Preparation of highly adsorptive biochar by sequential iron impregnation under refluxing and pyrolysis at low temperature for removal of tetracycline.

Iron-doping modification is a prevailing approach for improving adsorption capability of biochar with environmental friendliness, but usually requires high temperature and suffers from iron aggregation. Herein, a highly adsorptive biochar was manufactured via sequential disperse impregnation of iron by refluxing and pyrolysis at low temperature for eliminating tetracycline (TC) from aqueous solution. Iron oxides and hydroxides were impregnated and stably dispersed on the carbon matrix as pyrolyzed at 200 °C, meanwhile abundant oxygen and nitrogen functional groups were generated on surface. The iron-doped biochar exhibited up to 891.37 mg/g adsorption capacity at pH 5, and could be recycled with high adsorption capability. The adsorption of TC should be mostly contributed to the hydrogen bonding of N/O functional groups and the hydrogen bonding/coordination of iron oxides/hydroxides. This would provide a valuable guide for dispersedly doping iron and conserving functional groups on biochar, and a super iron-doped biochar was prepared with superior recyclability.

Facile production of cellulose nanofibers from raw elephant grass by an aluminum chloride-enhanced acidic deep eutectic solvent.

To develop a greener and more efficient method for producing cellulose nanofibers (CNFs) from raw plants, an AlCl3-enhanced ternary deep eutectic solvent, DES2 (consisting of choline chloride, citric acid, and AlCl3·6H2O in a molar ratio of 1:0.4:0.08), was synthesized. Raw elephant grass (EG) was pretreated with DES2, followed by sodium chlorite (NaClO2) bleaching and ultrasonic disruption to extract high-performance CNFs. The DES2 and NaClO2 treatments effectively removed hemicellulose and lignin, achieving removal rates of 99.23 % and 99.62 %, respectively, while maintaining a cellulose content of 78.3 %. DES2 demonstrated easy recyclability and maintained excellent biomass pretreatment performance even after multiple cycles. Following a brief 30-min intermittent ultrasound treatment, the resulting CNFs demonstrated superior crystallinity, increased carboxyl content, and a narrower width distribution compared to CNFs obtained from AlCl3-free DES1. Optimized conditions at 110 °C yielded CNFs with 85.3 % crystallinity, 0.64 mmol/g carboxyl content, 5.15 nm width distribution, and excellent dispersion in water for at least six months. Additionally, CNFs enhanced the tensile strength of chia seed mucilage (CM) composite films, showing a significant improvement to 26.6 MPa, representing a 231.3 % increase over the control film. This study offers a promising approach for efficiently producing CNFs from raw plants.