The plasticity of welded 441 ferritic stainless steel joints was controlled by varying the laser beam spot diameter during laser welding. A stainless steel plate thickness of 1.2 mm was used. The microstructures of the welded joints were analyzed for various spot diameters. The elongation of breaks and the reduced area of tensile specimens were analyzed to study the effects of spot diameter on plasticity of the welded joints. The results showed that the weld melt width and weld column crystal size increased with the spot diameter, but isometric crystals in the center of the weld were gradually reduced. Increasing spot diameter resulted in decreased tensile strength, elongation after breaks, and area reduction. So the parameter must be controlled during the laser welding.
RESUMO
To study the corrosion mechanism of high-nitrogen steel welds, this study investigated the effects of laser outputs on the corrosion behavior of high-nitrogen steel hybrid welded joints in hybrid laser-arc welding. The relationship between the ferrite content and laser output was characterized. The ferrite content increased with the increase in the laser power. The corrosion phenomenon first occurred at the two-phase interface, thereby forming corrosion pits. Ferritic dendrites were first corroded to form dendritic corrosion channels. Furthermore, first-principles calculations were performed to investigate the properties of the austenite and ferrite content. The work function and surface energy indicated that solid-solution nitrogen austenite exhibits a higher surface structural stability than austenite and ferrite. This study provides useful information for high-nitrogen steel weld corrosion.