Effects of sodium copper- and sodium iron-chlorophyllin primers on resin bonding to dentin.

This study evaluated the effects of two chlorophyll derivatives, sodium copper chlorophyllin (Cu-Chl) and sodium iron chlorophyllin (Fe-Chl), on the bond strength between a self-curing luting agent (4-META/MMA-TBB resin) and dentin. Five aqueous primers containing 35% 2-hydroxyethylmethacrylate with 0.007% Cu-Chl, 0.07% Cu-Chl, 0.007% Fe-Chl, 0.07% Fe-Chl, or neither Cu-Chl nor Fe-Chl (no-Chl) were prepared. The extracted human dentin surfaces were etched with 10% phosphoric acid (10PA), primed, and bonded to a resin block using the 4-META/MMA-TBB resin. A conventional etching agent (10-3) and 10PA without primer (PA/no-primer) were used as controls. The microtensile bond strength was determined after 48 h. The arithmetic medians for 20 stick specimens were calculated and statistically analyzed using a nonparametric Steel-Dwass test (α = 0.05). The maximum bond strength was achieved in the 0.007% Cu-Chl group, followed by those in the 0.07% Cu-Chl, 0.07% Fe-Chl, 10-3, 0.007% Fe-Chl, no-Chl, and PA/no-primer groups. No significant difference was observed between 0.007% Fe-Chl, 0.07% Fe-Chl, and 10-3. The bond strength to dentin etched with 10PA was influenced by the type and concentration of the chlorophyll derivatives applied. Cu-Chl rather than Fe-Chl should be useful as a component of surface treatment agents for bonding 4-META/MMA-TBB resin to dentin.

Modulation of osteoclastogenesis by macrogeometrically designed hydrophilic dual acid-etched titanium surfaces.

The aim of this study was to evaluate the influence of implant macrodesign and surface hydrophilicity on osteoclast (OC) differentiation, activation, and survival in vitro. Titanium disks were produced with a sandblasted, dual acid-etched surface, with or without additional chemical modification for increasing hydrophilicity (SAE-HD and SAE, respectively) and different macrodesign comprising trapezoidal (HLX) or triangular threads (TMX). This study evaluated 7 groups in total, 4 of which were experimental: HLX/SAE-HD, HLX-SAE, TMX/SAE-HD, and TMX/SAE; and 3 control groups comprising OC differentiated on polystyrene plates (CCPC): a positive CCPC (+), a negative CCPC (-), and a lipopolysaccharide-stimulated assay positive control group, CCPC-LPS. Murine macrophage RAW264.7 cells were seeded on the disks, differentiated to OC (RAW-OC) by receptor activator of nuclear factor-κB ligand (RANKL) treatment and cultured for 5 days. Osteoclast differentiation and cell viability were respectively assessed by specific enzymatic Tartrate-Resistant Acid Phosphatase (TRAP) activity and MTT assays. Expression levels of various OC-related genes were measured at the mRNA level by quantitative polymerase chain reaction (qPCR). HLX/SAE-HD, TMX/SAE-HD, and HLX/SAE significantly suppressed OC differentiation when compared to CCPC (+). Cell viability was significantly increased in TMX/SAE and reduced in HLX/SAE-HD. In addition, the expression of Interleukin (IL)-6 and Tumour Necrosis Factor (TNF)-α was upregulated in TMX/SAE-HD compared to CCPC (+). Hydrophilic surfaces negatively modulate macrophage/osteoclast viability. Specifically, SAE-HD with double triangular threads increases the cellular pro-inflammatory status, while surface hydrophilicity and macrodesign do not seem to have a distinct impact on osteoclast differentiation, activation, or survival.

A randomized controlled trial of immediate implant placement comparing hydroxyapatite nano-coated and uncoated sandblasted/acid-etched implants using a digital surgical guide.

PURPOSE: This study evaluated the implant stability, volumetric changes, and patient-reported outcome measures (PROMs) of hydroxyapatite (HA) nano-coated sandblasted/acid-etched (SLA) implants compared to uncoated SLA implants. METHODS: Forty patients were recruited and randomly allocated to HA nano-coated SLA group (test, n = 20) and uncoated SLA group (control, n = 20) using single-blinded/block randomization. Implants were immediately placed in maxillary posterior region using a digital surgical guide. Insertion torque and implant stability quotient (ISQ) were measured at implant surgery and 1, 2, 3, and 4 months postoperatively. Intraoral scans, PROMs and soft tissue inflammation data were collected, and multivariable linear regression analysis of ISQ was performed. RESULTS: In total, 48 implants (test; n = 24, control; n = 24) in 37 patients (test; n = 19, control; n = 18) were analyzed. Despite no significant between-group difference at surgery, the test group showed higher ISQ values than the control group at 2 (76.53 ± 4.17 vs. 71.32 ± 4.79, p < 0.01), 3 (77.45 ± 4.41 vs. 73.85 ± 4.69, p < 0.05), and 4 months (79.08 ± 2.96 vs. 73.43 ± 3.52, p < 0.0001) postoperatively. There were no significant differences in linear and volumetric changes, PROMs, and soft tissue inflammation analysis between two groups. The ISQ at implant surgery was influenced by age and diabetes mellitus (DM) at the implant level and DM and predicted total bone-to-implant contact area at the patient level. CONCLUSION: HA nano-coated SLA implants promoted favorable immediate implants stability during early osseointegration phase compared to uncoated SLA implants, but displayed similar dimensional changes, PROMs, and soft tissue inflammation outcomes. TRIAL REGISTRATION: Clinical Research Information Service (CRIS), KCT0006364. Registered 21 July 2021, https://cris.nih.go.kr/cris/search/detailSearch.do?seq=24221&search_page=L .

Ultrasonic activation of adhesive systems increases bond strength and intratubular penetration of resin cement in root dentin subjected to radiation therapy.

OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.

Influence of pretreating radicular dentin with different polyacrylic acids and isopropanol on the retention of posts.

STATEMENT OF PROBLEM: The optimal pretreatment of radicular dentin before cementing a post with glass ionomer cement is unclear. PURPOSE: The purpose of this in vitro study was to evaluate the retention of prefabricated tapered titanium posts to endodontically treated teeth after applying different pretreatment protocols on the radicular dentin. MATERIAL AND METHODS: The coronal part of 32 single-rooted human teeth was removed 1-mm coronally to the cemento-enamel junction. All specimens received endodontic treatment, and the root canals were prepared with an instrument to a depth of 10 mm to receive a titanium post. The dentin walls of each specimen were roughened with a hand-held diamond cutting instrument. The specimens were randomly divided according to the surface treatments into 4 groups (n=8): KW: etched with 20% to 30% polyacrylic acid (PAA) (Ketac Conditioner) and rinsed with water; KWI: etched with 20% to 30% PAA, rinsed with water and 70% isopropanol; DW: etched with 30% to 50% PAA (Durelon Liquid) and rinsed with water; DWI: etched with 30% to 50% PAA, rinsed with water and 70% isopropanol. The prefabricated titanium posts were airborne-particle abraded and cemented with glass ionomer cement. The specimens were fixed in custom-made brass cylindrical holders with autopolymerizing acrylic resin with the holder parallel to the long axis of the post. All specimens were stored in water for 3 days at 37 °C. Retention was evaluated using a tensile test with a universal testing machine (Zwick Z010) at a crosshead speed of 2 mm/min. Data were statistically analyzed with a 1-way ANOVA, followed by the Tukey post hoc test for pairwise comparisons between groups (α=.05). RESULTS: Mean ±standard deviation retention values ranged from 201.8 ±55.5 N (KW) to 328.1 ±70.9 N (DWI). Groups DWI and KWI (316 ±58.3 N) showed statistically higher retention values than group KW (P<.05) but did not significantly differ from retention values obtained in group DW (P>.05). CONCLUSIONS: An additional final rinse with isopropanol after using PAA increased the retention of the post significantly for all groups. Although group DWI achieved the highest retention values, pretreatment of radicular dentin as in group KWI may also be considered.

The influence of two distinct surface modification techniques on the clinical efficacy of titanium implants: A systematic review and meta-analysis.

PURPOSE: To compare the effectiveness of anodized and sandblasted large-grit acid-etched surface modification implants in clinical applications. METHODS: This systematic review has been registered at PROSPERO (CRD42023423656). A systematic search was performed using seven databases. The meta-analysis was performed using the RevMan 5.4 program and Stata 17.0 software. An analysis of the risk of bias in the included studies was conducted using the Cochrane Handbook for Systematic Reviews of Interventions and the Newcastle-Ottawa scale. RESULTS: A comprehensive analysis of 16 studies, which collectively encompassed a total of 2768 implants, was finished. Following a five years follow-up, the meta-analysis showed that the cumulative survival rate of implants was lower in the anodized group compared to the sandblasted large-grit acid-etched group (RR, 3.47; 95 % confidence interval [CI], 1.23 to 9.81; P = 0.02). Furthermore, the anodized group and the sandblasted large-grit acid-etched group had similar marginal bone loss over the one to three years follow-up period. However, it was observed that the marginal bone loss increased at the five years follow-up period in the anodized group in comparison to the sandblasted large-grit acid-etched group (SMD, 2.98; 95 % CI, 0.91 to 5.06; P = 0.005). In terms of biological complications, plaque index, bleeding on probing, and probing pocket depth, we found no statistically significant differences between the anodized and sandblasted large-grit acid-etched group. CONCLUSIONS: The sandblasted large-grit acid-etched group exhibited higher implants cumulative survival rate and less marginal bone loss compared to the anodized group. Moreover, both groups demonstrated similar incidences of biological complications, plaque index, bleeding on probing, and probing pocket depth, suggesting overall equivalence in these aspects.

Assessing push-out bond strength in re-irradiated teeth: Universal resin cement performance in self-etch and self-adhesive modes.

OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.

Efecto del tratamiento de la morfología oclusal con materiales para restauraciones preventivas / Effect of treating occlusal morphology with materials for preventive restorations

Introducción: las fosas y fisuras son áreas formadas por delgadas irregularidades de la capa del esmalte de la superficie oclusal. La compleja morfología en dientes posteriores es un determinante biológico asociado al desarrollo de caries. Objetivo: evaluar el efecto de diversas formas de tratar la morfología oclusal en la adaptación y penetración de materiales utilizados en restauraciones preventivas. Material y métodos: diseño experimental e in vitro. Sesenta terceros molares fueron distribuidos aleatoriamente en dos grupos: surco sin ameloplastia y con ameloplastia; además, contaban con acondicionamiento del esmalte que se subdividió en tres subgrupos: 1) sellador de fosas y fisuras, 2) adhesivo/sellador de fosas y fisuras y 3) adhesivo/ resina Flow. Resultados: los subgrupos adhesivo/sellador y adhesivo/ Flow alcanzaron mayores valores de adaptación íntima a las paredes del surco. Las diferencias fueron significativas entre los materiales (p = 0.0009). Las mayores zonas de desadaptación resultaron para el sellador sin y con ameloplastia. La penetración de los materiales fue mayor en los surcos con ameloplastia. En los surcos tratados con ameloplastia, el adhesivo/Flow reveló el mayor porcentaje de penetración y la mejor adaptación a las paredes del surco. Conclusiones: la penetración del material está positivamente correlacionada con la profundidad del surco. El sellador con y sin ameloplastia mostró pobre adaptación a las paredes del surco (AU)

Introduction: pits and fissures are areas formed by fine irregularities in the enamel layer of the occlusal surface. The complex morphology in posterior teeth are biological determinants associated with the development of caries. Objective: to evaluate the effect of various ways of treating occlusal morphology on the adaptation and penetration of materials used in preventive restorations. Material and methods: experimental design, in vitro. Sixty third molars were randomly distributed into two groups: groove without ameloplasty and with ameloplasty, with enamel conditioning with three subgroups: 1) pit and fissure sealer, 2) adhesive/pit and fissure sealer, 3) adhesive/resin flow. Results: the adhesive/sealant and adhesive/flow subgroups reached higher values of intimate adaptation to the furrow walls. The differences were significant between the materials (p = 0.0009). The largest areas of maladjustment were found for the sealant without and with ameloplasty. The penetration of the materials was greater in the grooves with ameloplasty. In the grooves treated with ameloplasty, the adhesive/flow revealed the highest percentage of penetration and the best adaptation to the walls of the groove. Conclusions: the penetration of the material is positively correlated with the depth of the furrow. The sealant with and without ameloplasty showed poor adaptation to the sulcus walls (AU)

Acid-Base Resistant Zone in Teeth with the Direct Restoration Using Different Adhesive System Generations: A Systematic Review

ABSTRACT Objective: To find out what the acid-base resistant zone (ABRZ) is and the mechanism of its formation. Material and Methods: This systematic review was based on the search of laboratory studies in which selfetching adhesive systems were used. The electronic database PubMed was used for the search. The search began on August 2021 and ended on June 2022. We have analyzed the materials and methods of each research and entered them in the appropriate tables to give a clearer assessment of the obtained results. Results: This systematic review included 15 full-text articles published from 2011 to 2019. The ABRZ is formed on both dentine and enamel. On dentine, the ABRZ is formed only when using self-etching adhesive systems; on the enamel, on the contrary, the step of preliminary etch and rinse contributes to the formation of a thicker ABRZ. The functional monomer MDP and fluorine increase the thickness of the ABRZ and provide a hybrid layer /ABRZ boundary without defects and erosions. Conclusion: Self-etching adhesive systems ensure the creation of an ABRZ resistant to acid-base tests. This phenomenon can provide the resistance of tooth tissues to demineralization, and therefore increase their resistance to caries.

Uso de adhesivo universal con pregrabado y autograbado en tejidos duros del diente / Use of universal adhesive with pre-etch and self etch strategies on hard tooth tissues

RESUMEN Introducción: Buscando satisfacer la demanda con procedimientos adhesivos más rápidos, menos sensibles a la técnica y facilidad de uso, se han desarrollado los adhesivos universales, que brindan al profesional la opción de seleccionar la estrategia de adhesión con diferentes modos de grabado, ya sea con grabado y enjuague, autograbado o grabado selectivo. Debido a la poca información existente, se han generado dudas sobre el rendimiento, propiedades y la aplicación de una técnica adhesiva adecuada sobre los tejidos dentales. Objetivo: Determinar el nivel de adhesión con el uso de adhesivos universales en modo de grabado y enjuague y autograbado. Métodos: Se realizó una revisión de la literatura, a través de la búsqueda electrónica en las bases de datos: SciELO, Scopus, PubMed, Springer y EBSCO. Inicialmente se seleccionaron por título y resumen, artículos duplicados se consideraron solo una vez, se incluyeron artículos de acceso libre y pagos, escritos en idioma español e inglés, publicados desde el año 2015, de los cuales 39 artículos fueron seleccionados para el estudio. Conclusiones: El uso de adhesivos universales sobre dentina presenta un nivel de adhesión mayor cuando se aplica en modo de autograbado. La aplicación activa del adhesivo universal en esmalte mejora la fuerza y resistencia de unión. El nivel de adhesión en el esmalte es mayor cuando se aplica en modo de grabado y enjuague. La resistencia inicial y por fatiga del adhesivo, no mejora con los tiempos prolongados del grabado ácido.

ABSTRACT Introduction: universal adhesives have been developed to satisfy the demand with faster adhesive procedures, less sensitive to the technique and ease of use, which offer the professional the option of selecting the adhesion strategy with different etching modes, either with etch-and-rinse, self-etch or selective etching ones. Doubts have been generated about the performance, properties and application of an adequate adhesive technique on dental tissues due to the little existing information. Objective: to determine the level of adhesion with the use of universal adhesives in etch-and-rinse and self-etch modes Methods: an electronic search of the literature was carried out in SciELO, Scopus, PubMed, Springer and EBSCO databases. Initially, articles were selected by title and abstract, duplicate ones were considered only once, free and paid access articles, written in Spanish and English and published since 2015 were included; 39 of them were selected for the study. Conclusions: the use of universal adhesives on dentin presents a higher level of adhesion when applied in self-etch mode. The active application of the universal adhesive improves the enamel bond strength. The level of adhesion on the enamel is higher when applied in etch-and-rinse. The initial fatigue resistance of the adhesive does not improve with prolonged acid etching times.

Uso efectivo de los adhesivos de octava generación / Effective use of eighth generation adhesives

Introducción: se realizó una revisión bibliográfica con el objetivo de conocer, analizar y comparar los diferentes tipos de adhesivos de octava generación que se encuentran en el mercado y la diferencia que existe entre cada uno. Los adhesivos universales han demostrado mejoras en su resistencia, sobre todo en las técnicas de aplicación y en las propiedades de estos materiales, al mejorar la fuerza adhesiva para que el odontólogo pueda brindar tratamientos restaurativos exitosos. Objetivo: conocer, analizar y comparar los diferentes tipos de adhe- sivos de la octava generación empleados en odontología. Material y métodos: se realizó una búsqueda en las bases de datos electrónicas PubMed, BVS, Redalyc y ScienceDirect. Se utilizaron 32 artículos que cumplieron con los criterios predeterminados y la especificidad reque- rida para la pregunta de investigación. Conclusiones: se demostró que la tecnología cada día avanza, sobre todo en el área de los adhesivos, ya que éstos son de mucha utilidad en el día a día del odontólogo; es importante conocer cada uno de éstos, puesto que es un poco complejo seleccionar el correcto, mas no el uso. En la actualidad, existen diversas opciones por las que el odontólogo puede optar, es por ello que el pro- fesional debe estar capacitado sobre cada una de las diferentes marcas existentes y, de acuerdo al tratamiento, debe elegir cuál es mejor utilizar en una rehabilitación. Es importante para el odontólogo conocer estos materiales, ya que esto lo beneficiará al momento de llevar un plan de tratamiento restaurador (AU)

Introduction: a bibliographic review was carried out to learn about, analyze, and compare the different types of eighth-generation adhesives on the market and the difference between each one. Universal adhesives have demonstrated improvements in their resistance, especially in the application techniques and properties of these materials, improving the adhesive strength so that the dentist can provide successful restorative treatments. Objective: to know, analyze and compare the different types of eighth-generation adhesives used in dentistry. Material and methods: a search was made of the following electronic databases: PubMed, BVS, Redalyc, ScienceDirect. Finally, 32 articles that met the predetermined criteria and the specificity required for the research question were used. Conclusions: it was demonstrated that technology is advancing every day, especially in the area of adhesives since these are very useful in the daily life of the dentist. It is important to know each one of these since it is a little complex at the moment of selecting the correct one, but not the use. Currently, there are several options that the dentist can choose, which is why the professional must be trained on each of the various existing brands and according to the treatment which is the best to use at the time of rehabilitation. The dentist needs to know these materials since they will benefit him/her when carrying out a restorative treatment plan (AU)

Comparación de la fuerza de adhesión a dentina de cementos de autograbado vs grabado total / Comparison of bond strength to dentin of self-etching cements vs total etching

Los sistemas cementantes han mejorado notablemente, los objetivos que persiguen los nuevos cementos es que la adhesión sea duradera y conseguir siempre que sea posible una interface cerrada con un sellado perfecto. Se han podido desarrollar nuevas técnicas y nuevos materiales de cementación que han ido perfeccionando la unión del material restaurador al diente. En el presente estudio se compara la fuerza de adhesión a dentina de cementos de autograbado y cementos de grabado total para comprobar los efectos positivos en el grabado de la dentina. Para el estudio se utilizaron dos cementos a base de resina (RelyX U200 Clicker 3M y RelyX Ultimate 3M). Se encapsularon 40 molares en acrílico en dos grupos de 20 muestras para la aplicación de dos sistemas cementantes de autograbado (grupo 1) y de grabado total (grupo 2), respectivamente, se desgastaron hasta descubrir la dentina; siguiendo las especificaciones del fabricante se colocó el cemento en cada grupo, y después se sometieron a pruebas de cizalla en una máquina de ensayo universal Instron. La medida expresada en megapascales (MPa) fue: grupo 1 = 7.5569 y grupo 2 = 12.6444. En este caso fueron analizados dos grupos, tomándose la primera significancia bilateral. Se realiza la prueba en t de Student, con 95% de intervalo de confianza en la diferencia, demostrando así que el cemento RelyX Ultimate 3M tiene mayor fuerza de adhesión que el cemento RelyX U200 Clicker 3M. Nuestra investigación fue factible y llegamos a nuestro propósito, en el cual comprobamos la mayor adhesión de cementos de grabado total, los cuales son sometidos a un previo tratamiento del diente (AU)

Tratamiento de la fractura corono-radicular no complicada de la corona: caso clínico / Treatment of non-complicated crown-root fracture: a clinical case

El trauma dentoalveolar se define como aquella lesión de extensión e intensidad variable y de ori- gen accidental o intencional, causada por fuerzas que actúan sobre el órgano dentario y los tejidos que lo rodean. Se puede diagnosticar a simple vista o con ayuda de la radiografía, se debe tratar sin demora para preservar la vitalidad de la pulpa, sobre todo en casos de niños y adolescentes, to- mando en cuenta la formación radicular. El trau- ma dental es motivo de urgencia por el dolor que provocan en los pacientes, la prevalencia varia del 26 al 76% de las lesiones dentales en dentición permanente (AU)

Adhesión a dentina parte I: características del sustrato y sistemas adhesivos / Dentin bonding part I: substrate characteristics and bonding systems

La Odontología Restauradora contemporánea no puede concebirse sin la adhesión de los materiales restauradores a las estructuras dentarias. En mu-chos procedimientos restauradores, no sólo el esmal-te sino también la dentina se encuentra involucrada, por lo tanto, la adhesión a esta última juega un rol cla-ve en el éxito clínico. No obstante, todavía supone un gran desafío lograr una adhesión estable y predeci-ble en el tiempo. El propósito del presente artículo es analizar las características principales de la dentina como sustrato adhesivo y describir los sistemas ad-hesivos actuales y sus mecanismos de acción (AU)

Contemporary Restorative Dentistry cannot be conceived without the adhesion of restorative materials to dental structures. In many restorative procedures not only the enamel, but also the dentin is involved, therefore dentin bonding plays a key role in their success. However, it is still a great challenge to achieve stable and predictable dentin bonding over time. The aim of this article is to analyze the main characteristics of dentin as an adhesive substrate and to describe current adhesive systems and their bonding mechanisms (AU)

Adhesión a dentina part II: estrategias para optimizar la adhesión a dentina y protocolos adhesivos / Dentin bonding part II: strategies to optimize dentin bonding and adhesive protocols

La adhesión a dentina con sistemas adhesivos polimé-ricos representa un desafío que surge de la necesi-dad de vincular un sustrato dentario heterogéneo y variable con materiales que presentan todavía cier-tos aspectos a atender para poder conseguir el máxi-mo desempeño. El propósito del presente artículo es evaluar algunas de las estrategias propuestas para mejorar la adhesión a dentina, y sugerir un protocolo de trabajo con los diferentes tipos de sistemas adhesivos (AU)

Dentin bonding with polymeric adhesive systems represents a challenge that arises from the need to link a heterogeneous and variable dental substrate with materials that still have certain aspects to be addressed in order to achieve maximum performance. The aim of this article is to evaluate some of the proposed strategies to improve dentin bonding and to suggest a protocol for each different type of bonding systems (AU)

Caracterización microscópica de la dentina de dientes temporales / Microscopic characterization of the dentin of temporary teeth

La dentina se compone de un mineral de fosfato de calcio identificado como dahllita, que se dispone en pequeños cristales de hidroxiapatita carbonatada con dimensiones de 36 × 25 × 4 nm, y por una fase orgánica cuyo principal componente es el colágeno tipo 1 en 90%, que se orienta en forma de malla. Esta conformación corresponde a los dientes permanentes. Dentro de las estructuras, encontramos túbulos dentinarios que miden, aproximadamente, entre 0.5-1 µm de diámetro en la periferia y hasta 3-5 µm cerca de la pulpa. En el presente estudio, realizado en dentina de dientes temporales, el lumen de dichos túbulos es más grande cuando se encuentra cerca de la pulpa dental. Asimismo, se encontraron cambios elementales importantes de acuerdo con las diferentes profundidades en las que se observó, encontrando un aumento en el peso porcentual de carbono cuando se encuentra a mayor profundidad, lo que indica una composición orgánica mayor en la dentina pulpar. En estudios de dientes permanentes esta composición es disminuida y con mayor concentración en la dentina cercana a la unión amelodentinaria. En dentina de dientes temporales se encontraron diferencias en el recuento de túbulos dentinarios por mm2, comparado a la dentina de dientes permanentes, donde el número de túbulos no varía mucho (AU)

Dentin is composed of a calcium phosphate mineral identified as dahllite, which is arranged in small crystals of carbonated hydroxyapatite with dimensions of 36 × 25 × 4 nm, and by an organic phase whose main component is type l collagen in 90%, which is oriented in the form of a mesh. This conformation corresponds to permanent teeth. Within the structures, we find dentin tubules that measure approximately 0.5-1 µm in diameter at the periphery and up to 3-5 µm near the pulp. In the present study, carried out in dentin of primary teeth, the lumen of these tubules is larger when it is close to the dental pulp. Likewise, important elemental changes were found according to the different depths in which it was observed, finding an increase in the percentage weight of carbon when it is at a greater depth, indicating a greater organic composition in the pulp dentin. In studies of permanent teeth, this composition is decreased and with a higher concentration in the dentin near the amelodentinal junction. In dentin of primary teeth, differences were found in the count of dentin tubules per mm2, compared to dentin of permanent teeth, where the number of tubules did not vary much (AU)

Influence of laser deproteinization of acid-etched dentin on marginal microleakage of class V composite restoration

Aim: Recent reports indicate that deproteinization of acid-etched dentin surface can extend penetration depth of adhesive agents. The main goal of the present research was to investigate the deproteinization effect of Nd:YAG and diode 940 lasers on acid-etched dentin and microleakage grade in class V composite restorations. Methods: 36 extracted human premolar teeth were selected to make standard buccal and lingual class V cavities. These samples were randomly split into three sub-groups: 1.Control group, in which composite was applied for restoration after etch and bonding process without deproteinization; 2.Nd:YAG laser group, in which the teeth were deproteinized with Nd:YAG laser after etching and painting internal surfaces of cavities with Van Geison stain and then composite restorations applied just as control group; 3.Diode laser group, in which the process was similar to Nd:YAG laser group, but instead, diode 940 laser was irradiated. The teeth were bisected into two equal longitudinal buccal and lingual halves. Marginal microleakage of samples was scored by using a stereomicroscope. Kruskal- Wallis, Mann-Whitney U and Fisher's statistical tests were employed for analysis of the obtained data. Results: A significant reduction in marginal microleakage was observed for both groups treated with laser (Nd:YAG and diode 940)compared to control (p=0.001 & p=0.047). There was no significant difference in marginal microleakage between Nd:YAG laser and diode 940groups (P = 0.333). Conclusion: Nd:YAG and diode 940 laser deproteinization of acid-etched dentin decreased the marginal microleakage of in-vitro class V resin composite restorations

A Comparison Between Phosphoric Acid- and Er:YAG Laser-Mediated Re-Etching of Enamel for Orthodontic Bracket Re-Bonding.

Objective: This study sought to compare enamel surface morphology and orthodontic bracket re-bonding strength after phosphoric acid- or erbium-doped yttrium aluminum garnet (Er:YAG) laser-mediated re-etching. Methods: A total of 81 extracted premolars were obtained from patients undergoing orthodontic procedures. Conventional etching with 35% phosphoric acid was first used to bond brackets to the enamel surface. Then brackets were de-bonded 1 week later. These samples were then separated randomly into three groups (n = 27 teeth each group) and re-bonded with new brackets after one of the following re-etching manners: Group A-35% phosphoric acid, Group B-Er:YAG laser (200 mJ, 30 Hz), and Group C-Er:YAG laser (250 mJ, 30 Hz). The enamel surface and the interface of enamel and adhesive were then analyzed through scanning electron microscopy. Shear bond strength (SBS) and adhesive remnant index (ARI) were also measured. Results: Samples in Group A exhibited significant residual adhesive at the enamel surface, whereas samples in Groups B and C showed a cleaner surface with more distinct and evenly distributed honeycomb-like structures. Further, samples in Group C displayed a larger average SBS value between the two laser-etching groups, although there were no significant differences in SBS values or ARI scores between the acid and laser re-etching groups (p > 0.05). Conclusions: Er:YAG laser-based enamel re-etching (250 mJ, 30 Hz) produces an uniform honeycomb-like structure and a trend of similar SBS compared with 35% phosphoric acid-mediated re-etching. Er:YAG laser-mediated re-etching seems to be a promising alternative approach for bracket re-bonding.

Sistemas adesivos universais ­ há 10 anos no Brasil: revisão de literatura / Universal adhesive systems ­ 10 years in Brasil: literature review

Objetivo: analisar, a partir da literatura publicada, os sistemas adesivos universais, conceituando sobre seu desempenho nos diferentes substratos, assim como potenciais estudos executados com eles após 10 anos no Brasil. Materiais e métodos: para esta revisão narrativa, foram pesquisados artigos na língua inglesa nas bases de dados eletrônicas PubMed/Medline, SciELO e Scopus, publicados de 2012 a 2022, período considerado por ser a última década, além dos 10 anos da chegada do sistema adesivo universal ao Brasil. Utilizaram-se os seguintes descritores: universal adhesives (adesivos universais) OR universal adhesive system (sistemas adesivos universais). Realizou-se a inclusão de estudos laboratoriais (in vitro), ensaios clínicos, revisões de literatura e sistemáticas com meta-análise. Resultados: após análise meticulosa, foram selecionados 56 estudos. Os adesivos universais são considerados mais "amigáveis" ao usuário, pois permitem ao clínico a utilização no modo condicione e lave e autocondicionante, principalmente devido à inclusão do monômero MDP ou de monômeros similares. No esmalte, o condicionamento ácido seletivo antes da aplicação do adesivo é recomendado. Permite ser utilizado com uma diversidade de substratos, a aplicação de forma ativa do adesivo melhora a resistência de união. Conclusão: os sistemas adesivos universais foram lançados para tornar os procedimentos de adesão mais simples. Entretanto, mais ensaios clínicos com maiores tempos de acompanhamento são necessários, para avaliar adequadamente a efetividade desse material.(AU)

Objective: To evaluate, from published literature, the universal adhesive systems, conceptualizing their performance, as well as potential studies performed using this material. MATERIAL AND METHODS: This narrative review considered articles in the English language searched on Pubmed/ Medline, Scielo and Scopus from 2012 to 2022, considered period to be the last decade, besides ten years of the universal adhesive system arrived in Brazil. The descriptors "universal adhesive" or "universal adhesive systems" were used. Laboratorial studies (in vitro), clinical trials, literature review and systematic review with meta-analysis were included. RESULTS: 56 studies were included. The universal adhesives are considered more user-friendly, allowing for etch & rinse and self-etch modes, mostly due to MDP monomer or similar monomers inclusion. In enamel selective acid etching before adhesive application is recommended. The system can be used with great amount of substrates and results in superior bond strength when applied through active mode. CONCLUSION: Universal adhesive systems were launched to simplify the adhesion procedure, however more clinical trials with longer follow-ups are required using this material, with adequate evaluation of their effectiveness.(AU)

Eficacia del cementado indirecto / Indirect bonding efficiency

La aparición de aparatología preadjustada ha colaborado en la efectividad de los tratamientos de ortodoncia, pero para que la expresión de esta aparatología se logre, es necesario una correcta colocación de los brackets y la permanencia de estos en boca durante todo el tratamiento. La precisión en la colocación mejora con la técnica de cementado indirecta, ya que permite el acceso a las zonas posteriores, a lugares donde se ve disminuida la visión y además disminuye la condensación de aliento y contaminación salival. Si bien esta técnica requiere tiempo extra de laboratorio, es más rápida en la etapa clínica (AU)