RESUMO
STATEMENT OF PROBLEM: The hydrophobic and bioinert nature of polyetheretherketone (PEEK) implants needs to be addressed for successful osseointegration. PURPOSE: The purpose of this in vitro study was to evaluate the osteoblast cell behavior on PEEK implant surfaces treated with airborne-particle abrasion using different grit size aluminum oxide (Al2O3) particles. MATERIAL AND METHODS: Disk-shaped specimens (n=96) were prepared from medical grade PEEK rods and were distributed into 4 groups (n=24) of untreated PEEK (PEEK 0), airborne-particle abrasion using 50-µm Al2O3 particles (PEEK 50), airborne-particle abrasion using 110-µm Al2O3 particles (PEEK 110), and airborne-particle abrasion using 150-µm Al2O3 particles (PEEK 150). The surface characteristics were assessed using water contact angle (WCA) measurements and scanning electron microscopy (SEM). MG-63 osteoblast cells were cultured, and the biocompatibility of PEEK was assessed using a CellTiter-blue cell viability assay and florescence staining at day 1, 3, and 7. The specimens were stained with Alizarin red to assess the osteoblast cell differentiation on day 10 and 14. The Levene test was used to test the homogeneity of variances. One-way and Welch ANOVA with post hoc corrections were used to assess the overall statistical significance of differences among the groups (α=.05). RESULTS: The lowest mean WCA was demonstrated in PEEK 150 (49.25 ±5.51) and the highest in PEEK 0 (89.14 ±4.24) (P<.001). SEM images of PEEK 150 illustrated a more complex structure with a large area of globular outcroppings throughout the surface. PEEK 150 showed the highest cell metabolic activity at each time point with florescence staining showing a substantial cell confluence at day 3 and 7. Although PEEK 150 did not show a significant increase in cell proliferation, the number of cells attached was significantly higher than other groups (P<.05). PEEK 110 and 150 also showed a substantial increase in the extent of mineralization. CONCLUSIONS: Airborne-particle abrasion using moderate Al2O3 grit size (110- or 150-µm) improved the hydrophilicity and osteoblast cell behavior on PEEK implants.
RESUMO
Implant-supported screw-retained fixed dental prostheses (FDPs) produced by CAD/ CAM have been introduced in recent years for the rehabilitation of partial or total endentulous jaws. However, there is a lack of data about the long-term mechanical characteristics. OBJECTIVE: The aim of this study was to investigate the failure mode and the influence of extended cyclic mechanical loading on the load-bearing capacity of these frameworks. MATERIAL AND METHODS: Ten five-unit FDP frameworks simulating a free-end situation in the mandibular jaw were manufactured according to the I-Bridge®2-concept (I-Bridge®2, Biomain AB, Helsingborg, Sweden) and each was screw-retained on three differently angulated Astra Tech implants (30º buccal angulation/0º angulation/30º lingual angulation). One half of the specimens was tested for static load-bearing capacity without any further treatment (control), whereas the other half underwent five million cycles of mechanical loading with 100 N as the upper load limit (test). All specimens were loaded until failure in a universal testing machine with an occlusal force applied at the pontics. Load-displacement curves were recorded and the failure mode was macro- and microscopically analyzed. The statistical analysis was performed using a t-test (p=0.05). RESULTS: All the specimens survived cyclic mechanical loading and no obvious failure could be observed. Due to the cyclic mechanical loading, the load-bearing capacity decreased from 8,496 N±196 N (control) to 7,592 N±901 N (test). The cyclic mechanical ...