Experimental and Theoretical Studies on Acid Corrosion Inhibition of API 5L X70 Steel with Novel 1-N-α-d-Glucopyranosyl-1H-1,2,3-Triazole Xanthines.

A series of novel 1-N-α-d-glucopyranosyl-1H-1,2,3-triazole xanthines was synthesized from azido sugars (glucose, galactose, and lactose) and propargyl xanthines (theophylline and theobromine) using a typical copper (I)-catalyzed azide-alkyne 1,3-dipolar cycloaddition. The corrosion inhibition activities of these new carbohydrate-xanthine compounds were evaluated by studying the corrosion of API 5 L X70 steel in a 1 M HCl medium. The results showed that, at 10 ppm, a 90% inhibition efficiency was reached by electrochemical impedance spectroscopy. The inhibitory efficiency of these molecules is explained by means of quantum chemical calculations of the protonated species with the solvent effect, which seems to better represent the actual situation of the experimental conditions. Some quantum chemical parameters were analyzed to characterize the inhibition performance of the tested molecules.

Adsorption and corrosion inhibition behaviour of new theophylline-triazole-based derivatives for steel in acidic medium.

The design and synthesis of a series of theophylline derivatives containing 1,2,3-triazole moieties are presented. The corrosion inhibition activities of these new triazole-theophylline compounds were evaluated by studying the corrosion of API 5 L X52 steel in 1 M HCl medium. The results showed that an increase in the concentration of the theophylline-triazole derivatives also increases the charge transference resistance (R ct) value, enhancing inhibition efficiency and decreasing the corrosion process. The electrochemical impedance spectroscopy under static conditions studies revealed that the best inhibition efficiencies (approx. 90%) at 50 ppm are presented by the all-substituted compounds. According to the Langmuir isotherm, the compounds 4 and 5 analysed exhibit physisorption-chemisorption process, with exception of the hydrogen 3, bromo 6 and iodo 7 substituted compounds, which exhibit chemisorption process. The corrosion when submerging a steel bar in 1 M HCl was studied using SEM-EDS. This experiment showed that the corrosion process decreases considerably in the presence of 50 ppm of the organic inhibitors. Finally, the theoretical study showed a correlation between EHOMO, hardness (η), electrophilicity (W), atomic charge and the inhibition efficiency in which the iodo 7 substituted compound presents the best inhibitor behaviour.