Optimized Pt-Co Alloy Nanoparticles for Reverse Water-Gas Shift Activation of CO2.

Different Co contents were used to tune bimetallic Pt-Co nanoparticles with a diameter of 8 nm, resulting in Pt:Co ratios of 3.54, 1.51, and 0.96. These nanoparticles were then applied to the MCF-17 mesoporous silica support. The synthesized materials were characterized with HR-TEM, HAADF-TEM, EDX, XRD, BET, ICP-MS, in situ DRIFTS, and quasi in situ XPS techniques. The catalysts were tested in a thermally induced reverse water-gas shift reaction (CO2:H2 = 1:4) at atmospheric pressure in the 200-700 °C temperature range. All bimetallic Pt-Co particles outperformed the pure Pt benchmark catalyst. The nanoparticles with a Pt:Co ratio of 1.51 exhibited 2.6 times higher activity and increased CO selectivity by 4% at 500 °C. Experiments proved that the electron accumulation and alloying effect on the Pt-Co particles are stronger with higher Co ratios. The production of CO followed the formate reaction pathway on all catalysts due to the face-centered-cubic structure, which is similar to the Pt benchmark. It is concluded that the enhanced properties of Co culminate at a Pt:Co ratio of 1.51 because decreasing the ratio to 0.96 results in lower activity despite having more Co atoms available for the electronic interaction, resulting in the lack of electron-rich Pt sites.

Pt/MnO Interface Induced Defects for High Reverse Water Gas Shift Activity.

The implementation of supported metal catalysts heavily relies on the synergistic interactions between metal nanoparticles and the material they are dispersed on. It is clear that interfacial perimeter sites have outstanding skills for turning catalytic reactions over, however, high activity and selectivity of the designed interface-induced metal distortion can also obtain catalysts for the most crucial industrial processes as evidenced in this paper. Herein, the beneficial synergy established between designed Pt nanoparticles and MnO in the course of the reverse water gas shift (RWGS) reaction resulted in a Pt/MnO catalyst having ≈10 times higher activity compared to the reference Pt/SBA-15 catalyst with >99 % CO selectivity. Under activation, a crystal assembly through the metallic Pt (110) and MnO evolved, where the plane distance differences caused a mismatched-row structure in softer Pt nanoparticles, which was identified by microscopic and surface-sensitive spectroscopic characterizations combined with density functional theory simulations. The generated edge dislocations caused the Pt lattice expansion which led to the weakening of the Pt-CO bond. Even though MnO also exhibited an adverse effect on Pt by lowering the number of exposed metal sites, rapid desorption of the linearly adsorbed CO species governed the performance of the Pt/MnO in the RWGS.

Surface Modification of Titanate Nanotubes with a Carboxylic Arm for Further Functionalization Intended to Pharmaceutical Applications.

Nanotechnology is playing a significant role in modern life with tremendous potential and promising results in almost every domain, especially the pharmaceutical one. The impressive performance of nanomaterials is shaping the future of science and revolutionizing the traditional concepts of industry and research. Titanate nanotubes (TNTs) are one of these novel entities that became an appropriate choice to apply in several platforms due to their remarkable properties such as preparation simplicity, high stability, good biocompatibility, affordability and low toxicity. Surface modification of these nanotubes is also promoting their superior characters and contributing more to the enhancement of their performance. In this research work, an attempt was made to functionalize the surface of titanate nanotubes with carboxylic groups to increase their surface reactivity and widen the possibility of bonding different molecules that could not be bonded directly. Three carboxylic acids were investigated (trichloroacetic acid, citric acid and acrylic acid), and the prepared composites were examined using FT-IR and Raman spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and dynamic light scattering (DLS). The toxicity of these functionalized TNTs was also investigated using adherent cancer cell lines and fibroblasts to determine their safety profile and to draw the basic lines for their intended future application. Based on the experimental results, acrylic acid could be the suitable choice for permanent surface modification with multiple carboxylic groups due to its possibility to be polymerized, thus presenting the opportunity to link additional molecules of interest such as polyethylene glycol (PEG) and/or other molecules at the same time.

Systematic screening of gas diffusion layers for high performance CO2 electrolysis.

Certain industrially relevant performance metrics of CO2 electrolyzers have already been approached in recent years. The energy efficiency of CO2 electrolyzers, however, is yet to be improved, and the reasons behind performance fading must be uncovered. The performance of the electrolyzer cells is strongly affected by their components, among which the gas diffusion electrode is one of the most critical elements. To understand which parameters of the gas diffusion layers (GDLs) affect the cell performance the most, we compared commercially available GDLs in the electrochemical reduction of CO2 to CO, under identical, fully controlled experimental conditions. By systematically screening the most frequently used GDLs and their counterparts differing in only one parameter, we tested the influence of the microporous layer, the polytetrafluoroethylene content, the thickness, and the orientation of the carbon fibers of the GDLs. The electrochemical results were correlated to different physical/chemical parameters of the GDLs, such as their hydrophobicity and surface cracking.

Unfolding the effects of decontamination treatments on the structural and functional integrity of N95 respirators via numerical simulations.

Filtering facepiece respirators (FFRs) provide effective protection against diseases spread through airborne infectious droplets and particles. The widespread use of FFRs during the COVID-19 pandemic has not only led to supply shortages, but the disposal of single-use facemasks also threatens the environment with a new kind of plastic pollution. While limited reuse of filtering facepiece respirators has been permitted as a crisis capacity strategy, there are currently no standard test methods available for decontamination before their repeated use. The decontamination of respirators can compromise the structural and functional integrity by reducing the filtration efficiency and breathability. Digital segmentation of X-ray microcomputed tomography (microCT) scans of the meltblown nonwoven layers of a specific N95 respirator model (Venus-4400) after treatment with one and five cycles of liquid hydrogen peroxide, ultraviolet radiation, moist heat, and aqueous soap solution enabled us to perform filtration simulations of decontaminated respirators. The computed filtration efficiencies for 0.3 µm particles agreed well with experimental measurements, and the distribution of particle penetration depths was correlated with the structural changes resulting from decontamination. The combination of X-ray microCT imaging with numerical simulations thus provides a strategy for quantitative evaluation of the effectiveness of decontamination treatments for a specific respirator model.