RESUMO
Aim To evaluate the cytotoxicity, biocompatibility and mineralization capacity of BIO-C PULPO, and MTA. Methodology L929 fibroblasts were cultured and MTT assay was used to determine the material cytotoxicity on 6, 24, and 48 h. A total of 30 male rats (Wistar) aged between 4 and 6 months, weighing between 250 and 300 g were used. Polyethylene tubes containing BIO-C PULPO, MTA, and empty tubes were implanted into dorsal connective tissue. After the experimental periods (7, 15, 30, 60, and 90 days) the tubes were histologically analyzed using hematoxylin-eosin (H&E), immunolabeling of IL-1ß and TNF-α, and von Kossa staining, or without staining for polarized light analysis. The average number of inflammatory cells was quantified; the mineralization assessment was determined by the area marked in µm2 and semiquantitative immunolabeling analyses of IL-1ß and TNF-α were performed. Then, data underwent statistical analysis with a 5% significance level. Results It was observed that BIO-C PULPO and MTA presented cytocompatibility at 6, 24, and 48 similar or higher than control for all evaluated period. On periods 7 and 15 days, BIO-C PULPO was the material with the highest number of inflammatory cells (p<0.05). On periods 30, 60, and 90 days, BIO-C PULPO and MTA presented similar inflammatory reactions (p>0.05). No statistical differences were found between Control, BIO-C PULPO, and MTA for immunolabeling of IL-1ß and TNF-α in the different periods of analysis (p<0.05). Positive von Kossa staining and birefringent structures under polarized light were observed in all analyzed periods in contact with both materials, but larger mineralization area was found with BIO-C PULPO on day 90 (p<0.05). Conclusion BIO-C PULPO was biocompatible and induced mineralization similar to MTA.
Assuntos
Biomineralização , Cimentos Dentários , Interleucina-1beta/metabolismo , Materiais Restauradores do Canal Radicular , Fator de Necrose Tumoral alfa/metabolismo , Compostos de Alumínio , Animais , Materiais Biocompatíveis , Compostos de Cálcio , Combinação de Medicamentos , Inflamação , Masculino , Óxidos , Ratos , Ratos Wistar , Silicatos , Tela SubcutâneaRESUMO
Abstract Aim To evaluate the cytotoxicity, biocompatibility and mineralization capacity of BIO-C PULPO, and MTA. Methodology L929 fibroblasts were cultured and MTT assay was used to determine the material cytotoxicity on 6, 24, and 48 h. A total of 30 male rats (Wistar) aged between 4 and 6 months, weighing between 250 and 300 g were used. Polyethylene tubes containing BIO-C PULPO, MTA, and empty tubes were implanted into dorsal connective tissue. After the experimental periods (7, 15, 30, 60, and 90 days) the tubes were histologically analyzed using hematoxylin-eosin (H&E), immunolabeling of IL-1β and TNF-α, and von Kossa staining, or without staining for polarized light analysis. The average number of inflammatory cells was quantified; the mineralization assessment was determined by the area marked in μm2 and semiquantitative immunolabeling analyses of IL-1β and TNF-α were performed. Then, data underwent statistical analysis with a 5% significance level. Results It was observed that BIO-C PULPO and MTA presented cytocompatibility at 6, 24, and 48 similar or higher than control for all evaluated period. On periods 7 and 15 days, BIO-C PULPO was the material with the highest number of inflammatory cells (p<0.05). On periods 30, 60, and 90 days, BIO-C PULPO and MTA presented similar inflammatory reactions (p>0.05). No statistical differences were found between Control, BIO-C PULPO, and MTA for immunolabeling of IL-1β and TNF-α in the different periods of analysis (p<0.05). Positive von Kossa staining and birefringent structures under polarized light were observed in all analyzed periods in contact with both materials, but larger mineralization area was found with BIO-C PULPO on day 90 (p<0.05). Conclusion BIO-C PULPO was biocompatible and induced mineralization similar to MTA.
Assuntos
Animais , Masculino , Ratos , Materiais Restauradores do Canal Radicular , Fator de Necrose Tumoral alfa/metabolismo , Cimentos Dentários , Interleucina-1beta/metabolismo , Biomineralização , Óxidos , Materiais Biocompatíveis , Ratos Wistar , Silicatos , Compostos de Cálcio , Compostos de Alumínio , Tela Subcutânea , Combinação de Medicamentos , InflamaçãoRESUMO
This article describes the use of Photodynamic Therapy (PDT) during the endodontic treatment of teeth with periapical lesion. Patients presented tooth 35 with diagnostic hypotheses of Periapical Cyst or Granuloma. The Crown-Down preparation was performed with the HyFlex CM system. In case I it was not possible to reach the working length, in case II the foraminal debridement was performed at the actual tooth length. In the final irrigation, the E1 - Irrisonic ultrasonic insert was used, promoting sequentially agitation of NaOCl 2.5%, EDTA 17% and NaOCl 2.5%. Then, PDT was applied with 0.005% methylene blue dye. Calcium Hydroxide with Parammonochlorophenol was used and after 15 days, the final irrigation protocol and PDT were performed again. After 90 days of case I and 1â¯year of case II, the total lesion regression was observed in both cases. It is concluded that the proposed treatment improved the microbial disinfection favoring the regression of the periapical alterations providing satisfactory clinical and radiographic results.
Assuntos
Necrose da Polpa Dentária/terapia , Fotoquimioterapia/métodos , Irrigantes do Canal Radicular/uso terapêutico , Tratamento do Canal Radicular/métodos , Necrose da Polpa Dentária/diagnóstico por imagem , Desinfecção/métodos , Humanos , Materiais Restauradores do Canal Radicular/uso terapêutico , Hipoclorito de Sódio/uso terapêuticoRESUMO
Abstract This study evaluated the effect of hypertension on tissue response and biomineralization capacity of white Mineral Trioxide Aggregate (MTA), High-plasticity MTA (MTA HP), and Biodentine® (BDT) in rats. Polyethylene tubes filled with MTA, MTA HP, BDT, and the control group (empty tubes) were placed into the dorsal subcutaneous tissue of 32 male rats (16 normotensive (NT) and 16 hypertensive rats - 8 per group). After 7 and 30 days, the polyethylene tubes surrounded by connective tissue were removed, fixed, and embedded in histological resin. The mean number of inflammatory cells was estimated in HE-stained sections, biomineralization was quantified as area (µm2) by Kossa (VK) staining, and examination by polarized light (LP) microscopy was performed. The differences amongst the groups were analyzed statistically by the Mann-Whitney or Student's t test, according to Shapiro-Wilk test of normality (p < 0.05). The inflammatory responses to all materials were greater in hypertensive rats than in NT rats (p < 0.05). Positive VK staining in MTA and BDT were more pronounced in NT rats at 7 and 30 days (p < 0.05). Birefringent structures in LP for MTA, MTA HP, and BDT were more pronounced in NT rats at 7 days (p<0.05). In rats, hypertension was able to increase inflammatory infiltrate and decrease biomineralization of the tested materials.
Assuntos
Óxidos/farmacologia , Materiais Biocompatíveis/farmacologia , Silicatos/farmacologia , Compostos de Cálcio/farmacologia , Compostos de Alumínio/farmacologia , Tela Subcutânea/efeitos dos fármacos , Tela Subcutânea/fisiopatologia , Biomineralização/fisiologia , Hipertensão/fisiopatologia , Fatores de Tempo , Teste de Materiais , Reprodutibilidade dos Testes , Ratos Wistar , Tela Subcutânea/patologia , Combinação de Medicamentos , Hipertensão/complicações , Inflamação/fisiopatologia , Inflamação/patologia , Microscopia de PolarizaçãoRESUMO
Objective: This study evaluated the leakage volume of 1% Rhodamine B which received or not an internal waterproofing material. The hypothesis is that the waterproofing reduces microleakage. Material and Methods: Forty-two human teeth were selected for this study. After access, preparation, and filling of root canals, the teeth were divided into 3 groups: GI sealed with Cimpat Blanc®, without intraradicular post/core preparation; GII - sealed with Cimpat Blanc®, with intraradicular post/core preparation, and GIII sealed with Cimpat Blanc®, with intraradicular post/core preparation and internal waterproofing material with ethyl cyanoacrylate. T-test was used to analyze difference between initial and final weight and there was difference (p < 0.05). To analyze infiltration of the colorant, the volume was the comparison variable. Results: Shapiro Wilktest was applied and showed normal distribution of the variables. ANOVA (p = 0.0013 / p< 0.5). Conclusion: In endodontically treated teeth receiving temporary restoration, the use of ethyl cyanoacrylate as internal waterproofing material is effective in preventing microleakage. (AU)
Objetivos: Este estudo avaliou o volume de infiltração de Rhodamine B 1% com ou sem impermeabilização interna. A hipótese é que a impermeabilização reduz a microinfiltração. Material e Métodos: Foram selecionados 42 dentes humanos para este estudo. Após o acesso, o preparo e a obturação dos canais radiculares, os dentes foram divididos em 3 grupos: GI - sem preparo para núcleo intrarradicular e selado com Cimpat Blanc®; GII - com preparo para núcleo intrarradicular e selado com Cimpat Blanc®, e GIII - com preparo para núcleo intrarradicular, impermeabilizado internamente com cianoacrilato de etila e selado com Cimpat Blanc®. O teste T foi utilizado para analisar a diferença entre o peso inicial e o peso final (p < 0,05). Para analisar a infiltração do corante, o volume era a variável de comparação. Resultados: o teste de Shapiro Wilk foi aplicado e mostrou distribuição normal das variáveis. O teste ANOVA (p = 0,0013 / p < 5%) foi aplicado e determinou uma diferença estatística entre os grupos. Ao comparar os grupos em conjunto, GIII mostra a menor taxa de vazamento quando comparado aos outros grupos, sendo estatisticamente diferente (teste de Tukey - p < 0,5). Conclusão: Nos dentes endodonticamente tratados com restauração temporária, o uso de cianoacrilato de etila como material impermeabilizante interno é eficaz na prevenção da microinfiltração (AU)
Assuntos
Humanos , Corantes , Infiltração Dentária , Restauração Dentária Temporária , EndodontiaRESUMO
Introduction: Both Mineral Trioxide Aggregate (MTA) and Portland cement (PC) have been highlighted because of their favorable biological properties, with extensive applications in Endodontics, including the possibility of using into root canal filling. Objective: This article reviews literature related to MTA and PC comparing their physical, chemical and biological properties, as well as their indications. Literature review: Literature reports studies revealing the similarities between these materials' properties, including both biocompatibility and bone repair induction. Moreover, there is the need for the development of a root canal sealer based on these materials (MTA and PC). Conclusion: MTA and CP show promissory perspective both in Dentistry and Endodontics.
RESUMO
O grande número de cirurgiões-dentistas no mercado de trabalho brasileiro tem elevado a competitividade no âmbito odontológico, levando o profissional a recorrer a diferentes estratégias na tentativa de atrair pacientes. Este trabalho visou relatar diferentes formas de marketing odontológico, mostrando como estas podem fortalecer o vínculo entre profissional e paciente e tornar-se uma alternativa para enfrentar a concorrência do mercado. Concluiu-se que os recursos de marketing em Odontologia são inúmeros e podem ser aplicados de maneira eficaz e simples, desde que amparados nos fundamentos da ética, podem fazer com que o cirurgião-dentista se destaque, atraia e fidelize pacientes, garantindo seu sucesso profissional.
Assuntos
Odontologia , Mercado de Trabalho , MarketingRESUMO
Os equipamentos automatizados permitem maior praticidade e rapidez nos procedimentos clínicos, auxiliam na realização de um diagnóstico mais preciso, além de atuarem como uma poderosa ferramenta de marketing que diferencia o cirurgião-dentista frente a um mercado cada vez mais competitivo. O objetivo deste trabalho foi relatar alguns aparelhos automatizados e novidades tecnológicas com aplicação na área odontológica, demonstrando os benefícios que estes proporcionam para o profissional e seus pacientes. A sinformações foram obtidas em sites de fabricantes e representantes dos equipamentos, por meio de ferramentas de busca na Internet. Observou-se que os equipamentos automatizados disponíveis no mercado odontológico apresentam destacada aplicabilidade clínica, maximizando a qualidade do procedimento e minimizando o tempo de atendimento.
Assuntos
Equipamentos Odontológicos , Informática Odontológica , Tecnologia OdontológicaRESUMO
Softwares odontológicos promovem o gerenciamento prático das tarefas clínico-administrativas de consultórios odontológicos. O objetivo deste trabalho foi correlacionar diferentes softwares (Pro Dent, IS-Odonto, ExDental, Dental Pro, Dental Office, Dental Clinic, Dentalis, Easy Dental), através de pesquisa em sites especializados na internet, enumerando suas vantagens e desvantagens. Diante da diversidade de softwares odontológicos disponíveis no mercado, para sua escolha devem ser considerados aspectos como facilidade de utilização, presença de agenda e controles administrativos, arquivamento de imagens, abrangência da especialidade do cirurgião-dentista, contato direto com os responsáveis pelo seu desenvolvimento, além dos aspectos éticos que envolvem sua utilização.
Assuntos
Administração da Prática Odontológica/tendências , Consultórios Odontológicos/tendências , Informática Odontológica , SoftwareRESUMO
Objetivo: Verificar por meio de análise histológica os efeitos de agentes hemostáticos na reparação óssea, colocados em defeitos ósseos nas tíbias direita e esquerda de ratos jovens. Métodos: Foram utilizados 32 ratos machos (Holtzman). Após assepsia e anestesia, foi realizada incisão de 1cm em cada perna, expondo a região anterior da tíbia. Utilizando um micromotor e broca esférica, foram preparadas cavidades, expondo a medula óssea, as quais foram irrigadas com ácido épsilon-aminocapróico (EACA) ou preenchidas com gelatina absorvível Gelfoam. Nos períodos de sete, 14, 30, 45 dias, os animais foram sacrificados segundo o protocolo bioético, as tíbias removidas e fixadas em formol a 10% para inclusão em parafina e análise em microscopia de luz. Resultados: A análise dos cortes histológicos demonstrou que em todos os grupos (controle e tratados) os fenômenos biológicos da reparação óssea estiveram presentes, com diferença apenas na cronologia. As reações da reparação óssea confirmaram a biocompatibilidade dos materiais; o grupo tratado com Gelfoam apresentou discreta aceleração no processo de reparação tecidual em relação aos demais grupos, principalmente nos períodos de 14, 30 e 45 dias pós-cirurgia. O Gelfoam foi totalmente reabsorvido; a remoção dos agentes hemostáticos das lojas cirúrgicas acelera o processo de reparação tecidual. Conclusão: Em todos os grupos experimentais, a seqüência de fenômenos biológicos que compõem a reparação óssea esteve presente, havendo diferença na cronologia. As reações apresentadas no reparo ósseo confirmaram a biocompatibilidade dos materiais. A remoção total dos agentes hemostáticos nas lojas cirúrgicas acelera o processo de reparação tecidual...