Cellulose Nanocrystal-Templated Tin Dioxide Thin Films for Gas Sensing.

Porous tin dioxide is an important low-cost semiconductor applied in electronics, gas sensors, and biosensors. Here, we present a versatile template-assisted synthesis of nanostructured tin dioxide thin films using cellulose nanocrystals (CNCs). We demonstrate that the structural features of CNC-templated tin dioxide films strongly depend on the precursor composition. The precursor properties were studied by using low-temperature nuclear magnetic resonance spectroscopy of tin tetrachloride in solution. We demonstrate that it is possible to optimize the precursor conditions to obtain homogeneous precursor mixtures and therefore highly porous thin films with pore dimensions in the range of 10-20 nm (ABET = 46-64 m2 g-1, measured on powder). Finally, by exploiting the high surface area of the material, we developed a resistive gas sensor based on CNC-templated tin dioxide. The sensor shows high sensitivity to carbon monoxide (CO) in ppm concentrations and low cross-sensitivity to humidity. Most importantly, the sensing kinetics are remarkably fast; both the response to the analyte gas and the signal decay after gas exposure occur within a few seconds, faster than in standard SnO2-based CO sensors. This is attributed to the high gas accessibility of the very thin porous film.

Facile Uptake and Release of Ammonia by Nickel Halide Ammines.

Although major difficulties are experienced for hydrogen- storage materials to meet performance requirements for mobile applications, alternative fuel cell feedstocks such as ammonia can be stored in the solid state safely at high capacity. We herein describe the NiX2 -NH3 (X=Cl, Br, I) systems and demonstrate their exceptional suitability for NH3 storage (up to 43 wt % NH3 with desorption that begins at 400 K). The structural effects that result from the uptake of NH3 were studied by powder X-ray diffraction (PXD), FTIR spectroscopy and SEM. NH3 release at elevated temperatures was followed by in situ PXD. The cycling capabilities and air stability of the systems were also explored. NH3 is released from the hexaammines in a three-step process to yield the diammine, monoammine and NiX2 dihalides respectively and (re)ammoniation occurs readily at room temperature. The hexaammines do not react with air after several hours of exposure.