RESUMO
BACKGROUND: Theoretically, collagen-stabilized deproteinized bovine bone mineral (DBBM-C) has better operability compared with DBBM. DBBM-C avoids dispersing during the transalveolar sinus floor elevation (TSFE) because of its block shape. PURPOSE: To evaluate radiological changes of using DBBM-C in TSFE. MATERIALS AND METHODS: Patients who received TSFE using DBBM (Bio-Oss®) or DBBM-C (Bio-Oss® collagen) with simultaneous implantation were recruited. Graft bone height apically (aGH), endo-sinus bone gain (ESBG), and crest bone level (CBL) were assessed through panoramic radiograph and cone beam computed tomography (CBCT). RESULTS: A total of 138 patients (138 implants) were retrospectively enrolled. After 2 years of implantation, the incidence of postoperative complications was 4.2% (95% CI: 0.9%-11.7%) and 4.5% (95% CI: 0.9%-12.7%) for DBBM and DBBM-C groups, respectively. Measured in panoramic radiograph, ΔaGH of DBBM-C (1.8 mm, SD: 1.4, 95% CI: 1.2-2.4, P = 0.044) group was significantly higher than that of DBBM (1.2 mm, SD: 1.4, 95% CI: 0.7-1.7) after 24 months. No significant differences for ΔCBL were noted during the entire observation period. Measured through CBCT, ESBG was 5.0 (SD: 1.8, 95% CI: 4.1-5.8) mm in DBBM group and 4.6 (SD: 1.6, 95% CI: 3.9-5.3) mm in DBBM-C group 24 months after implantation. The aGH value of DBBM-C group was significantly higher compared with DBBM in CBCT (OR = 1.4, 95% CI: 1.1-1.9, P = 0.020). CONCLUSIONS: DBBM-C could achieve similar bone generation as DBBM in TSFE. Both materials could maintain aGH, ESBG, and CBL relatively stable 2 years after implantation.