RESUMO
This study evaluated the effect of contamination of composite resins (CRs) handled by undergraduate students during restorative procedures, varying the time (baseline, 30 days and 60 days) and experimental condition (before and after handling, contamination with saliva [positive control] and photoactivation). Eight CR tubes were randomly distributed at the dental clinic and the samples were organized into four groups: CR fragments collected before (GB) and after (GA) the restorative procedure; CR fragments contaminated with saliva (GS) and photoactivated (GP) both collected after the procedure. These 4 groups were evaluated in 3 different times: baseline (after sealing), 30 days and 60 days of use of the CR. Samples that had positive turbidity in Brain HeartInfusion (BHI) broth were sown in BHI and Sabouraud Dextrose (SB) agars for subsequent counting of Colony Forming Units (CFU mL-1). The results showed that the handling was responsible for increasing contamination (p < 0.05) at the baseline (GB [n = 0] and GA [n = 3]), as well as after 30 (GB [n = 1] and GA [n = 6]) and 60 (GB [n = 1] and GA [n = 5]) days of use. Photoactivation was responsible for the reduction for microorganisms in T0 and T60. Additionally, the time use and conservation did not influencethe contamination of CRs. Handling was responsible for the increase of contamination of CR, the photoactivation seems to reduce the number of viable microorganisms and the time of use seems not to potentiate the effect of tube contamination.
Assuntos
Indicadores de Contaminação , Resinas Compostas/análise , Boas Práticas de Manipulação , Cura Luminosa de Adesivos Dentários/instrumentação , Estudantes de Odontologia , Interpretação Estatística de Dados , Recuperação e Remediação Ambiental , Conservantes de Alimentos/análise , Microbiologia/instrumentaçãoRESUMO
Abstract Objective: To evaluate the effect of two types of light-curing units (second and third generations) and two types of bulk-fill composite resins with different photoinitiators - Tetric N-Ceram Bulk Fill (TNCB) and Xtra Fil (XTF) on gap formation at the gingival margins of Cl II restorations. Material and Methods: Fifty-six standard Cl II cavities were prepared on the mesial and distal surfaces of premolar teeth, with the gingival margin of the cavities 1 mm apical to the CEJ. The samples were randomly assigned to two groups based on the composite resin type and two subgroups based on the light-curing unit type and restored. After 5000 rounds of thermocycling, gingival margin gap in each sample was measured in µm under an electron microscope at ×2000 magnification. Data were analyzed by two-way ANOVA and Tukey tests (α=0.05). Results: Marginal gaps of TNCB composite resin were significantly smaller than those of XTF composite resin (p<0.001). There were no significant differences between the two light-curing units in each group (p=0.887 with XTF and p=0.999 with TNCB). Conclusion: The gaps at gingival margins of Cl II cavities with TNCB bulk-fill composite were smaller than XTF composite resin. Both composite resins can be cured with both the second- and third-generation LEDs (AU).
Assuntos
Humanos , Dente Pré-Molar , Adaptação Marginal Dentária , Resinas Compostas/química , Cura Luminosa de Adesivos Dentários/instrumentação , Fotoiniciadores Dentários/química , Técnicas In Vitro/métodos , Microscopia Eletrônica de Varredura/instrumentação , Análise de VariânciaRESUMO
Abstract: Aim: Sufficient polymerization remains as crucial for composites to prevent discoloration. Both LEDs and halogen units are used for polymerization and different curing modes are improved to overcome inadequate polymerization. This in vitro study investigated staining susceptibility of a nano-hybrid resin composite light-cured in different modes and immersed in different staining media. Methods: Disc-shaped specimens were prepared from nano-hybrid resin composite (Filtek Z550) and light- cured according to following modes: Halojen (GI), LED standard (GII), LED pulse (GIII) or LED ramp (GIV). Half of the specimens of each group (n=7) were stored in one of the staining media (red wine or coffee) for 10 min/day during experimental period. Measurements were performed using spectrophotometer according to CIEL*a*b system at baseline and on 7, 28 and 56 days. Colour differences (∆E) between groups were submitted to statistical analysis. Results: Regarding 7-day evaluation, colour change values of specimens immersed in coffee revealed no remarkable difference among curing modes (p>0.05); whereas specimens in GIV were significantly less stained compared to specimens in GII and GIII when immersed in red wine. Regarding 56- days of evaluation, specimens of GIV showed statistically significant colour change in red wine compared to other groups. However specimens in GI revealed the least staining after 56-days of coffee immersion, and this result was statistically different from LED groups. Conclusion: This study suggest that light-curing mode influences the staining susceptibility of the tested composite. Composites polymerized with halogen unit showed lower staining than all LED modes. Despite novel light sources, halogen units may still used reliably at clinics.
Resumen: Objetivo: La polimerización suficiente sigue siendo crucial para que los compuestos eviten la decoloración. Tanto los LED como las unidades halógenas se utilizan para la polimerización y se mejoran los diferentes modos de curado para superar la polimerización inadecuada. Este estudio in vitro investigó la susceptibilidad a la tinción de un compuesto de resina nano-híbrida curado a la luz en diferentes modos y se sumergió en diferentes medios de tinción. Métodos: Las muestras en forma de disco se prepararon a partir de un compuesto de resina nano-híbrida (Filtek Z550) y se curaron con luz de acuerdo con los siguientes modos: Halojen (GI), estándar de LED (GII), pulso de LED (GIII) o rampa de LED (GIV). La mitad de las muestras de cada grupo (n = 7) se almacenaron en uno de los medios de tinción (vino tinto o café) durante 10 minutos / día durante el período experimental. Las mediciones se realizaron utilizando un espectrofotómetro de acuerdo con el sistema CIEL * a * b en la línea de base y en 7, 28 y 56 días. Las diferencias de color (∆E) entre los grupos se sometieron a análisis estadístico. Resultados: Con respecto a la evaluación de 7 días, los valores de cambio de color de las muestras sumergidas en café no revelaron diferencias notables entre los modos de curado (p> 0.05); mientras que las muestras en GIV se tiñeron significativamente menos en comparación con las muestras en GII y GIII cuando se sumergieron en vino tinto. Con respecto a los 56 días de evaluación, las muestras de GIV mostraron un cambio de color estadísticamente significativo en el vino tinto en comparación con otros grupos. Sin embargo, las muestras en GI revelaron la menor tinción después de 56 días de inmersión en el café, y este resultado fue estadísticamente diferente de los grupos LED. Conclusión: este estudio sugiere que el modo de fotopolimerización influye en la susceptibilidad de tinción del material compuesto probado. Los compuestos polimerizados con una unidad halógena mostraron una tinción más baja que todos los modos LED. A pesar de las nuevas fuentes de luz, las unidades halógenas todavía pueden usarse de manera confiable en las clínicas.
Assuntos
Descoloração de Dente/diagnóstico , Resinas Compostas , Cura Luminosa de Adesivos Dentários/instrumentaçãoRESUMO
Abstract Contemporary dentistry literally cannot be performed without use of resin-based restorative materials. With the success of bonding resin materials to tooth structures, an even wider scope of clinical applications has arisen for these lines of products. Understanding of the basic events occurring in any dental polymerization mechanism, regardless of the mode of activating the process, will allow clinicians to both better appreciate the tremendous improvements that have been made over the years, and will also provide valuable information on differences among strategies manufacturers use to optimize product performance, as well as factors under the control of the clinician, whereby they can influence the long-term outcome of their restorative procedures.
Assuntos
Lâmpadas de Polimerização Dentária , Cimentos Dentários/química , Cura Luminosa de Adesivos Dentários/instrumentação , Cura Luminosa de Adesivos Dentários/métodos , Fotoiniciadores Dentários/química , Polimerização , Absorção de Radiação , Cimentos Dentários/efeitos da radiação , Restauração Dentária Permanente/instrumentação , Restauração Dentária Permanente/métodos , Polimerização/efeitos da radiação , Doses de Radiação , Temperatura , Fatores de TempoRESUMO
Introdução: uma complicação inerente a todas as resinas compostas é o stress gerado pela contração de polimerização. As resinas compostas da atualidade, após a polimerização, perdem entre 2% a 3% de todo o seu volume. Essa perda pode acarretar em alterações fortemente comprometedoras a nível micro e macroscópico. Objetivo: abordar a importância do uso de técnicas e manobras clínicas, que visam diminuir a contração de polimerização das resinas compostas, reduzindo seus efeitos na cavidade, para que se tenha um procedimento restaurador com elevado índice de sucesso clínico e boa aceitação pelos pacientes. Material e Métodos: foi realizada uma revisão da literatura por meio de uma busca bibliográfica nas seguintes bases de pesquisa online: PUBMED/MEDLINE, LILACS, BBO e SCIENCE DIRECT, através do rastreio de artigos relevantes publicados entre o período de 2000 a 2015. Resultados: comparando as formas de ativação dos compósitos, os compósitos fotopolimerizáveis possuem um menor escoamento e maior stress de contração se comparados a compósitos com ativação química, isso se dá devido à fotoativação que se destaca por ser uma reação rápida quando comparada a outros métodos, não dispondo de tempo para a resina se acomodar na cavidade e ter uma boa interação com o sistema adesivo previamente aplicado, levando a grande parte dos problemas clínicos das restaurações. Conclusão: questionamentos sobre os efeitos da contração de polimerização, ainda não foram completamente elucidados no meio científico, por isso algumas técnicas como a escolha de fotopolimerizadores a LED, manutenção da fase pré gel, manutenção do Fator C e técnica de inserção incremental, podem ser usadas para minimizar os efeitos dessa contração nas restaurações feitas com resina, afim de reduzir insucessos como, sensibilidade pós operatória, infiltração marginal e riscos de agressão pulpar levando a uma maior longevidade dos procedimentos restauradores com materiais resinosos. (AU)
Introduction: a complication inherent in all composite resins is the stress generated by the polymerization contraction. The present composite resins, after polymerization, lose between 2% and 3% of their entire volume. This loss can lead to strongly compromising micro and macroscopic changes. Objective: to address the importance of using technical and clinical maneuvers, which aim to reduce polymerization shrinkage of composite resins, reducing its effects in the cavity, in order to have a restorative procedure with high clinical success rate and good patient acceptance. Material and Methods: a review of the literature through a literature search in the following search online databases was performed: PubMed/MEDLINE, LILACS, BBO and SCIENCE DIRECT, through the screening of relevant articles published between 2000 to 2015. Results: comparing both activation of composites, the dental composites have a lower flow and higher stress of contraction compared to composites with chemical activation, this is the due to photoactivation that stands out for being a quick reaction when compared to other methods, not providing time for the resin to settle in well and have a good interaction with the previously applied adhesive system, leading to much of the clinical problems of restorations. Conclusion: questions about the effects of polymerization shrinkage have not been fully elucidated in the scientific community, so some techniques such as the choice of curing lights to LED, the pre gel phase maintenance, maintenance of Factor C and incremental insertion technique can It is used to minimize the effects of this contraction in restorations made with resin in order to reduce failures as post-operative sensitivity, microleakage and pulp assault risks leading to increased longevity of restorative procedures with resinous materials. (AU)
Assuntos
Resinas Compostas/administração & dosagem , Autocura de Resinas Dentárias/instrumentação , Cura Luminosa de Adesivos Dentários , Cura Luminosa de Adesivos Dentários/instrumentação , Fotoiniciadores Dentários/classificação , Resinas Sintéticas/administração & dosagem , Literatura de Revisão como Assunto , Preparo da Cavidade Dentária/instrumentação , Infiltração Dentária/reabilitação , Materiais Dentários/efeitos adversos , PolimerizaçãoRESUMO
The present study aimed to assess the influence of curing distance on the loss of irradiance and power density of four curing light devices. The behavior in terms of power density of four different dental curing devices was analyzed (Valo, Elipar 2, Radii-Cal, and Optilux-401) using three different distances of photopolymerization (0 mm, 4 mm, and 8 mm). All devices had their power density measured using a MARC simulator. Ten measurements were made per device at each distance. The total amount of energy delivered and the required curing time to achieve 16 J/cm2 of energy was also calculated. Data were statistically analyzed with one-way analysis of variance and Tukey’s tests (p < 0.05). The curing distance significantly interfered with the loss of power density for all curing light devices, with the farthest distance generating the lowest power density and consequently the longer time to achieve an energy density of 16 J/cm2 (p < 0.01). Comparison of devices showed that Valo, in extra power mode, showed the best results at all distances, followed by Valo in high power mode, Valo in standard mode, Elipar 2, Radii-Cal, and Optilux-401 halogen lamp (p < 0.01). These findings indicate that all curing lights induced a significant loss of irradiance and total energy when the light was emitted farther from the probe. The Valo device in extra power mode showed the highest power density and the shortest time to achieve an energy density of 16 J/cm2 at all curing distances.
Assuntos
Lâmpadas de Polimerização Dentária , Resinas Compostas/efeitos da radiação , Cura Luminosa de Adesivos Dentários/instrumentação , Cura Luminosa de Adesivos Dentários/métodos , Análise de Variância , Resinas Compostas/química , Equipamentos Odontológicos , Teste de Materiais , Polimerização/efeitos da radiação , Doses de Radiação , Equipamentos e Provisões para Radiação , Valores de Referência , Reprodutibilidade dos Testes , Estatísticas não Paramétricas , Fatores de TempoRESUMO
OBJECTIVE: The purpose of this study was to investigate the effects of various surface pretreatments in the ridge lap area of acrylic resin denture teeth on the shear bond strength to heat-polymerized polymethylmethacrylate (PMMA) denture base resin. BACKGROUND DATA: Tooth debonding of the denture is a major problem for patients with removable prostheses. METHODS: A total of 84 central incisor denture teeth were used in this study. Seven test groups with 12 specimens for each group were prepared as follows: untreated (control, group C), ground, with a tungsten carbide bur (group H), airborne-particle abrasion (group AA), primed with methyl methacrylate (group M), treated with izobutyl methacrylate (group iBMA), Eclipse Bonding Agent applied (group E), and Er:YAG laser irradiated (group L). Test specimens were produced according to the manufacturers' instructions and mounted to a universal testing machine for shear testing with a crosshead speed of 1 mm/min. Data were evaluated by one way variance analysis (ANOVA) and Tukey's test (α=0.05). RESULTS: Similar bond strength values were found between groups L and M, and these were the highest shear bond strengths among the groups. The lowest one was observed in group E. All surface treatments, except group E, exhibited significant difference when compared with group C (p<0.05). CONCLUSIONS: Lasing of the ridge lap area to enhance the bond strength of acrylic resin denture teeth to PMMA denture base resin might be an alternative to wetting with MMA monomer. To overcome tooth debonding, surface treatment of the ridge lap area should be performed as part of denture fabrication.
Assuntos
Colagem Dentária/métodos , Bases de Dentadura , Dentaduras , Lasers de Estado Sólido , Cura Luminosa de Adesivos Dentários/instrumentação , Polimetil Metacrilato/química , Resinas Acrílicas/química , Resinas Compostas/química , Descolagem Dentária , Análise do Estresse Dentário , Incisivo , Teste de Materiais , Metacrilatos/química , Propriedades de SuperfícieRESUMO
OBJECTIVE: development of a new device to be coupled to light-curing units for bonding orthodontic brackets and accessories, and test its efficacy in an in vitro mechanical trial. The inner surface of the device is mirrored and is based on physical concepts of light refraction and reflection. The main advantage of such device is the reduced clinical time needed for bonding and the low possibility of contamination during the process. METHODS: One hundred and twenty specimens were used for testing the shear bond strength of brackets bonded with the device. The Adhesive Remnant Index (ARI) was also determined. The sample was divided into 2 groups. In group 1 a halogen light-curing unit was used while in group 2 a led light-curing unit was used. Each group was then subdivided. In subgroups H1 and L1, a conventional light guide rod was used while in subgroups H2 and L2 bonding was performed with the mirrored device coupled to the tip of the guide light rod. RESULTS: The values obtained for the shear bond strength and the ARI in the subgroups were compared. Results showed that there was no statistically significant difference for the shear strength (p > 0.05) and the ARI (p > 0.05) between the subgroups. CONCLUSION: The tests of mechanical trials and the ARI analysis showed that the new device fulfilled the requirements for bonding orthodontic accessories, and that the time for bonding was reduced to half, being necessary only one light exposure.
OBJETIVO: desenvolver uma nova ponteira para ser acoplada aos aparelhos fotopolimerizadores utilizados para colagem de braquetes e acessórios ortodônticos, e testar sua da efetividade em ensaio mecânico in vitro. A ponteira é espelhada na superfície interna e baseia-se em conceitos físicos de refração e reflexão de luz. Apresenta como principal vantagem o menor tempo clínico durante o procedimento de colagem, reduzindo a possibilidade de contaminação durante o processo. MÉTODOS: por meio de ensaio de resistência ao cisalhamento e determinação do índice remanescente de adesivo (IRA), testou-se a ponteira desenvolvida em 120 corpos de prova. A amostra foi dividia em dois grupos. No grupo 1, foi utilizado aparelho fotopolimerizador de fonte de luz halógena e, no grupo 2, fonte de LED. Cada grupo foi subdividido. Nos subgrupos H1 e L1, utilizou-se a ponteira convencional. Nos subgrupos H2 e L2 a colagem foi feita utilizando a ponteira desenvolvida para a polimerização do material de colagem. RESULTADOS: os valores dos testes de cisalhamento e IRA para os subgrupos foram comparados entre si. Os resultados mostraram que não houve diferença estatisticamente significativa para o ensaio de resistência ao cisalhamento (p > 0,05) nem para o IRA (p > 0,05) entre os subgrupos. CONCLUSÃO: os testes de ensaio mecânico, assim como a análise do IRA, mostraram que a nova ponteira desenvolvida cumpriu os requisitos necessários à colagem dos acessórios ortodônticos, e que o tempo de colagem foi reduzido pela metade, sendo necessária uma só incidência.
Assuntos
Humanos , Lâmpadas de Polimerização Dentária , Colagem Dentária/instrumentação , Cura Luminosa de Adesivos Dentários/instrumentação , Braquetes Ortodônticos , Adesividade , Lâmpadas de Polimerização Dentária/classificação , Análise do Estresse Dentário/instrumentação , Desenho de Equipamento , Contaminação de Equipamentos/prevenção & controle , Teste de Materiais , Fibras Ópticas , Cimentos de Resina/química , Cimentos de Resina/efeitos da radiação , Resistência ao Cisalhamento , Estresse Mecânico , Propriedades de Superfície , Fatores de TempoRESUMO
This study evaluated the temperature variation in the pulp chamber during photoactivation of two restorative composite resins (Filtek P90 silorane-based composite and Heliomolar methacrylate-based composite) with either a quartz-tungsten-halogen (QTH) or light-emitting diodes (LED) light-curing unit (LCU) and using dentin thicknesses (0.5 and 1.0 mm). Standardized cavities (2x2x2 mm) were prepared in 80 bovine incisors, which were randomly assigned to 8 groups according to the photoactivation method and dentin thickness. Filtek P90 and Heliomolar (both in shade A3) were used with their respective adhesive systems (P90 self-etch primer / P90 adhesive bond and Excite adhesive). All experiments were carried out in a controlled environment (37°C). The temperature variations (°C) were recorded using a digital thermometer attached to a K-type thermocouple. The results were analyzed statistically by ANOVA and Tukey's test (α=0.05). For composite/dentin thickness interaction, temperature increase was significantly higher in 0.5 mm dentin thickness (40.07°C) compared with 1.0 mm dentin thickness (39.61°C) for Filtek P90. For composite/LCU interaction, the temperature increase was significantly higher for Filtek P90 (39.21°C - QTH and 40.47°C - LED) compared with Heliomolar (38.40°C - QTH and 39.30°C - LED). The silorane-based composite promoted higher temperature increase in the pulp chamber than the methacrylate-based composite.
Este estudo avaliou a variação de temperatura na câmara pulpar durante a fotoativação de duas resinas compostas (Filtek P90 – compósito à base de silorano e Heliomolar – compósito à base de metacrilato) com as unidades foto-ativadoras (UFs) luz de quartzo-tungstênio-halogênio (QTH) ou diodo emissor de luz (LED) e utilizando espessuras de dentina (0,5 e 1,0 mm). Cavidades padronizadas (2×2×2 mm) foram preparadas em 80 incisivos bovinos, as quais foram aleatoriamente divididas em 8 grupos de acordo com os métodos de fotoativação e espessura da dentina. Filtek P90 e Heliomolar (ambos na cor A3) foram utilizadas com seus respectivos sistemas adesivos (Primer P90 auto-condicionante / adesivo P90 e adesivo Excite). Todos os experimentos foram realizados em um ambiente controlado (37°C). As variações de temperatura (°C) foram mensuradas usando um termômetro digital conectado a um termopar tipo-K. Os resultados foram analisados estatisticamente por ANOVA e teste de Tukey (α=0,05). Para interação compósito/espessura de dentina, o aumento da temperatura foi estatisticamente superior para a espessura de dentina de 0,5 mm (40,07°C) quando comparado com a espessura de dentina de 1,0 mm (39,61°C) para a Filtek P90. Para a interação compósito/UFs, o aumento de temperatura foi estatisticamente superior para o Filtek P90 (39,21°C – QTH e 40,47°C – LED) quando comparado ao Heliomolar (38,40°C – QTH e 39,30°C – LED). Compósitos à base de silorano promovem maior aumento da temperatura na câmara pulpar em relação aos compósitos à base de metacrilato.
Assuntos
Animais , Bovinos , Resinas Acrílicas/química , Resinas Compostas/química , Lâmpadas de Polimerização Dentária/classificação , Materiais Dentários/química , Dentina/ultraestrutura , Poliuretanos/química , Resinas de Silorano/química , Bis-Fenol A-Glicidil Metacrilato/química , Temperatura Corporal/fisiologia , Preparo da Cavidade Dentária/métodos , Cavidade Pulpar/fisiologia , Temperatura Alta , Cura Luminosa de Adesivos Dentários/instrumentação , Teste de Materiais , Metacrilatos/química , Polimerização , Distribuição Aleatória , TermômetrosRESUMO
The purpose of this study was to evaluate in vitro the shear bond strength to enamel, flexural strength, flexural modulus, and contraction stress of one orthodontic composite and two flowable composites. Orthodontic brackets were bonded to 45 human maxillary premolars with the composites Transbond XT, Filtek Z-350 flow and Opallis flow and tested for shear bond strength. For measurement of flexural strength and flexural modulus, specimens were fabricated and tested under flexion. For the contraction stress test, cylindrical specimens were tested and an extensometer determined the height of the specimens. The data were subjected to one-way ANOVA and Tukey's test (α=0.05). The shear bond strength values were significantly lower (p<0.05) for the flowable composites compared with the orthodontic composite. For the flexural strength, no statistically significant difference was found among the composites (p>0.05) while the flexural modulus was significantly higher (p<0.05) for Transbond XT than for Filtek Z-350 flow and Opallis flow. The orthodontic composite presented significantly lower contraction stress values than the flowable composites (p<0.05). The light-activated orthodontic composite material presented higher flexural modulus and shear bond strength and lower contraction stress than both flowable composites.
O objetivo desse estudo foi avaliar a resistência ao cisalhamento no esmalte, resistência flexural, módulo flexural, tensão de contração de polimerização de duas resinas flow e uma resina ortodôntica. Os bráquetes ortodônticos foram colados em 45 pré-molares humanos e divididos: Transbond XT, Filtek Z-350 flow, Opallis flow e testado para resistência ao cisalhamento (n=15). Para a resistência e módulo flexural espécimes foram confeccionados e testados sob flexão. Para o teste de tensão de contração de polimerização, espécimes cilíndricos foram confeccionados e monitorados com um extensômetro (Instron). Os dados foram submetidos aos testes ANOVA a um critério e Tukey (α=0,05) para contraste de média. (n=15). A resistência de união das resinas flow foram significantemente menos que o da resina ortodôntica (p>0,05). A resistência flexural não demonstrou diferença significante entre os grupos testados (p>0,05). O módulo flexural da resina ortodôntica foi significantemente maior que o grupo das resinas flow (p<0,05). A tensão de contração de polimerização da resina ortodôntica foi significantemente menor (p<0,05). A resina ortodôntica obteve os maiores valores de resistência de união ao cisalhamento, resistência flexural e a menor tensão de contração de polimerização quando comparada as resinas flow testadas.
Assuntos
Humanos , Resinas Compostas/química , Colagem Dentária , Aparelhos Ortodônticos , Cimentos de Resina/química , Adesividade , Condicionamento Ácido do Dente/métodos , Bis-Fenol A-Glicidil Metacrilato/química , Cimentos Dentários/química , Esmalte Dentário/ultraestrutura , Análise do Estresse Dentário/instrumentação , Módulo de Elasticidade , Cura Luminosa de Adesivos Dentários/instrumentação , Teste de Materiais , Metacrilatos/química , Maleabilidade , Polimerização , Ácidos Fosfóricos/química , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Resistência ao Cisalhamento , Estresse MecânicoRESUMO
OBJECTIVE: Light-curable polymers are commonly used in restorative surgery, prosthodontics and surgical procedures. Despite the fact of wide application, there are clinical problems due to limitations of blue light penetration: application is restricted to defects exposed to the light source, layered filling of defect is required. METHODS: Combining photo-activation and up conversion allows efficient polymer hardening by deep penetrating near-infrared (NIR) light. The prerequisite 450 nm blue light to polymerize dental resins could be achieved by filler particles, which absorb the incident NIR irradiation and convert it into visible light. RESULTS: The on spot generated blue light results in uniform polymer hardening. Composite samples of 5mm thickness were cured two times faster than pure polymer cured by blue light (30 and 60 s, respectively). Overall degree of monomer conversion resulted in higher values of more than 40%. The enhanced transmission of NIR light was confirmed by optical analysis of dentin and enamel. The NIR transmittance surge in the 800-1200 nm window could improve sealing of complex and deep caries lesions. SIGNIFICANCE: We demonstrate faster curing and an improved degree of polymerization by using upconversion filler particles as multiple light emission centers. This study represents an alternative approach in curing dental resins by NIR source.
Assuntos
Resinas Compostas/química , Cura Luminosa de Adesivos Dentários/instrumentação , Cura Luminosa de Adesivos Dentários/métodos , Substâncias Luminescentes , Polímeros/química , Animais , Bovinos , Resinas Compostas/efeitos da radiação , Dureza , Raios Infravermelhos , Teste de Materiais , Tamanho da Partícula , Polimerização , Polímeros/efeitos da radiação , Espalhamento de RadiaçãoRESUMO
The aim of this study was to assess the bond strength of a resin cement to intraradicular dentin varying the light-curing unit and the moment at which the light was applied. Post spaces of endodontically treated canines were prepared. The roots were distributed into 6 groups (n=10) according to the light-curing unit and the moment of light exposure: I) Quartz tungsten halogen-600 mW/cm² (QTH) + immediate light activation (t0); II) QTH + light activation after 10 min (t10); III) Light-emitting diodes (LED)-800 mW/cm² (LED-800)+ t0; IV) LED-800 + t10; V) LED-1,500 mW/cm² (LED-1500)+ t0; VI) LED-1500 + t10. After post cementation, slices from coronal, middle and apical post/root regions were submitted to the push-out test and failure evaluation. It was verified that LED-800 (4.40 ± 3.00 MPa) and LED-1500 (4.67 ± 3.04 MPa) provided bond strength statistically superior to QTH (3.13 ± 1.76 MPa) (p<0.05), and did not differ from each other (p>0.05). There was no significant difference between t0 and t10 (p>0.05). Coronal post/root region (4.75 ± 3.10 MPa) presented significantly higher bond strength than the apical (3.32 ± 2.30 MPa) (p<0.05) and middle regions (4.14 ± 2.99 MPa) showed intermediate values. Adhesive failures were predominant when using QTH. Adhesive and mixed failures occurred more frequently in the apical region. Higher adhesion of the resin cement to intraradicular dentin was observed in the coronal region with LED light-activation, regardless of the moment of light exposure.
O objetivo deste estudo foi avaliar a resistência de união do cimento resinoso à dentina intrarradicular em função da fonte fotoativadora e do momento de aplicação da luz. Os espaços para cimentação dos pinos foram preparados em caninos tratados endodonticamente. As raízes foram distribuídas em seis grupos (n = 10) de acordo com a fonte fotoativadora e momento de exposição à luz: I) Luz halógena (LH) com densidade de potência 600 mW/cm² + fotoativação imediata (t0); II) LH + fotoativação após 10 min (t10); III) LED com densidade de potência 800 mW/cm² (LED-800)+ t0; IV) LED-800 + t10; V) LED com densidade de potência 1.500 mW/cm² (LED-1500)+ t0; VI) LED-1500 + t10. Após a cimentação dos pinos, slicesdas regiões cervical, média e apical foram submetidos ao teste de push-out e avaliação das falhas. Verificou-se que LED-800 (4,40 ± 3,00 MPa) e LED-1500 (4,67 ± 3,04 MPa) proporcionaram resistência de união estatisticamente superior à LH (3,13 ± 1,76 MPa) (p<0,05), e não diferiram entre si (p>0,05).Não houve diferença estatisticamente significante da resistência de união entre t0 e t10 (p>0,05). A região cervical (4,75 ± 3,10 MPa) apresentou maiores valores de resistência de união que a apical (3,32 ± 2,30 MPa) (p<0,05) e a região média (4,14 ± 2,60 MPa) mostrou valores intermediários. Falhas adesivas foram predominantes no grupo LH, independentemente da região pino/canal. A parte apical apresentou predomínio de falhas adesivas e mistas. Concluiu-se que a resistência de união do cimento resinoso à dentina intrarradicular foi maior no terço cervical,com fotoativação com LED, independente do momentode exposição à luz.
Assuntos
Humanos , Lâmpadas de Polimerização Dentária/classificação , Colagem Dentária , Dentina/ultraestrutura , Cura Luminosa de Adesivos Dentários/métodos , Cimentos de Resina/química , Adesividade , Cimentação/métodos , Resinas Compostas/química , Dente Canino/ultraestrutura , Materiais Dentários/química , Cavidade Pulpar/ultraestrutura , Análise do Estresse Dentário/instrumentação , Vidro/química , Umidade , Cura Luminosa de Adesivos Dentários/instrumentação , Teste de Materiais , Metacrilatos/química , Técnica para Retentor Intrarradicular/instrumentação , Cimentos de Resina/efeitos da radiação , Preparo de Canal Radicular/métodos , Estresse Mecânico , Temperatura , Fatores de Tempo , Ápice Dentário/ultraestrutura , Dente não Vital/terapiaRESUMO
This study evaluated the transdentinal cytotoxicity (TC) and the bond strength (BS) of a resin-modified glass-ionomer cement (RMGIC) applied to dentin covered with smear layer (SL) of different thicknesses. Forty dentin discs had thick (TSL) or thin (THSL) smear layer created on their occlusal side. In artificial pulp chambers, MDPC-23 cells were seeded on the pulpal side of the dentin discs and divided into five groups: G1TC: no treatment (control); G2TC: TSL + RMGIC; G3TC: THSL + RMGIC; G4TC: TSL removal + RMGIC; G5TC: THSL removal + RMGIC. After 24 h, cell metabolism and morphology were evaluated by the methyltetrazolium (MTT) assay and by scanning electron microscopy (SEM), respectively. For BS, the following groups were determined: G1BS: TSL removal + RMGIC; G2BS: THSL removal + RMGIC; G3BS: TSL + RMGIC; G4BS: THSL + RMGIC. Shear bond strength was tested to failure in a mechanical testing machine MTS (0.5 mm/min). Statistically significant difference was observed only between the control and experimental groups (Kruskal-Wallis, p<0.05). The metabolic activity of the viable MDPC-23 cells in G2TC, G3TC, G4TC and G5TC decreased by 54.85%, 60.79%, 64.12% and 62.51%, respectively. Mean shear bond strength values for G1BS, G2BS, G3BS and G4BS were 7.5, 7.4, 6.4 and 6.7 MPa, respectively, without significant difference among them (ANOVA, p>0.05). RMGIC presented moderate transdentinal cytotoxic effects. Maintenance or removal of smear layer did not affect the bond strength of RMGIC to dentin substrate.
Este estudo avaliou a citotoxicidade transdentinária (CT) e a resistência de união (RU) de um cimento de ionômero de vidro modificado por resina (CIVMR) aplicado sobre dentina coberta com smear layer (SL) de diferentes espessuras. Quarenta discos de dentina tiveram smear layer espessa (TSL) ou delgada (THSL) criadas sobre a superfície oclusal. Após terem sido posicionados em câmaras pulpares artificiais, os discos de dentina receberam células MDPC-23, as quais foram semeadas sobre a supefície pulpar. Assim, os seguintes grupos foram estabelecidos: G1TC: sem tratamento (controle); G2TC: TSL + CIVMR; G3TC: THSL + CIVMR; G4TC: remoção TSL + CIVRM; G5TC: remoção THSL + CIVMR. Após 24 h, o metabolismo e morfologia celular foram avaliados pelo ensaio de metiltetrazolium (MTT) e por microscopia eletrônica de varredura (MEV), respectivamente. Para BS, os seguintes grupos foram determinados: G1BS: remoção TSL + CIVRM; G2BS: remoção THSL + CIVRM; G3BS: TSL + CIVRM; G4BS: THSL + CIVMR. A resistência de união ao cisalhamento foi avaliada em uma máquina de ensaios mecânicos MTS (0,5 mm/min). Diferença estatisticamente significativa foi observada apenas entre os grupos controle e experimentais (Kruskal-Wallis, p<0,05). A redução da atividade metabólica das células MDPC-23 viáveis nos grupos G2TC, G3TC, G4TC e G5TC foi de 54,85%; 60,79%; 64,12%; e 62,51%, respectivamente. Os valores médios de resistência de união para G1BS, G2BS, G3BS e G4BS foram de 7,5; 7,4; 6,4; e 6,7 MPa, respectivamente, sem diferença significativa entre eles (ANOVA, p>0,05). O CIVMR avaliado neste estudo apresentou moderado efeito citotóxico transdentinário. A manutenção ou remoção da smear layer não afetou a resistência de união deste material resinoso ionomérico sobre a dentina.
Assuntos
Humanos , Colagem Dentária , Dentina/ultraestrutura , Cimentos de Ionômeros de Vidro/toxicidade , Cimentos de Resina/toxicidade , Camada de Esfregaço , Técnicas de Cultura de Células , Linhagem Celular , Forma Celular , Lâmpadas de Polimerização Dentária , Sobrevivência Celular/efeitos dos fármacos , Corantes , Polpa Dentária/citologia , Polpa Dentária/efeitos dos fármacos , Análise do Estresse Dentário/instrumentação , Permeabilidade da Dentina/efeitos dos fármacos , Cimentos de Ionômeros de Vidro/química , Cura Luminosa de Adesivos Dentários/instrumentação , Cura Luminosa de Adesivos Dentários/métodos , Microscopia Eletrônica de Varredura , Cimentos de Resina/química , Resistência ao Cisalhamento , Estresse Mecânico , Temperatura , Fatores de Tempo , Sais de Tetrazólio , Tiazóis , Água/químicaRESUMO
The purpose of the present study was to evaluate in vivo the failure rate of metallic brackets bonded with two orthodontic composites. Nineteen patients with ages ranging from 10.5 to 38.7 years needing corrective orthodontic treatment were selected for study. The enamel surfaces from second premolars to second premolars were treated with Transbond Plus-Self Etching Primer (3M Unitek). Next, 380 orthodontic brackets were bonded on maxillary and mandibular teeth, as follows: 190 with Transbond XT composite (3M Unitek) (control) and 190 with Transbond Plus Color Change (3M Unitek) (experimental) in contralateral quadrants. The bonded brackets were light cured for 40 s, and initial alignment archwires were inserted. Bond failure rates were recorded over a six-month period. At the end of the evaluation, six bond failures occurred, three for each composite. Kaplan-Meyer method and log-rank test (Mantel-Cox) was used for statistical analysis, and no statistically significant difference was found between the materials (p=0.999). Both Transbond XT and Transbond Plus Color Change composites had low debonding rates over the study period.
O objetivo do presente estudo foi avaliar in vivo a taxa de falha de braquetes metálicos colados com dois compósitos ortodônticos. Dezenove pacientes com idades entre 10,5 e 38,7 anos, que necessitavam de tratamento ortodôntico corretivo, foram selecionados para estudo. As superfícies de esmalte de segundos pré-molares a segundos pré-molares foram tratadas com Transbond Plus Self-Etching Primer (3M Unitek). Em seguida, 380 bráquetes foram colados nos dentes superiores e inferiores, como segue: 190 com compósito Transbond XT (3M Unitek) (controle) e 190 com Transbond Plus Color Change (3M Unitek) (experimental), em quadrantes contralaterais. Os bráquetes colados foram fotopolimerizados por 40 s e arcos de alinhamento inicial foram inseridos. As taxas de insucesso na adesão foram registrados durante um período de seis meses. No final da avaliação, seis falhas de adesão ocorreram, três para cada composto. Para a análise estatística foram utilizados os testes de Kaplan-Meyer e log-rank (Mantel-Cox), e não houve diferença estatisticamente significante entre os materiais (p=0,999). Ambos compósitos, Transbond XT e Transbond Plus Color Change, tiveram baixas taxas de descolagem durante o período de estudo.
Assuntos
Adolescente , Adulto , Criança , Feminino , Humanos , Masculino , Adulto Jovem , Resinas Compostas/química , Colagem Dentária , Ligas Dentárias/química , Braquetes Ortodônticos , Cimentos de Resina/química , Dente Pré-Molar/ultraestrutura , Lâmpadas de Polimerização Dentária/classificação , Esmalte Dentário/ultraestrutura , Falha de Equipamento , Seguimentos , Cura Luminosa de Adesivos Dentários/instrumentação , Mandíbula , Maxila , Fios Ortodônticos , Fatores de TempoRESUMO
PURPOSE: In the treatment of midface fractures, the fragments are immobilized using screws and plates for osteosynthesis until reunion has occurred. This method involves drilling holes for the insertion of the screws, which can be associated with additional fracturing of the corresponding bone owing to the complex architecture and thin layers of facial bone. To alleviate this problem, new adhesive techniques for fixing the plates for osteosynthesis have been investigated, mitigating the detrimental effects of screw hole drilling. In the present experimental study, the strength of this adhesive bond and its resistance to hydrolysis were investigated. MATERIALS AND METHODS: To determine the adhesive bonding strength, a tension test was implemented. Osteosynthesis plates with screw holes 1.3 mm in diameter were fixed to cortical bone samples of bovine femur using ultraviolet (UV) light-curing polymethylmethacrylate bone cement. To facilitate bonding, the surface of the bone was conditioned with an amphiphilic bonding agent before cementing. UV light curing was implemented using either a conventional UV unit, such as is used in dentistry, or with a specialized UV unit with a limited emission spectrum but high luminosity. Reference control samples were prepared without application of the bone bonding agent. After this procedure, the samples were stored for 1 to 7 days at 37°C submerged in 0.9% saline solution before being subjected to the tension test. RESULTS: Without the bone bonding agent, the bonding strength was 0.2 MPa. The primary average bonding strength at day 0 was 8.5 MPa when cured with the conventional UV unit and 14 MPa for the samples cured with the specialized UV unit. An almost constant average bond strength of 8 and 16 MPa was noted for all samples stored up to 7 days after curing with the conventional and specialized UV unit, respectively. CONCLUSION: With the development of a new bone bonding agent, a method is now available to promote the bonding between the hydrophilic bone surface and the hydrophobic polymethylmethacrylate bone cement by creating an interlayer that is beneficial for adhesion. In the present in vitro study, the strength of this bond and its resistance to hydrolysis were investigated. This new method could have clinical bearing in cases in which conventional fixation with screws and plates is limited, such as can occur in comminuted fractures. The observed average bonding strengths of 8 to 16 MPa support the implementation of this technique in nonload-bearing regions such as the midface, facilitating immobilization until the bone reunion is complete.
Assuntos
Placas Ósseas , Cimentação/métodos , Cimentos Dentários/uso terapêutico , Fixação Interna de Fraturas/métodos , Polimetil Metacrilato/uso terapêutico , Animais , Bovinos , Lâmpadas de Polimerização Dentária , Fixação Interna de Fraturas/instrumentação , Fraturas Ósseas/terapia , Hidrólise , Cura Luminosa de Adesivos Dentários/instrumentação , Cura Luminosa de Adesivos Dentários/métodos , Teste de Materiais , TíbiaRESUMO
The aim of this study was to evaluate the characteristics of new-generation light-emitting diode (LED) units in comparison with the conventional tungsten-halogen, plasma arc, and first-generation LED units reported in our previous study. The irradiance of light from new-generation LED units, the temperature rise of the bovine enamel surface, and the depth of cure of composites exposed to each unit were investigated. The irradiances in the range 400-515 nm emitted from the new-generation LED units were greater than those from the first-generation LED units. The temperature increase was 15-25 degrees C for new-generation LED units compared with a typical value of 5 degrees C for the first-generation LED units at 10 s of irradiation. The relationship between the depth of cure and the logarithm of total exposure energy suggested that LED units can cure light-cured composite resins more efficiently than tungsten-halogen or plasma arc units.
Assuntos
Resinas Compostas/efeitos da radiação , Lâmpadas de Polimerização Dentária , Esmalte Dentário/efeitos da radiação , Cura Luminosa de Adesivos Dentários/instrumentação , Animais , Bovinos , Lâmpadas de Polimerização Dentária/classificação , Relação Dose-Resposta à Radiação , Cura Luminosa de Adesivos Dentários/métodos , TemperaturaRESUMO
The purpose of this study was to evaluate, in vitro, the color stability of three composite resins of two different shades (A3 and C3) cured with either a quartz tungsten halogen (QTH) or a light emitting diode (LED) source. Forty specimens (20 x 2 mm) were prepared for each composite (Tetric Ceram®, Heliomolar® and Esthet-X®), being 20 for each shade. In each group, 10 specimens were light-cured using the QTH unit and 10 with the LED source. The shade of the materials was evaluated before and after submitting the specimens to artificial accelerated aging (4 h UV-B/4 h condensing vapor), using a reflection spectrophotometer. deltaE means were calculated and analyzed statistically by 2-way ANOVA and Tukey's test at 5 percent significance level. Both A3 and C3 shades of Esthet-X composite resin showed the lowest color change when cured with the QTH light, while Tetric C3 cured with the QTH light showed the highest color change.
O objetivo deste estudo foi verificar a estabilidade de cor de três compósitos polimerizados com dois tipos de unidades polimerizadoras, luz halógena ou diodo emissor de luz (LED). Quarenta amostras (20 mm de diâmetro por 2 mm de espessura) foram construídas com cada compósito (Tetric Ceram®, Heliomolar® and Esthet-X®), vinte na cor A3 e vinte na cor C3. Dentro de cada grupo, 10 amostras foram polimerizadas com luz halógena e as outras com LED. A cor dos materiais foi verificada antes e depois das amostras serem submetidas ao envelhecimento artificial acelerado (4h UV-B/4h de condensação de vapor), usando um espectrofotômetro de reflexão. As médias deltaE de foram calculadas e analisadas estatisticamente (ANOVA a dois critérios e teste de Tukey, 95 por cento). Os compósitos Esthet-X A3 e C3 demonstraram a menor alteração de cor quando polimerizados com luz halógena enquanto a resina. Tetric C3 apresentou a maior alteração de cor quando polimerizada por essa mesma fonte de luz.