Safety Assessment of Polypyrrole Nanoparticles and Spray-Coated Textiles.

Polypyrrole (PPy) nanoparticles (NPs) are used for the coating of materials, such as textiles, with biomedical applications, including wound care and tissue engineering, but they are also promising antibacterial agents. In this work, PPy NPs were used for the spray-coating of textiles with antimicrobial properties. The functional properties of the materials were verified, and their safety was evaluated. Two main exposure scenarios for humans were identified: inhalation of PPy NPs during spray (manufacturing) and direct skin contact with NPs-coated fabrics (use). Thus, the toxicity properties of PPy NPs and PPy-coated textiles were assessed by using in vitro models representative of the lung and the skin. The results from the materials' characterization showed the stability of both the PPy NP suspension and the textile coating, even after washing cycles and extraction in artificial sweat. Data from an in vitro model of the air-blood barrier showed the low toxicity of these NPs, with no alteration of cell viability and functionality observed. The skin toxicity of PPy NPs and the coated textiles was assessed on a reconstructed human epidermis model following OECD 431 and 439 guidelines. PPy NPs proved to be non-corrosive at the tested conditions, as well as non-irritant after extraction in artificial sweat at two different pH conditions. The obtained data suggest that PPy NPs are safe NMs in applications for textile coating.

Antibacterial properties of polypyrrole-treated fabrics by ultrasound deposition.

Antimicrobial textiles can contribute to the fighting against antibiotic resistance pathogenic microorganisms. Polypyrrole is a conjugated polymer that exerts a biocidal action thanks to positive charges on its backbone chain produced during it synthesis. In this work, dispersions of stable polypyrrole nanoparticles were produced by chemical oxidative polymerization at room temperature in water. An ultrasound-assisted coating process was then used to effectively treat a polyester fabric with the nanoparticles to obtain an optimal antibacterial coating which efficiently eradicates the bacteria. The results showed that the treated fabric with about 4 g/m2 of polypyrrole had log bacteria reductions of 6.0 against Staphylococcus aureus and 7.5 against Escherichia coli. The combination of a polypyrrole synthesis in the form of water nanoparticles dispersions and a continuous coating of fabrics supported by ultrasound overcomes some issues of upscaling of the traditional in-situ chemical deposition used until now for the production of polypyrrole-coated textiles.

Highly polydisperse keratin rich nanofibers: Scaffold design and in vitro characterization.

The use of bioactive proteins such as keratin has been successfully explored to improve the biological interface of scaffolds with cells during the tissue regeneration. In this work, it is optimized the fabrication of nanofibers combining wool keratin extracted by sulfitolysis, with polycaprolactone (PCL) in order to design bicomponent fibrous matrices able to exert a self-adapting pattern of signals-morphological, chemical, or physical-confined at the single fiber level, to influence cell and bacteria interactions. It is demonstrated that the blending of highly polydisperse keratin with PCL (50:50) improves the stability of the electrospinning process, promoting the formation of nanofibers-144.1 ± 43.9 nm-without the formation of defects (i.e., beads, ribbons) typically recognized in the fabrication of keratin ones. Moreover, keratin drastically increases the fiber hydrophilicity-compared with PCL fiber alone-thus improving the hMSC adhesion and in vitro proliferation until 14 days. Moreover, the growth of bacterial strains (i.e., Escherichia coli and Staphylococcus aureus) seems to be not specifically inhibited by the contribution of keratin, so that the integration of further selected compounds (i.e., metal ions) is suggested to more efficiently fight against bacteria resistance, to make them suitable for the regeneration of different interfaces and soft tissues (i.e., skin and cornea). © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 107A: 1803-1813, 2019.

Biomineralization of a titanium-modified hydroxyapatite semiconductor on conductive wool fibers.

Metal ions are frequently incorporated into crystalline materials to improve their electrochemical properties and to confer new physicochemical properties. Naturally-occurring phosphate apatite, which is formed geologically and in biomineralization processes, has extensive potential applications and is therefore an attractive functional material. In this study, we generate a novel building block for flexible optoelectronics using bio-inspired methods to deposit a layer of photoactive titanium-modified hydroxyapatite (TiHA) nanoparticles (NPs) on conductive polypyrrole(PPy)-coated wool yarns. The titanium concentration in the reaction solution was varied between 8-50 mol% with respect to the phosphorous, which led to titanate ions replacing phosphate in the hydroxyapatite lattice at levels up to 17 mol%. PPy was separately deposited on wool yarns by oxidative polymerization, using two dopants: (i) anthraquinone-2,6-disulfonic acid to increase the conductivity of the PPy layer and (ii) pyroglutamic acid, to reduce the resistivity of the wool yarns and to promote the heterogeneous nucleation of the TiHA NPs. A specific titanium concentration (25 mol% wrt P) was used to endow the TiHA NPs on the PPy-coated fibers with a desirable band gap value of 3.68 eV, and a specific surface area of 146 m2 g-1. This is the first time that a thin film of a wide-band gap semiconductor has been deposited on natural fibers to create a fiber-based building block that can be used to manufacture flexible electronic devices.