RESUMO
Saliva substitutes with enhanced dentin remineralization properties were expected to help manage caries progression in patients with xerostomia. This in vitro study examined the rheological properties and remineralization action of experimental saliva substitutes containing propolis extract and aloe vera extract on demineralized dentin. Four experimental saliva substitutes were formulated with varying concentrations of propolis extract (P) and aloe vera extract (A) were prepared. A commercial saliva substitute (Biotene Oral Rinse) was used as a commercial comparison. The rheological properties and viscosity of these materials were measured using a strain-controlled rheometer (n = 3). The remineralizing actions of saliva substitutes on demineralized dentin after 2 weeks were determined using ATR-FTIR and SEM-EDX (n = 8). The results were expressed as a percentage increase in the mineral-to-matrix ratio. Biotene demonstrated a significantly higher viscosity (13.5 mPa·s) than experimental saliva substitutes (p<0.05). The addition of extracts increased the viscosity of the saliva substitutes from 4.7 mPa·s to 5.2 mPa·s. All formulations showed minimal shear thinning behavior, which was the viscoelastic properties of natural saliva. The formulation containing 5 wt% of propolis exhibited the highest increase in the median mineral-to-matrix ratio (25.48%). The SEM-EDX analysis revealed substantial mineral precipitation in demineralized dentin, especially in formulations with 5 wt% or 2.5 wt% of propolis. The effect of the aloe vera extract was minimal. The addition of propolis and aloe vera extracts increased the viscosity of saliva substitutes. the addition of propolis for 2.5 or 5 wt% to saliva substitutes increased mineral apatite precipitation and tubule occlusion. To conclude, the saliva substitute containing propolis extract demonstrated superior remineralizing actions compared with those containing only aloe vera extract.
Assuntos
Aloe , Dentina , Extratos Vegetais , Própole , Reologia , Saliva Artificial , Própole/química , Própole/farmacologia , Aloe/química , Extratos Vegetais/química , Extratos Vegetais/farmacologia , Saliva Artificial/química , Dentina/química , Dentina/efeitos dos fármacos , Humanos , Viscosidade , Remineralização Dentária/métodos , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
To incorporate different concentrations of Al2O9Zr3 (1%, 5%, and 10%) nanoparticles (NP) into the ER adhesive and subsequently assess the impact of this addition on the degree of conversion, µTBS, and antimicrobial efficacy. The current research involved a wide-ranging examination that merged various investigative techniques, including the application of scanning electron microscopy (SEM) for surface characterization of NP coupled with energy-dispersive x-ray spectroscopy (EDX), Fourier-transform infrared (FTIR) spectroscopy, µTBS testing, and microbial analysis. Teeth were divided into four groups based on the application of modified and unmodified three-step ER adhesive primer. Group 1 (0% Al2O9Zr3 NPs) Control, Group 2 (1% Al2O9Zr3 NPs), Group 3 (5% Al2O9Zr3 NPs), and Group 4 (10% Al2O9Zr3 NPs). EDX analysis of Al2O9Zr3 NPs was performed showing elemental distribution in synthesized NPs. Zirconium (Zr), Aluminum (Al), and Oxides (O2). After primer application, an assessment of the survival rate of Streptococcus mutans was completed. The FTIR spectra were analyzed to observe the characteristic peaks indicating the conversion of double bonds, both before and after the curing process, for the adhesive Etch and rinse containing 1,5,10 wt% Al2O9Zr3 NPs. µTBS and failure mode assessment were performed using a Universal Testing Machine (UTM) and stereomicroscope respectively. The µTBS and S.mutans survival rates comparison among different groups was performed using one-way ANOVA and Tukey post hoc (p = .05). Group 4 (10 wt% Al2O9Zr3 NPs + ER adhesive) specimens exhibited the minimum survival of S.mutans (0.11 ± 0.02 CFU/mL). Nonetheless, Group 1 (0 wt% Al2O9Zr3 NPs + ER adhesive) displayed the maximum surviving S.mutans (0.52 ± 0.08 CFU/mL). Moreover, Group 2 (1 wt% Al2O9Zr3 NPs + ER adhesive) (21.22 ± 0.73 MPa) samples displayed highest µTBS. However, the bond strength was weakest in Group 1 (0 wt% Al2O9Zr3 NPs + ER adhesive) (14.13 ± 0.32 MPa) study samples. The etch-and-rinse adhesive exhibited enhanced antibacterial activity and micro-tensile bond strength (µTBS) when 1% Al2O9Zr3 NPs was incorporated, as opposed to the control group. Nevertheless, the incorporation of Al2O9Zr3 NPs led to a decrease in DC. RESEARCH HIGHLIGHTS: 10 wt% Al2O9Zr3 NPs + ER adhesive specimens exhibited the minimum survival of S.mutans. 1 wt% Al2O9Zr3 NPs + ER adhesive samples displayed the most strong composite/CAD bond. The highest DC was observed in Group 1: 0 wt% Al2O9Zr3 NPs + ER adhesive.
Assuntos
Alumínio , Antibacterianos , Dentina , Microscopia Eletrônica de Varredura , Streptococcus mutans , Resistência à Tração , Zircônio , Zircônio/química , Streptococcus mutans/efeitos dos fármacos , Alumínio/química , Alumínio/análise , Alumínio/farmacologia , Antibacterianos/farmacologia , Humanos , Dentina/química , Dentina/efeitos dos fármacos , Dentina/microbiologia , Cárie Dentária/microbiologia , Nanopartículas/química , Espectroscopia de Infravermelho com Transformada de Fourier/métodos , Cimentos Dentários/química , Cimentos Dentários/farmacologia , Espectrometria por Raios X/métodos , Colagem Dentária , Propriedades de Superfície , Adesivos/químicaRESUMO
Accomplishment of an ideal root canal treatment is attributed to various essential factors such as proper instrumentation, chemomechanical preparation, obturation and post endodontic restoration. The main aim of this study is to test the null hypothesis that is the moisture condition of root dentin would not affect the bond strength and sealer penetration. This is an in vitro study conducted in Department of Conservative Dentistry and Endodontics, M A Rangoonwala Dental College, Pune, India over a period of two years (from 2021 to 2023). One hundred and twenty single-rooted Premolars with fully formed apices and similar root morphology were obtained and stored in 0.1% thymol solution. The specimens were randomly assigned to 3 broad experimental groups (n=40) according to the drying protocol such as Group A- Paper points (P), Group B- diode laser (L) and Group C- isopropyl alcohol (A). For each drying protocol, the specimens were further assigned to 2 subgroups (n=20) with respect to the sealers used: AH Plus (AH) and Apexit Plus sealers (APx). The effect of drying protocol using paper points, isopropyl alcohol and diode-lasers on the bond strength and tag penetration of two different sealers to the root dentin was evaluated. Maximum overall push-out Bond strength was seen in group AH+L and least in group APx+ L. Inter-site push-out bond Strength was highest in the coronal third followed by the middle and least in the apical third of all the groups. Maximum over all depth of penetration was seen in group AH+L and minimum in group APx+L. AH plus sealer showed better bond strength, sealer penetration and adaptation to the dentinal walls compared to Apexit plus sealer, irrespective of the drying protocol followed. All the drying protocols used did not show statistically significant results in the apical thirds of root canals of all the groups.
Assuntos
Hidróxido de Cálcio , Materiais Restauradores do Canal Radicular , Humanos , Materiais Restauradores do Canal Radicular/análise , Materiais Restauradores do Canal Radicular/química , Resinas Epóxi/análise , Resinas Epóxi/química , 2-Propanol/análise , Índia , Dentina/químicaRESUMO
To evaluate the efficiency and effectiveness of three minimally invasive (MI) techniques in removing deep dentin carious lesions. Forty extracted carious molars were treated by conventional rotary excavation (control), chemomechanical caries removal agent (Brix 3000), ultrasonic abrasion (WOODPECKER, GUILIN, China); and Er, Cr: YSGG laser ablation (BIOLASE San Clemente, CA, USA). The assessments include; the excavation time, DIAGNOdent pen, Raman spectroscopy, Vickers microhardness, and scanning electron microscope combined with energy dispersive X-ray spectroscopy (SEM-EDX). The rotary method recorded the shortest excavation time (p < 0.001), Brix 3000 gel was the slowest. DIAGNOdent pen values ranged between 14 and 18 in the remaining dentin and laser-ablated surfaces recorded the lowest reading (p < 0.001). The Ca:P ratios of the remaining dentin were close to sound dentin after all excavation methods; however, it was higher in the ultrasonic technique (p < 0.05). The bur-excavated dentin showed higher phosphate and lower matrix contents with higher tissue hardness that was comparable to sound dentin indicating the non-selectiveness of this technique in removing the potentially repairable dentin tissue. In contrast, the MI techniques exhibited lower phosphate and higher organic contents associated with lower microhardness in the deeper dentin layers. This was associated with smooth residual dentin without smearing and patent dentinal tubules. This study supports the efficiency of using MI methods in caries removal as conservative alternatives to rotary excavation, providing a promising strategy for the clinical dental practice.
Assuntos
Cárie Dentária , Lasers de Estado Sólido , Humanos , Dentina/química , Suscetibilidade à Cárie Dentária , Dureza , Fosfatos/análise , Cárie Dentária/cirurgia , Cárie Dentária/patologiaRESUMO
OBJECTIVES: Evaluate the ability of current ion-releasing materials to remineralise bacteria-driven artificial caries lesions. MATERIALS AND METHODS: Standardised class I cavities were obtained in 60 extracted human molars. Specimens underwent a microbiological cariogenic protocol (28 days) to generate artificial caries lesions and then were randomly divided into four restorative groups: adhesive + composite (negative control); glass ionomer cement (GIC); calcium silicate cement (MTA); and resin-modified calcium silicate cement (RMTA). Microhardness analysis (ΔKHN) was performed on 40 specimens (10/group, t = 30 days, 45 days, 60 days in artificial saliva, AS). Micro-CT scans were acquired (3/group, t = 0 days, 30 days, and 90 days in AS). Confocal microscopy was employed for interfacial ultra-morphology analysis (2/group, t = 0 days and 60 days in AS). Additional specimens were prepared and processed for scanning electron microscopy (SEM) and FTIR (n = 3/group + control) to analyse the ability of the tested materials to induce apatite formation on totally demineralised dentine discs (60 days in AS). Statistical analyses were performed with a significance level of 5%. RESULTS: Adhesive + composite specimens showed the lowest ΔKHN values and the presence of gaps at the interface when assessed through micro-CT even after storage in AS. Conversely, all the tested ion-releasing materials presented an increase in ΔKHN after storage (p < 0.05), while MTA best reduced the demineralised artificial carious lesions gap at the interface. MTA and RMTA also showed apatite deposition on totally demineralised dentine surfaces (SEM and FTIR). CONCLUSIONS: All tested ion-releasing materials expressed mineral precipitation in demineralised dentine. Additionally, calcium silicate-based materials induced apatite precipitation and hardness recovery of artificial carious dentine lesions over time. CLINICAL RELEVANCE: Current ion-releasing materials can induce remineralisation of carious dentine. MTA shows enhanced ability of nucleation/precipitation of hydroxyapatite compared to RMTA and GIC, which may be more appropriate to recover severe mineral-depleted dentine.
Assuntos
Cárie Dentária , Dentina , Humanos , Apatitas , Compostos de Cálcio , Cárie Dentária/patologia , Cárie Dentária/terapia , Dentina/química , Cimentos de Ionômeros de Vidro , Hidroxiapatitas , Teste de Materiais , Minerais/análise , Cimentos de Resina , Saliva Artificial , SilicatosRESUMO
To evaluate i) the inhibitory and bactericidal activity of cashew nut shell liquid (CNSL) and its isolated compounds (anacardic acid and cardol) against oral bacteria; ii) the biofilm formation inhibition, resin-dentin bond strength and physicochemical properties of a dental adhesive incorporated with these substances. The antibacterial effect of CNSL, anacardic acid, and cardol were assessed by determining the minimum inhibitory (MIC) and minimum bactericidal (MBC) concentrations. Effect in inhibiting biofilm formation of the adhesive incorporated with the substances (15 µg/ml) against a mixed-species biofilm of Streptococcus mutans and Candida Albicans and was determined by direct contact test. Additional Analysis included microtensile bond strength (µTBS) test, elastic modulus (EM), flexural strength (FS), degree of conversion (DC), water sorption (WS) and solubility (SL). The data were submitted to statistical analysis by one-way ANOVA and Tukey's test (p < 0.05). CNSL, anacardic acid and cardol showed antibacterial activity for all strains tested, with MIC and MBC values ranging from 3.12 to 25 µg/ml. There was no growth of colonies forming units in the adhesives incorporated with the substances. EM increased in the adhesive incorporated with anacardic acid, decreased after incorporation of cardol and it was not affected by incorporation of CNSL. The substances tested showed no effect in FS, DC, WS, SL and µTBS. In conclusion, the CNSL, anacardic acid and cardol showed antibacterial effects against oral bacteria and, the incorporation of substances did not reduce the performance of the adhesive.
Assuntos
Anacardium , Colagem Dentária , Anacardium/química , Antibacterianos/farmacologia , Cimentos Dentários/química , Dentina/química , Adesivos Dentinários/química , Teste de Materiais , Nozes/química , Cimentos de Resina/química , Cimentos de Resina/farmacologia , Streptococcus mutans , Resistência à TraçãoRESUMO
Dentine hypersensitivity (DH) is one of the most common dental conditions affecting most adults during their lifetime. Tubule occlusion is a widely accepted method for treating DH. Current in-vitro techniques such as focused ion beam, scanning electron microscopy (SEM), or hydraulic conductance that are used to determine tubule occlusion do not provide the depth of occlusion, are time-consuming, expensive and the volume of dentine tested is limited. The presented study aimed to assess the ability of serial block-face SEM (SBF-SEM) to section dentine, to quantify the number of occluded tubules including the depth of penetration by NovaMin and stannous fluoride (SnF2 ) and to compare mineral density between the control and treated dentine. Results demonstrated that NovaMin provided a better occlusion with 100% of the tubules blocked at the surface compared to 83% for SnF2 . The grayscale value (230.42) was significantly higher (p ≤ 0.05) after treatment with NovaMin compared to SnF2 (222.06) and the control (196.37), indicating increased mineral density and dentine mineralization. SBF-SEM has the potential to be used for large volume analysis of bone-like materials at high resolution with minimal sample preparation over a short period. It can be significantly useful in the development and research of new biomaterials.
Assuntos
Materiais Biocompatíveis/química , Dentina/química , Vidro/química , Fluoretos de Estanho/química , Cremes Dentais , Animais , Bovinos , Sensibilidade da Dentina , Fluoretos , Técnicas In Vitro , Teste de Materiais , Microscopia Eletrônica de Varredura , FosfatosRESUMO
We assess diet and economies of middle Holocene (â¼7,500 to 4,000 calibrated [cal] B.P.) humans at coexisting mound sites (Huaca Prieta and Paredones) in north coastal Peru and document regular consumption of maize by â¼6,500 to 6,000 cal B.P. and its earliest use as a staple food in this area of the Andes between 5,000 and 4,500 cal B.P. Stable isotope data from enamel carbonates and dentin collagen (childhood diet) and dental microwear texture analysis (adult diet) demonstrate dietary and economic specialization. Previous studies revealed maize and mixed-food refuse at both sites, but this study documents actual food consumption, showing that these communities situated a few hundred meters apart had significantly distinct diets in childhood and adulthood. Huaca Prieta focused on marine resources, although there are some contributions from terrestrial meat. Paredones individuals primarily consumed maize during childhood (up to 70% of the juvenile diet), as shown by δ13C values, apatite-collagen spacing, and discriminant analysis of δ13Ccoll, δ13Ccarb, and δ15N values. Maize was likely used as a weaning food (e.g., gruel and/or chicha-a maize beverage), hinting at the significant role of breastfeeding mothers, weanling infants, and children in the development of maize as a staple crop. Additionally, dental microwear data show Paredones adult diets are high in abrasives, potentially from maize processing. The distinct foodways at these neighboring sites result from and also reflect their social and political distinctions. These differences in food production, distribution, and consumption generated opportunities for exchange, an interaction that bound them together in mutual benefit.
Assuntos
Produtos Agrícolas/história , Esmalte Dentário/química , Comportamento Alimentar , Alimentos Marinhos , Zea mays , Animais , Isótopos de Carbono/análise , Criança , Fenômenos Fisiológicos da Nutrição Infantil , Colágeno/química , Dentina/química , Fósseis , História Antiga , Humanos , Dente Molar/química , Isótopos de Nitrogênio/análise , Isótopos de Oxigênio/análise , PeruRESUMO
Dentine erosion is an increasingly recognised problem, especially in aging population, and various methods have been utilised for its assessment. This narrative review was planned to summarise the methods for the assessment of the early stages of dentine erosion. Relevant original articles published in the English language from 2013 to 2017 were reviewed. Laboratory techniques and methods with in vivo potential were separately studied. It is evident that the assessment of early dentine erosion is complex and requires a combination of methods. For clinical evaluation, chemical analysis and optical methods show great potential but are in need of more validation.
Assuntos
Dentina/diagnóstico por imagem , Erosão Dentária/diagnóstico , Cálcio/análise , Dentina/química , Dentina/patologia , Testes de Dureza , Humanos , Microrradiografia , Microscopia de Força Atômica , Fosfatos/análise , Fluorescência Quantitativa Induzida por Luz , Tomografia de Coerência Óptica , Erosão Dentária/diagnóstico por imagem , Erosão Dentária/patologiaRESUMO
Using micro-computed tomography (micro-CT), this study assessed the inhibitory effect of three different types of restorations on root-caries formation under a cariogenic challenge. Bovine-root dentin blocks with a cylindrical cavity were divided into three restoration groups: a fluoride-free self-etch adhesive and a resin composite (SE-ES); a self-etch adhesive and a resin composite with multi-ion release (FL-BF); and a glass ionomer cement (Fuji-VII). After the restorative procedures, the specimens were stored in artificial saliva for 1 d, then subjected to a demineralization solution for 4 d and a remineralization solution for 28 d. Mineral density and mean mineral loss of dentin around the restorations were measured using micro-CT. The mean mineral loss values of dentin around the restorations were highest among SE-ES restorations and lowest among Fuji-VII restorations. Fuji-VII showed the highest mineral density and the lowest mineral loss after 28 d of remineralization. The observations made by scanning electron microscopy demonstrated that Fuji-VII created the smallest outer lesion followed by FL-BF and SE-ES. Fuji-VII has a larger inhibitory effect on root caries around the restorations and enhances remineralization more effectively than either FL-BF or SE-ES. Multi-ion and fluoride release from the restorative materials may be beneficial for inhibition of root-dentin caries around the restorations.
Assuntos
Restauração Dentária Permanente/métodos , Fluoretos/farmacologia , Desmineralização do Dente/patologia , Desmineralização do Dente/prevenção & controle , Remineralização Dentária , Raiz Dentária/efeitos dos fármacos , Raiz Dentária/diagnóstico por imagem , Microtomografia por Raio-X/métodos , Animais , Densidade Óssea/efeitos dos fármacos , Cariostáticos/efeitos adversos , Bovinos , Resinas Compostas/química , Cárie Dentária/patologia , Materiais Dentários/química , Dentina/química , Dentina/diagnóstico por imagem , Dentina/efeitos dos fármacos , Dentina/patologia , Fluoretos/química , Cimentos de Ionômeros de Vidro/farmacologia , Minerais , Cimentos de Resina/química , Cárie Radicular , Materiais de Ensino , Fatores de Tempo , Desmineralização do Dente/diagnóstico por imagem , Raiz Dentária/químicaRESUMO
OBJECTIVES: Stable carbon and nitrogen isotope ratios (δ13 C and δ15 N) were used to reconstruct the history of subsistence strategies in the middle Euphrates valley, NE Syria, in six temporal subsets dating from the Early Bronze Age (c. 2300 BCE) to the Modern period (19th/20th century CE). The study aims to demonstrate that changes in political and social organization over time, for which the archaeological record suggests different goals of land use and modes of production, register through dietary patterns that are reflected in isotopic data. MATERIALS AND METHODS: 173 dentin samples were taken from human individuals buried at three sites (Tell Ashara, Tell Masaikh and Gebel Mashtale) together with 15 animal bone samples. Distribution of the δ13 C and δ15 N values in collagen was interpreted in diachronic perspective, and with regard to lifetime shifts between childhood and adolescence. RESULTS: Diachronically, isotope signatures indicate a clear decrease in δ15 N values accompanied by a small shift in δ13 C values between the Old Babylonian (c. 1800-1600 BCE) and the Neo-Assyrian (c. 850-600 BCE) subsets. A major shift in δ13 C values occurred between the Early Islamic (c. 600-1200 CE) and Modern (c. 1800-1950) periods. Ontogenetic changes only occur in a few individuals, but these suggest change of residence between childhood and adolescence. DISCUSSION: The depletion in 15 N from the Neo-Assyrian period onwards is best explained in terms of a shift from intensive to extensive farming, triggered by the fall of regional city-states after the Old Babylonian period and the formation of large supra-regional polities in the Neo-Assyrian period and later. The enrichment in 13 C during the Modern period was most likely the effect of more widely utilizing the dry steppes, abundant in C4 plants, as pasture.
Assuntos
Agricultura/história , Isótopos de Carbono/análise , Isótopos de Nitrogênio/análise , Adolescente , Animais , Arqueologia , Osso e Ossos/química , Criança , Dentina/química , Dieta/história , História Antiga , Humanos , Mesopotâmia/etnologia , Síria/etnologiaRESUMO
BACKGROUND: Recent public health lead crises in urban areas emphasize the need to better understand exposure to environmental toxicants, particularly in higher risk groups. Although African-American children have the highest prevalence of elevated blood lead levels in the United States, little is known about when this trajectory of disproportionate burden of lead exposure first emerges. OBJECTIVES: Using tooth-matrix biomarkers that directly measure fetal and early childhood metal levels, the primary goal of this study was to determine if there were racial disparities in lead levels during fetal development and early childhood. Manganese, an essential nutrient that modifies the neurotoxic effects of lead, was also measured. METHODS: Pregnant women served by the Henry Ford Health System and living in a predefined geographic area in and around Detroit, Michigan, were recruited during the second trimester or later into the Wayne County Health, Environment, Allergy and Asthma Longitudinal Study (WHEALS), a population-based birth cohort. Offspring born between September 2003 and December 2007 were studied in childhood. Child race was parent-reported. Lead and manganese during the second and third trimesters, early postnatal life (birth through age 1year) and early childhood (age 1 through time of tooth shedding, which ranges from 6 to 12years) were measured via high-resolution microspatial mapping of dentin growth rings, a validated biomarker for prenatal and childhood metal exposure. RESULTS: African-American children (N=71) had 2.2 times higher lead levels in the second and third trimesters (both p<0.001) and 1.9 times higher lead levels postnatally in the first year of life (p=0.003) compared to white children (N=51). Lead levels in African-American children were also higher during childhood, but this effect was only marginally significant (p=0.066) and was attenuated after covariate adjustment. Additionally, we observed that African-American children had lower toothmanganese levels during the third trimester (p=0.063) and postnatally (p=0.043), however these differences were attenuated after covariate adjustment. CONCLUSION: The disproportionate burden of lead exposure is vertically transmitted (i.e., mother-to-child) to African-American children before they are born and persists into early childhood. Our results suggest that testing women for lead during pregnancy (or in pre-conception planning), may be needed to identify the risk to their future offspring, particularly for African-American women.
Assuntos
Negro ou Afro-Americano , Exposição Ambiental , Poluentes Ambientais/análise , Desenvolvimento Fetal , Chumbo/análise , Adulto , Criança , Pré-Escolar , Estudos de Coortes , Dentina/química , Feminino , Humanos , Lactente , Recém-Nascido , Estudos Longitudinais , Masculino , Exposição Materna , Michigan , Gravidez , Prevalência , Fatores de Risco , População BrancaRESUMO
OBJECTIVES: To evaluate the sealing ability and the microtensile bond strength (MTBS) of different adhesive systems bonded to dentin in class I cavities. METHODS: Round tapered dentin cavities (3-mm diameter, 1.5-mm height) prepared in extracted human molars were restored using composite resin (Clearfil Majesty Posterior) with two-step etch-and-rinse adhesive system (Adper Single Bond 2: ASB2), two-step self-etch adhesive (Clearfil SE Bond: CSEB), all-in-one adhesives (G-Bond Plus: GBP; Tri-S Bond Plus: TSBP), or no adhesive (Control), or bonded using low-shrinkage composite with its proper adhesive (Filtek Silorane, Silorane Adhesive System: FSS). After 24-h water storage or 10,000 cycles of thermal stress, the specimens were immersed into a contrast agent. Two and three-dimensional images were obtained using optical coherence tomography (OCT). The mean percentage of high brightness (HB%) at the interfacial zone in cross-sectional images was calculated as an indicator of contrast agent or gap at the interface. The specimens were then sectioned into beams and the MTBS measured. RESULTS: The HB% (ASB2=TSBP=CSEB
Assuntos
Cárie Dentária/terapia , Prótese Dentária , Dentina/química , Dente Molar/química , Resinas de Silorano/química , Colagem Dentária , Preparo da Cavidade Dentária , Análise do Estresse Dentário , Humanos , Resistência à Tração , Tomografia de Coerência ÓpticaRESUMO
INTRODUCTION: EndoSequence BC Sealer (Brasseler, Savannah, GA) is a premixed tricalcium silicate-based root canal sealer that requires moisture from the root dentin to hydrate. The aim of this study was to investigate the setting of EndoSequence BC Sealer and other sealers in contact with human dentin in a simulated clinical environment. METHODS: EndoSequence BC Sealer, MTA Fillapex (Angelus, Londrina, Brazil), Septodont Sealer (Septodont, Saint Maur-des-Fosses, France), and Apexit Plus (Ivoclar, Schaan, Lichtenstein) were assessed. Caries-free lower premolars extracted for orthodontic purposes in patients aged 13-16 years were standardized to a 10-mm root length and were filled with test sealers and set up in a dentin pressure model for 14 days. In addition, set sealers immersed in physiologic solution for 14 days were also assessed. The set materials in solution and materials retrieved from the dentin pressure setup were characterized by scanning electron microscopy and X-ray diffraction analysis. The setting time and radiopacity were assessed using ISO 6876:2002 specifications. Furthermore, mineral ion leaching was evaluated by inductively coupled plasma mass spectrometry. RESULTS: All the sealers tested exhibited formation of a calcium phosphate phase when in contact with physiologic solution. Septodont Sealer and Apexit Plus did not exhibit the formation of a calcium phosphate phase in the dentin pressure setup. The fluid in the system was enough to allow the setting of EndoSequence BC Sealer, which did not set in a dry environment. All materials leached calcium with the Septodont Sealer, exhibiting double the calcium ion leaching compared with EndoSequence BC Sealer. CONCLUSIONS: Using the dentinal fluid pressure system resulted in an adequate flow of dentinal fluid that allowed EndoSequence BC Sealer to set inside the root canal. Although the sealers tested were tricalcium silicate based, the hydration reaction and bioactivity in the presence of dentinal fluid were different to hydration in vitro. Thus, clinically, material bioactivity cannot be assumed.
Assuntos
Compostos de Cálcio/química , Dentina/química , Materiais Restauradores do Canal Radicular/química , Silicatos/química , Cimento de Óxido de Zinco e Eugenol/química , Adolescente , Fosfatos de Cálcio/química , Cavidade Pulpar , Dentina/diagnóstico por imagem , Humanos , Teste de Materiais , Propriedades de Superfície , Difração de Raios XRESUMO
INTRODUCTION: One of the disadvantages of mineral trioxide aggregate (MTA) is washout (ie, the tendency of freshly prepared cement paste to disintegrate upon early contact with physiological fluids). A novel MTA (MTA Plus; Prevest Denpro, Jammu City, India) exhibits low washout and superior physical properties when mixed with a gel instead of water. When used as a root-end filler, MTA is in contact with both bone and root dentin. This study aimed to investigate the porosity and interfacial characteristics of the novel MTA mixed with water or antiwashout gel. METHODS: Porosity was evaluated after 1 or 28 days of immersion in Hank's balanced salt solution using mercury intrusion porosimetry. The root dentin to material interface was investigated using a scanning electron microscope and energy-dispersive X-ray spectroscopy complete with line scans and elemental maps. RESULTS: Anti-washout-type MTA Plus was found to have lower initial porosity than MTA Plus mixed with water although this trend was reversed after 28 days of immersion in physiological fluid. Both materials exhibited good marginal adaptation. The diffusion of silicon, calcium, and phosphorus across the cement/dentin interface was observed. CONCLUSIONS: MTA Plus mixed with antiwashout gel was found to have lower initial porosity than MTA Plus mixed with water. Both materials exhibited good marginal adaptation and the diffusion of silicon, calcium, and phosphorous across the cement/dentin interface. Thus, the anti-washout-type MTA can be considered to be a suitable substitute for ordinary MTA in all its indications.
Assuntos
Compostos de Alumínio/química , Compostos de Cálcio/química , Cavidade Pulpar/ultraestrutura , Dentina/ultraestrutura , Mercúrio/química , Óxidos/química , Materiais Restauradores do Canal Radicular/química , Silicatos/química , Cálcio/química , Adaptação Marginal Dentária , Cavidade Pulpar/química , Dentina/química , Difusão , Combinação de Medicamentos , Géis , Humanos , Soluções Isotônicas/química , Teste de Materiais , Microscopia Eletrônica de Varredura , Fósforo/química , Porosidade , Obturação Retrógrada/métodos , Silício/química , Solubilidade , Espectrometria por Raios X , Propriedades de Superfície , Fatores de Tempo , Água/químicaRESUMO
OBJECTIVES: The aim of this study was to evaluate the porosity and assess the root dentine to material interface of four root-end filling materials based on tricalcium silicate cement using two microscopy techniques. METHODS: The porosity of Bioaggregate, Biodentine, a prototype radiopacified tricalcium silicate cement (TCS-20-Zr) and intermediate restorative material (IRM) was evaluated after immersion for 28 days in Hank's balanced salt solution (HBSS) using mercury intrusion porosimetry. The root dentine to material interface of the cements when used as root-end filling materials in extracted human teeth was assessed after 28 days of dry storage and immersion in HBSS using a confocal microscope together with fluorescent tracers and also a field emission gun scanning electron microscope. RESULTS: Biodentine and IRM exhibited the lowest level or degree of porosity. The confocal microscopy used in conjunction to fluorescent tracers demonstrated that dry storage resulted in gaps at the root dentine to material interface and also cracks in the material with Biodentine being the most affected. Zinc was shown to be present in root dentine adjacent to the IRM restorations. CONCLUSIONS: Dry storage of Biodentine resulted in changes in the material microstructure and cracks at the root dentine to Biodentine interface. Furthermore, the gaps resulting from material shrinkage allowed the passage of the fluorescent microspheres thus indicating that these gaps are significant and can potentially allow the passage of micro-organisms.
Assuntos
Compostos de Cálcio/química , Dentina/química , Materiais Restauradores do Canal Radicular , Silicatos/química , Raiz Dentária/química , Humanos , PorosidadeRESUMO
The aim of this study was to compare two endodontic preparation systems using micro-CT analysis. Twenty-four one-rooted mandibular premolars were selected and randomly assigned to two groups. The samples (n = 12) of Group 1 were prepared using the ProTaper Universal rotary system, while Group 2 (n = 12) was prepared using the EndoEZE AET system complemented by manual apical preparation with K-type hand files up to #30. A 2.5% sodium hypochlorite solution was used in both groups for irrigating. Both groups were scanned by high-resolution microcomputed tomography before and after preparation (SkyScan 1172, SkyScan, Kontich, Belgium). The root canal volume and surface area was measured before and after preparation, and the differences were calculated and analyzed for statistically significant differences using ANOVA complemented by the Tukey test (p < 0.05). The results showed no statistically significant differences between the mean volumes of dentin removal by the two systems. However, the EndoEZE AET system presented a significantly greater mean surface area compared to the ProTaper system (p < 0.05). The EndoEZE AET system enabled preparation of a greater root canal surface area when compared to the ProTaper Universal system. There seemed to be no difference in dentin volume loss between the two systems used.
Assuntos
Humanos , Instrumentos Odontológicos , Cavidade Pulpar , Preparo de Canal Radicular/instrumentação , Microtomografia por Raio-X , Ligas Dentárias , Dentina/química , Desenho de Equipamento , Níquel , Distribuição Aleatória , Reprodutibilidade dos Testes , Preparo de Canal Radicular/métodos , Aço Inoxidável , Estatísticas não Paramétricas , Propriedades de Superfície , TitânioRESUMO
The aim of this study was to compare two endodontic preparation systems using micro-CT analysis. Twenty-four one-rooted mandibular premolars were selected and randomly assigned to two groups. The samples (n = 12) of Group 1 were prepared using the ProTaper Universal rotary system, while Group 2 (n = 12) was prepared using the EndoEZE AET system complemented by manual apical preparation with K-type hand files up to #30. A 2.5% sodium hypochlorite solution was used in both groups for irrigating. Both groups were scanned by high-resolution microcomputed tomography before and after preparation (SkyScan 1172, SkyScan, Kontich, Belgium). The root canal volume and surface area was measured before and after preparation, and the differences were calculated and analyzed for statistically significant differences using ANOVA complemented by the Tukey test (p < 0.05). The results showed no statistically significant differences between the mean volumes of dentin removal by the two systems. However, the EndoEZE AET system presented a significantly greater mean surface area compared to the ProTaper system (p < 0.05). The EndoEZE AET system enabled preparation of a greater root canal surface area when compared to the ProTaper Universal system. There seemed to be no difference in dentin volume loss between the two systems used.
Assuntos
Instrumentos Odontológicos , Cavidade Pulpar/diagnóstico por imagem , Preparo de Canal Radicular/instrumentação , Microtomografia por Raio-X , Ligas Dentárias , Dentina/química , Desenho de Equipamento , Humanos , Níquel , Distribuição Aleatória , Reprodutibilidade dos Testes , Preparo de Canal Radicular/métodos , Aço Inoxidável , Estatísticas não Paramétricas , Propriedades de Superfície , TitânioRESUMO
This study evaluated the ability of ions from a non-alcoholic calcium hydroxide-propolis paste to diffuse through dentinal tubules. Thirty-six single-rooted bovine teeth were used. The tooth crowns were removed, and the root canals were instrumented and divided into 3 groups: Group 1 - calcium hydroxide-propylene glycol paste; Group 2 - calcium hydroxide-saline solution paste; Group 3 - calcium hydroxide-propolis paste. After the root canal dressings were applied, the teeth were sealed and placed in containers with deionized water. The pH of the water was measured after 3, 24, 72 and 168 hours to determine the diffusion of calcium hydroxide ions through the dentinal tubules. All of the pastes studied promoted the diffusion of calcium hydroxide ions through the dentinal tubules. Associating propolis to calcium hydroxide resulted in a pH increase, which occurred with greater intensity after 72 hours. The calcium hydroxide-propolis paste was able to diffuse in dentin.
Assuntos
Animais , Bovinos , Anti-Infecciosos/farmacocinética , Hidróxido de Cálcio/farmacocinética , Dentina/química , Própole/farmacocinética , Anti-Infecciosos/química , Hidróxido de Cálcio/química , Difusão , Cavidade Pulpar/química , Cavidade Pulpar/efeitos dos fármacos , Dentina/efeitos dos fármacos , Concentração de Íons de Hidrogênio , Íons/farmacocinética , Teste de Materiais , Própole/química , Preparo de Canal Radicular , Fatores de TempoRESUMO
This study evaluated the ability of ions from a non-alcoholic calcium hydroxide-propolis paste to diffuse through dentinal tubules. Thirty-six single-rooted bovine teeth were used. The tooth crowns were removed, and the root canals were instrumented and divided into 3 groups: Group 1 - calcium hydroxide-propylene glycol paste; Group 2 - calcium hydroxide-saline solution paste; Group 3 - calcium hydroxide-propolis paste. After the root canal dressings were applied, the teeth were sealed and placed in containers with deionized water. The pH of the water was measured after 3, 24, 72 and 168 hours to determine the diffusion of calcium hydroxide ions through the dentinal tubules. All of the pastes studied promoted the diffusion of calcium hydroxide ions through the dentinal tubules. Associating propolis to calcium hydroxide resulted in a pH increase, which occurred with greater intensity after 72 hours. The calcium hydroxide-propolis paste was able to diffuse in dentin.