Anisotropic Pinning-Effect of Inclusions in Mg-Based Low-Carbon Steel.

In this study, the effect of austenite grain size on acicular ferrite (AF) nucleation in low-carbon steel containing 13 ppm Mg is determined. The average austenite grain size was calculated using OM Leica software. Results show that the predicted and experimental values of austenite grain size are extremely close, with a deviation of less than 20 µm. AF formation is difficult to induce by either excessively small and large austenite grain sizes; that is, an optimal austenite grain size is required to promote AF nucleation probability. The austenite grain size of 164 µm revealed the highest capacity to induce AF formation. The effects of the maximum distance of carbon diffusion and austenite grain size on the microstructure of Mg-containing low carbon steel are also discussed. Next, the pinning ability of different inclusion types in low-carbon steel containing 22 Mg is determined. The in situ observation shows that not every inclusion could inhibit austenite grain migration; the inclusion type influences pinning ability. The grain mobility of each inclusion was calculated using in situ micrographs of confocal scanning laser microscopy (CSLM) for micro-analysis. Results show that the austenite grain boundary can strongly be pinned by Mg-based inclusions. MnS inclusions are the least effective in pinning austenite grain boundary migration.

Inclusions properties at 1673 K and room temperature with Ce addition in SS400 steel.

Inclusion species formed in SS400 steel with Ce-addition was predicted by thermodynamic calculation. The analysis of the inclusion morphology and size distribution was carried out by applying Scanning Electron Microscopy (SEM) and Transmission Electron Microscope (TEM). Nano-Fe3O4 particles were also found in cerium-deoxidized and -desulfurized steel and their shapes were nearly spherical. The complex Ce2O3 inclusions covering a layer of 218 nm composed by several MnS particles with similar diffraction pattern. Most importantly, the complex Ce2O3 characterized by using TEM diffraction is amorphous in the steel, indicating that Ce2O3 formed in the liquid iron and then MnS segregated cling to it.

Thermodynamic Calculation among Cerium, Oxygen, and Sulfur in Liquid Iron.

Thermodynamic calculation has been applied to predict the inclusion formation in molten SS400 steel. When the Cerium addition in liquid iron is 70 ppm and the initial Oxygen and Sulphur are both 110 ppm, the formation of oxides containing Cerium would experience the transformation from Ce2O3 to CeO2 and also the formation of sulfides containing Cerium would experience the transformation from CeS to Ce2S3 and then to Ce3S4. Below 2000 K the most thermodynamic stable matter is CeO2 and the less thermodynamic stable inclusion is CeS. Only when the amount of [O] is extremely low and the amount of [S] and [Ce] is relatively high, Ce2S3 has the possibility to form.

Effects of Rare Earth Metals on Steel Microstructures.

Rare earth metals are used in semiconductors, solar cells and catalysts. This review focuses on the background of oxide metallurgy technologies, the chemical and physical properties of rare earth (RE) metals, the background of oxide metallurgy, the functions of RE metals in steelmaking, and the influences of RE metals on steel microstructures. Future prospects for RE metal applications in steelmaking are also presented.

Chelating agent-assisted heat treatment of a carbon-supported iron oxide nanoparticle catalyst for PEMFC.

Iron complexes were supported on commercial carbon black and heat treated to create FeO(x)/C catalysts that showed a larger normalized current density and normalized power density than commercial Pt/C catalysts; the coordination number of the iron complexes used affected the formation of the active site for oxygen reduction in PEMFC.