Assessment of the potential hazard represented by natural raw materials containing mineral fibres-The case of the feldspar from Orani, Sardinia (Italy).

This work describes the nature of the potentially hazardous fibrous amphibole found in the Orani's feldspar mine (Sardinia, Italy). To identify its nature, a protocol of analysis including morphometric, chemical and crystallographic characterizations was applied. Thanks to this approach, it was possible to classify the observed fibres as tremolite after comparing chemical data, SEM/TEM observations, FTIR/ Raman spectra and X-ray diffraction data with those reported for a standard sample. The unit cell parameters of the investigated tremolite phase are a = 9.82(1) Å, b = 18.08(3) Å, c = 5.27(1) Å, and the angle ß corresponds to 104.4(1)°. The mean concentration of asbestos tremolite in the Orani's feldspar is 0.28 wt%. Most of the fibres (0.26 wt%) are respirable 'regulated' fibres, representing a potential hazard. Because the total amount of tremolite in the sample is 0.6 wt%, a large fraction of it has a crystal habit other than fibrous-asbestiform or acicular. The obtained results allowed us to suggest possible solutions for a safe exploitation and mineral processing of the Orani's mine. The procedure proposed herein may be a general tool suitable to identify the mineralogical nature of fibrous minerals in raw materials and assess if they may represent a potential health/environmental hazard.

Assessment of asbestos body formation by high resolution FEG-SEM after exposure of Sprague-Dawley rats to chrysotile, crocidolite, or erionite.

This work presents a comparative FEG-SEM study of the morphological and chemical characteristics of both asbestos bodies and fibres found in the tissues of Sprague-Dawley rats subjected to intraperitoneal or intrapleural injection of UICC chrysotile, UICC crocidolite and erionite from Jersey, Nevada (USA), with monitoring up to 3 years after exposure. Due to unequal dosing based on number of fibres per mass for chrysotile with respect to crocidolite and erionite, excessive fibre burden and fibre aggregation during injection that especially for chrysotile would likely not represent what humans would be exposed to, caution must be taken in extrapolating our results based on instillation in experimental animals to human inhalation. Notwithstanding, the results of this study may help to better understand the mechanism of formation of asbestos bodies. For chrysotile and crocidolite, asbestos bodies are systematically formed on long asbestos fibres. The number of coated fibres is only 3.3% in chrysotile inoculated tissues. In UICC crocidolite, Mg, Si, and Fe are associated with the fibres whereas Fe, P and Ca are associated with the coating. Even for crocidolite, most of the observed fibres are uncoated as coated fibres are about 5.7%. Asbestos bodies do not form on erionite fibres. The crystal habit, crystallinity and chemistry of all fibre species do not change with contact time, with the exception of chrysotile which shows signs of leaching of Mg. A model for the formation of asbestos bodies from mineral fibres is postulated. Because the three fibre species show limited signs of dissolution in the tissue, they cannot act as source of elements (primarily Fe, P and Ca) promoting nucleation and growth of asbestos bodies. Hence, the limited number of coated fibres should be due to the lack of nutrients or organic nature.