demonstrated. Therefore, functional hormone-active parathyroid tissue substitute was engineeredin vitrothrough 3D printed hydrogels and autologous cells.

Corrosion Resistance and Cytocompatibility of Magnesium-Calcium Alloys Modified with Zinc- or Gallium-Doped Calcium Phosphate Coatings.

In orthopedic surgery, metals are preferred to support or treat damaged bones due to their high mechanical strength. However, the necessity for a second surgery for implant removal after healing creates problems. Therefore, biodegradable metals, especially magnesium (Mg), gained importance, although their extreme susceptibility to galvanic corrosion limits their applications. The focus of this study was to control the corrosion of Mg and enhance its biocompatibility. For this purpose, surfaces of magnesium-calcium (MgCa1) alloys were modified with calcium phosphate (CaP) or CaP doped with zinc (Zn) or gallium (Ga) via microarc oxidation. The effects of surface modifications on physical, chemical, and mechanical properties and corrosion resistance of the alloys were studied using surface profilometry, goniometry, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), nanoindentation, and electrochemical impedance spectroscopy (EIS). The coating thickness was about 5-8 µm, with grain sizes of 43.1 nm for CaP coating and 28.2 and 58.1 nm for Zn- and Ga-doped coatings, respectively. According to EIS measurements, the capacitive response (Yc) decreased from 11.29 to 8.72 and 0.15 Ω-1 cm-2 sn upon doping with Zn and Ga, respectively. The Ecorr value, which was -1933 mV for CaP-coated samples, was found significantly electropositive at -275 mV for Ga-doped ones. All samples were cytocompatible according to indirect tests. In vitro culture with Saos-2 cells led to changes in the surface compositions of the alloys. The numbers of cells attached to the Zn-doped (2.6 × 104 cells/cm2) and Ga-doped (6.3 × 104 cells/cm2) coatings were higher than that on the surface of the undoped coating (1.0 × 103 cells/cm2). Decreased corrosivity and enhanced cell affinity of the modified MgCa alloys (CaP coated and Zn and Ga doped, with Ga-doped ones having the greatest positive effect) make them novel and promising candidates as biodegradable metallic implant materials for the treatment of bone damages and other orthopedic applications.