Micro-CT assessment of the effect of silver diammine fluoride on inhibition of root dentin demineralization.

This study evaluated the ability of different types of silver diammine fluoride (SDF) to inhibit dentin demineralization using micro-focused X-ray computed-tomography (µCT). Dentin specimens were divided into five groups (n=10); no-treatment (control), 3.8% SDF (RC), 38% SDF, 38% SDF with potassium iodide (SDF/KI), and potassium fluoride (KF). The treated-dentin surfaces were subjected to demineralization for 7-days and assessed using µCT to determine mineral loss (ML) values. Specimens were also analyzed with scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). The ML values of the SDF and KF groups were significantly lower than those of the RC and SDF/KI groups. EDS detected fluoride ions in the SDF and KF groups but not in the RC and SDF/KI groups. It was concluded that 38% SDF demonstrated a high ability to inhibit dentin demineralization while additional application of KI may diminish the inhibitory effect of SDF. The amount of dentin demineralization with SDF treatments was material dependent.

Micro-computed tomography assessment of root dentin around fluoride-releasing restorations after demineralization/remineralization.

Using micro-computed tomography (micro-CT), this study assessed the inhibitory effect of three different types of restorations on root-caries formation under a cariogenic challenge. Bovine-root dentin blocks with a cylindrical cavity were divided into three restoration groups: a fluoride-free self-etch adhesive and a resin composite (SE-ES); a self-etch adhesive and a resin composite with multi-ion release (FL-BF); and a glass ionomer cement (Fuji-VII). After the restorative procedures, the specimens were stored in artificial saliva for 1 d, then subjected to a demineralization solution for 4 d and a remineralization solution for 28 d. Mineral density and mean mineral loss of dentin around the restorations were measured using micro-CT. The mean mineral loss values of dentin around the restorations were highest among SE-ES restorations and lowest among Fuji-VII restorations. Fuji-VII showed the highest mineral density and the lowest mineral loss after 28 d of remineralization. The observations made by scanning electron microscopy demonstrated that Fuji-VII created the smallest outer lesion followed by FL-BF and SE-ES. Fuji-VII has a larger inhibitory effect on root caries around the restorations and enhances remineralization more effectively than either FL-BF or SE-ES. Multi-ion and fluoride release from the restorative materials may be beneficial for inhibition of root-dentin caries around the restorations.

Micro-CT assessment of comparative radiopacity of adhesive/composite materials in a cylindrical cavity.

This study was performed to evaluate the comparative radiopacity of adhesive/resin composite materials in cylindrical cavities using micro-computed X-ray tomography (µCT). The two-step self-etch adhesive systems, Clearfil SE Bond (SE) and FL-Bond II (FL), and flowable resin composites, Beautifil Flow F10 (BF) and Clearfil Majesty ES Flow High (MJ), were used. The radiopacity of bovine tooth structures and restorative materials was measured by µCT. In addition, cylindrical cavities prepared in bovine teeth were restored with the following adhesive/composite combinations: SE-BF, SE-MJ, FL-BF, and FL-MJ. The mean gray values of the composite restorations were calculated. The threshold values of the µCT images were evaluated using the Otsu's thresholding method. The current results show that the comparative radiopacity of the materials and tooth structure varied, which affected distinguishing the µCT images of the composite restorations in the cylindrical cavity. The proper combination of restorative materials should be considered when conducting in vitro µCT assessments of composite restorations.

Assessment of natural enamel lesions with optical coherence tomography in comparison with microfocus x-ray computed tomography.

A technology to characterize early enamel lesions is needed in dentistry. Optical coherence tomography (OCT) is a noninvasive method that provides high-resolution cross-sectional images. The aim of this study is to compare OCT with microfocus x-ray computed tomography ([Formula: see text]) for assessment of natural enamel lesions in vitro. Ten human teeth with visible white spot-like changes on the enamel smooth surface and no cavitation (ICDAS code 2) were subjected to imaging by µCT (SMX-100CT, Shimadzu) and 1300-nm swept-source OCT (Dental SS-OCT, Panasonic Health Care). In [Formula: see text], the lesions appeared as radiolucent dark areas, while in SS-OCT, they appeared as areas of increased signal intensity beneath the surface. An SS-OCT attenuation coefficient based on Beer-Lambert law could discriminate lesions from sound enamel. Lesion depth ranged from 175 to [Formula: see text] in SS-OCT. A correlation between [Formula: see text] and SS-OCT was found regarding lesion depth ([Formula: see text], [Formula: see text]) and also surface layer thickness ([Formula: see text], [Formula: see text]). The images obtained clinically in real time using the dental SS-OCT system are suitable for the assessment of natural subsurface lesions and their surface layer, providing comparable images to a laboratory high-resolution [Formula: see text] without the use of x-ray.

Effect of different desensitizers on inhibition of bovine dentin demineralization: micro-computed tomography assessment.

This study evaluated the effect of two desensitizers on inhibition of dentin demineralization, after immersion in artificial saliva using micro-computed tomography (µCT). Dentin blocks cut from bovine incisors were treated with deionized water (DW, a negative control) or one of three desensitizers: a fluoride varnish (Duraphat, a positive control), a calcium phosphate desensitizer (Teethmate Desensitizer), and a fluoro-alumino-calcium silicate-based desensitizer (Nanoseal). After each treatment, the specimens in Duraphat, Nanoseal, and Teethmate Desensitizer groups were pre-immersed in artificial saliva (pH 6.5) for either 1 d or 1 wk. The mineral loss of the specimens after demineralization (pH 5.0, 3 h) was evaluated by µCT. The treated surface was investigated with scanning electron microscopy. Mineral loss in all treatment groups was significantly lower than that in DW. Duraphat was the most effective treatment against demineralization, followed by Nanoseal. Nanoseal showed significantly better reduction in mineral loss following immersion for 1 wk in artificial saliva than for 1 d. However, Teethmate Desensitizer and Duraphat did not exhibit enhanced inhibition of demineralization over a longer period of immersion in artificial saliva. Scanning electron microscopy images showed deposition of particles on the dentin in both Teethmate Desensitizer. The application of Teethmate Desensitizer and Nanoseal to the exposed dentin surface resulted in inhibition of demineralization, with Nanoseal resulting in improved inhibition after prolonged immersion in artificial saliva.