Identification of Synergies in Fe, Co-Coordinated Polyphthalocyanines Scaffolds for Electrochemical CO2 Reduction Reaction.

The synergistic interaction between the isolated metal sites promoted the electrocatalytic activity of the catalysts. However, the structural heterogeneity of the isolated sites makes it challenging to evaluate this effect accurately. In this work, metal-coordinated polyphthalocyanine molecules (Fe-PPc, Co-PPc, FeCo-PPc) with long-range ordered and precise coordination structures are used as a platform to study the synergies of different isolated metal sites in the electrochemical CO2 reduction reaction. The combination means of experimental and theoretical calculation clearly reveal that the coexistence of Fe and Co sites in PPc significantly enhances the conjugation effect of the macrocycle. This enhancement subsequently causes the metal sites to lose more electrons, thereby improving their adsorption of CO2 and facilitating the formation of intermediate *COOH on them. As a result, FeCo-PPc achieves a CO partial current density of about 57.4 mA/cm2 with a high turnover frequency of over 49000 site-1 h-1 at -0.9 V (vs RHE).

Confining High-Valence Iridium Single Sites onto Nickel Oxyhydroxide for Robust Oxygen Evolution.

Enhancing activity and stability of iridium- (Ir-) based oxygen evolution reaction (OER) catalysts is of great significance in practice. Here, we report a vacancy-rich nickel hydroxide stabilized Ir single-atom catalyst (Ir1-Ni(OH)2), which achieves long-term OER stability over 260 h and much higher mass activity than commercial IrO2 in alkaline media. In situ X-ray absorption spectroscopy analysis certifies the obvious structure reconstruction of catalyst in OER. As a result, an active structure in which high-valence and peripheral oxygen ligands-rich Ir sites are confined onto the nickel oxyhydroxide surface is formed. In addition, the precise introduction of atomized Ir not only surmounts the large-range dissolution and agglomeration of Ir but also suppresses the dissolution of substrate in OER. Theoretical calculations further account for the activation of Ir single atoms and the promotion of oxygen generation by high-valence Ir, and they reveal that the deprotonation process of adsorbed OH is rate-determining.