Preliminary Exploration of Economic Polypropylene-Fiber-Reinforced ECC with Superfine River Sand (SSPP-ECC) Applied to a Bridge Pavement Leveling Overlay.

In response to the current common disease of concrete leveling overlays of bridge pavement in China, the feasibility of using an economic SSPP-ECC with local waste superfine sand as an alternative material for a leveling overlay was proposed in this study. To evaluate the interface bonding property in the girder between the SSPP-ECC and concrete, a slant shear test and split tensile test were designed to study the interfacial shear and tensile properties of the ordinary concrete/ordinary concrete (OC/OC) and ordinary concrete/SSPP-ECC (OC/ECC), where the results showed that SSPP-ECC could significantly improve the interface shear stress and split tensile strength compared to ordinary concrete. Furthermore, the damage status of OC/ECC no longer involved fracturing along the interface; instead, each of the two substrates was partially destroyed, which revealed that OC/ECC had a high bonding effect. Moreover, a restrained shrinkage test was carried out to evaluate the shrinkage property of SSPP-ECC, where the result showed that the shrinkage strain of SSPP-ECC was slightly lower than concrete, where the average cracking time for SSPP-ECC was far longer than for ordinary concrete under the same ambient drying conditions; furthermore, the stress rate for SSPP-ECC revealed that it was a low-cracking-risk material. Meanwhile, the crack width of SSPP-ECC was only 0.1 mm after 35 d, which showed that SSPP-ECC had a more substantial crack width control capacity relative to concrete. The test results initially verified the feasibility and great potential of economic SSPP-ECC applied in a bridge pavement leveling overlay.

Natural Frequency Response Evaluation for RC Beams Affected by Steel Corrosion Using Acceleration Sensors.

This paper presented a laboratory investigation for analyzing the natural frequency response of reinforced concrete (RC) beams affected by steel corrosion. The electrochemical acceleration technique induced the corroded RC beams until the predetermined value of the steel corrosion ratio was achieved. Then, the natural frequency responses of the corroded beams were tested utilizing piezoelectric acceleration sensors. The damage states of the corroded beams were assessed through the measurement of crack parameters and the equivalent elastic modulus of the beams, which aims to clarify the fundamental characteristics of the dynamic response for the corroded RC beam with the increased steel corrosion ratio. The results revealed that steel corrosion reduces the bending stiffness of the RC beams and, thus, reduces the modal frequency. The variation of natural frequency can identify the corrosion damage even if no surface cracking of the RC beam, and the second-order frequency should be more indicative of the damage scenario. The degradations of stiffness and the natural frequency were estimated in this study by the free vibration equation of a simply supported beam, and a prediction method for the RC beam's residual service life was established. This study supports the use of variations in natural frequency as one diagnostic indicator to evaluate the health of RC bridge structures.

Preliminary Analysis of the Ductility and Crack-Control Ability of Engineered Cementitious Composite with Superfine Sand and Polypropylene Fiber (SSPP-ECC).

Engineered cementitious composite (ECC) is a potential cement-based material with the abilities of large deformation and crack width control. However, ECC is difficult to popularize in many developing countries because the costs of silica sand and polyvinyl alcohol (PVA) fiber with a surface coating are too high for practical engineering. Therefore, we proposed an economical ECC with superfine river sand and polypropylene (PP) fiber (SSPP-ECC) to replace PVA fiber and silica sand. The SSPP-ECC proposed in this paper is a sustainable material using local material ingredients, which has considerable adaptability for large-scale engineering applications. The 16 groups of specimens were prepared through a factorial design method, curing for four-point bending tests. The bending strength, deflection, flexural modulus of elasticity, and crack width were measured and calculated during the test. The factor analysis of the test results shows that the contents of fiber and fly ash had significant effects on the ductility of SSPP-ECC with an extra combined effect at the same time, and a response surface model with high accuracy was fitted to predict the yield length of SSPP-ECC. The ductility of SSPP-ECC was positively related to its crack-control ability and it was shown that the crack width of SSPP-ECC increased significantly with a high content of superfine sand. This paper proposed a reasonable way to utilize superfine sand and provided the mix proportion of SSPP-ECC with characteristics of deformation hardening and multi-cracking, which may cater to the demands of many concrete components on ductility and crack resistance.

Performance Evaluation of Styrene-Butadiene-Styrene-Modified Stone Mastic Asphalt with Basalt Fiber Using Different Compaction Methods.

Superpave gyratory compaction (SGC) and Marshall compaction methods are essentially designed according to volumetric properties. In spite of the similarity, the optimum asphalt contents (OAC) of the two methods are greatly affected by the laboratory compaction process, which would further influence their performance. This study aims to evaluate the performance of styrene-butadiene-styrene (SBS)-modified stone mastic asphalt (SMA) with basalt fiber by using SGC and Marshall compaction methods. Basalt fiber was proved to improve and strength the basic properties of SBS-asphalt according to test results of asphalt binder. The effects of SGC and Marshall compaction methods on OAC and volumetric properties, i.e., density, air voids (VA), voids in mineral aggregates (VMA), and voids filled with asphalt (VFA), were evaluated in detail. Finally, the pavement performance of asphalt mixture prepared by SGC and Marshall compaction methods were compared in order to analyze the high-temperature creep, low-temperature splitting, and moisture stability performance. Results showed that the OAC of SGC (~5.70%) was slightly lower than that of Marshall method (5.80%). Furthermore, the pavement performance of SGC specimens were improved to a certain extent compared with Marshall specimens, indicating that SGC has a better compaction effect and mechanical performance.