Determining weathering-induced heterogeneous oxidation profiles of polyethylene, polypropylene and polystyrene using laser-induced breakdown spectroscopy.

Weathering-induced polymer degradation is typically heterogeneous which plays an integral part in fragmentation. Despite that, the current selection of techniques to investigate such heterogeneities, especially beneath the sample surface, is sparse. We introduce Laser-induced Breakdown Spectroscopy (LIBS) as an analytical tool and evaluate its performance for depth profiling. Three types of polymers were selected (polyethylene, polypropylene, and polystyrene) that were aged under controlled conditions. We demonstrate that LIBS can detect heterogeneous oxidation on the surface and inside the samples. The results reveal that different oxidation behaviors are linked to the sample's lattice structure and the subsequent formation of microcracks. This implies that LIBS is beneficial to give additional insights into the weathering and degradation behavior of environmentally relevant plastics.

Carbon-based biosensors from graphene family to carbon dots: A viewpoint in cancer detection.

According to the latest report by International Agency for Research on Cancer, 19.3 million new cancer cases and 10 million cancer deaths were globally reported in 2020. Early diagnosis can reduce these numbers significantly, and biosensors have appeared to be a solution to this problem as, unlike the traditional methods, they have low cost, rapid process, and do not need experts present on site for use. These devices have been incorporated to detect many cancer biomarkers and measure cancer drug delivery. To design these biosensors, a researcher must know about their different types, properties of nanomaterials, and cancer biomarkers. Among all types of biosensors, electrochemical and optical biosensors are the most sensitive and promising sensors for detecting complicated diseases like cancer. The carbon-based nanomaterial family has attracted lots of attention due to their low cost, easy preparation, biocompatibility, and significant electrochemical and optical properties. In this review, we have discussed the application of graphene and its derivatives, carbon nanotubes (CNTs), carbon dots (CDs), and fullerene (C60), for designing different electrochemical and optical cancer-detecting biosensors. Furthermore, the application of these carbon-based biosensors for detecting seven widely studied cancer biomarkers (HER2, CEA, CA125, VEGF, PSA, Alpha-fetoprotein, and miRNA21) is reviewed. Finally, various fabricated carbon-based biosensors for detecting cancer biomarkers and anticancer drugs are comprehensively summarized as well.

Comparison of Melting Processes for WPC and the Resulting Differences in Thermal Damage, Emissions and Mechanics.

The necessity for resource-efficient manufacturing technologies requires new developments within the field of plastic processing. Lightweight design using wood fibers as sustainable reinforcement for thermoplastics might be one solution. The processing of wood fibers requires special attention to the applied thermal load. Even at low processing temperatures, the influence of the dwell time, temperature and shear force is critical to ensure the structural integrity of fibers. Therefore, this article compares different compounding rates for polypropylene with wood fibers and highlights their effects on the olfactory, visual and mechanical properties of the injection-molded part. The study compares one-step processing, using an injection-molding compounder (IMC), with two-step processing, using a twin-scew-extruder (TSE), a heating/cooling mixer (HCM) and an internal mixer (IM) with subsequent injection molding. Although the highest fiber length was achieved by using the IMC, the best mechanical properties were achieved by the HCM and IM. The measured oxidation induction time and volatile organic compound content indicate that the lowest amount of thermal damage occurred when using the HCM and IM. The advantage of one-time melting was evened out by the dwell time. The reinforcement of thermoplastics by wood fibers depends more strongly on the structural integrity of the fibers compared to their length and homogeneity.

Impact of Enzymatic Degradation on the Material Properties of Poly(Ethylene Terephthalate).

With macroscopic litter and its degradation into secondary microplastic as a major source of environmental pollution, one key challenge is understanding the pathways from macro- to microplastic by abiotic and biotic environmental impact. So far, little is known about the impact of biota on material properties. This study focuses on recycled, bottle-grade poly(ethylene terephthalate) (r-PET) and the degrading enzyme PETase from Ideonella sakaiensis. Compact tension (CT) specimens were incubated in an enzymatic solution and thermally and mechanically characterized. A time-dependent study up to 96 h revealed the formation of steadily growing colloidal structures. After 96 h incubation, high amounts of BHET dimer were found in a near-surface layer, affecting crack propagation and leading to faster material failure. The results of this pilot study show that enzymatic activity accelerates embrittlement and favors fragmentation. We conclude that PET-degrading enzymes must be viewed as a potentially relevant acceleration factor in macroplastic degradation.

Investigations on Epoxy-Carbamate Foams Modified with Different Flame Retardants for High-Performance Applications.

In transport sectors such as aviation, automotive and railway, materials combining a high lightweight potential with high flame retardant properties are in demand. Polymeric foams are suitable materials as they are lightweight, but often have high flammability. This study focuses on the influence of different flame retardants on the burning behavior of Novolac based epoxy foams using Isophorone Diamine carbamate (B-IPDA) as dual functional curing and blowing agent. The flame retardant properties and possible modifications of these foams are systematically investigated. Multiple flame retardants, representing different flame retardant mechanisms, are used and the effects on the burning behavior as well as mechanical and thermal properties are evaluated. Ammonium polyphosphate (APP), used with a filler degree of 20 wt.% or higher, functions as the best performing flame retardant in this study.

Insights into the Bead Fusion Mechanism of Expanded Polybutylene Terephthalate (E-PBT).

Expandable polystyrene (EPS) and expanded polypropylene (EPP) dominate the bead foam market. As the low thermal performance of EPS and EPP limits application at elevated temperatures novel solutions such as expanded polybutylene terephthalate (E-PBT) are gaining importance. To produce parts, individual beads are typically molded by hot steam. While molding of EPP is well-understood and related to two distinct melting temperatures, the mechanisms of E-PBT are different. E-PBT shows only one melting peak and can surprisingly only be molded when adding chain extender (CE). This publication therefore aims to understand the impact of thermal properties of E-PBT on its molding behavior. Detailed differential scanning calorimetry was performed on neat and chain extended E-PBT. The crystallinity of the outer layer and center of the bead was similar. Thus, a former hypothesis that a completely amorphous bead layer enables molding, was discarded. However, the incorporation of CE remarkably reduces the crystallization and re-crystallization rate. As a consequence, the time available for interdiffusion of chains across neighboring beads increases and facilitates crystallization across the bead interface. For E-PBT bead foams, it is concluded that sufficient time for polymer interdiffusion during molding is crucial and requires adjusted crystallization kinetics.