ABSTRACT
AIM: To fabricate and characterize nano-hydroxyapatite (nHA) grafted and non-grafted glass fibre-based endodontic posts. METHODOLOGY: Experimental glass fibre posts were fabricated using silanized nHA grafted (ex-HA) and non-grafted glass fibre (ex-P) reinforced resins. The structural analysis and morphological patterns were analysed with Fourier transform infrared spectroscopy and scanning electron microscopy, respectively. EverStick® glass fibre posts (eS) were used as a control group. The degree of conversion, flexural strength, and flexural modulus was investigated and the fractured structure was evaluated with a scanning electron microscope. Root canals were prepared in human extracted teeth restored with experimental and control posts. The push-out bond strength was evaluated with radicular dentine at days 7, 30, and 90, and the presence of voids at the interface were measured at day 1, 7, 30, and 90 with micro-computed tomography. The Shapiro-Wilk test and one-way ANOVA post-hoc Tukey's test were performed. The level of significance was set at 0.05. RESULTS: The SEM and FTIR confirmed the presence of a silane-coupling agent on the glass fibres. The ex-HA post had a significantly lower degree of conversion compared to the ex-P post (p = .0008), but a significantly higher conversion than the eS post (p = .0014). The maximum flexural strength value was obtained with the ex-HA post with an insignificant difference (p = .366) compared to ex-P post and a significant difference (p = .029) compared to the eS post. The flexural modulus of ex-HA, ex-P, and eS posts were significantly different (p = .037). Similarly, the ex-HA post had a significantly higher push-out bond strength at days 7 and 30 (p = .037) compared to the ex-P and eS posts. The volume of voids had a nonlinear behaviour amongst the groups with no significant difference between the posts. CONCLUSION: The fabrication of the experimental posts was successful and the ex-HA post had greater flexural strength and push-out bond strength compared to the ex-P post. The degree of conversion of the ex-HA post was lower than the ex-P and eS posts. The volume of voids of ex-HA and ex-P posts was lower than that of eS posts.
Subject(s)
Dental Bonding , Post and Core Technique , Apatites , Composite Resins , Dental Stress Analysis , Dentin , Glass , Humans , Laboratories , Materials Testing , Resin Cements , X-Ray MicrotomographyABSTRACT
AIM: The International Endodontic Journal (IEJ) has served as a platform for research and clinical practice in Endodontics since 1967. This study provides a bibliographic analysis and overview of the publications that have appeared in the IEJ from 1967 to 2020. METHODOLOGY: A literature search was performed in Elsevier's Scopus database to locate all the publications of the International Endodontic Journal. Various bibliometric software packages including the open-source visualization software Gephi and Biblioshiny (version 2.0) were employed for data visualization and analysis. RESULTS: A total of 3739 records with citation and bibliographic details were selected and retrieved to allow a bibliometric analysis to be performed. The bibliometric analysis indicates that the IEJ has grown both in terms of productivity and influence. Over time, the journal has been associated with an increase in the number of manuscripts published and the citations they have attracted, but with minor downward fluctuations in citations in the last few years. Bibliographic coupling of the IEJ articles revealed that the major research themes published in the journal include 'endodontics', 'root canal treatment', 'calcium hydroxide', 'apical periodontitis', 'mineral trioxide aggregate', 'microbiology', 'cyclic fatigue', 'cone-beam computed tomography' and 'micro-computed tomography'. Authors affiliated to institutions in the UK were the major contributors to the journal and were linked with other countries such as Brazil, USA and Malaysia. The largest number of publications were from the University of São Paulo, Brazil. CONCLUSION: The IEJ is one of the leading journals in Endodontology and has been providing a platform for innovative research and clinical reports for more than 50 years. Publications have been associated with a wide range of authors, institutions and countries around the world.