ABSTRACT
Digital light processing (DLP) 3D printing has shown great advantages such as high resolution in the fabrication of 3D objects toward a range of applications. Despite the rapid development of photocurable materials for DLP printing, tailoring properties to meet the specific demands for various applications remains challenging. Herein, we introduce copolymers of caprolactone and allyl caprolactone offering built-in functionality for thiol-ene photochemistry, thereby omitting the need for postfunctionalization. A crystalline block copolymer and an amorphous statistical copolymer were synthesized with the same comonomer composition and molecular weight. Thio-ene photocuring with a tetrafunctional thiol cross-linker was studied at different thiol to double-bond ratios for the copolymers and their blends. All formulations undergo rapid photocuring within several seconds of irradiation with slightly higher gel fractions observed for the statistical copolymer over the block copolymer under the same conditions, suggesting a somewhat higher cross-link density. Thermal properties of the networks were dependent on the presence of the semicrystalline block copolymer, where higher melting enthalpies were reached at higher block copolymer content. Similarly, crystallinity was found to be the main contributor to the mechanical properties. For a comparable composition, the modulus of a block copolymer network was found to be 31 times higher than that of the statistical copolymer network (27.7 vs 0.89 MPa). Intermediate moduli could be obtained by blending the two copolymers. DLP-printed scaffolds from these copolymers retained their thermal properties, therefore offering an efficient approach to tailoring mechanical properties, through crystallinity. Moreover, the printed scaffold displayed shape memory properties as the first example of poly(carprolactone) (PCL) copolymers in DLP printing. These materials are readily synthesized, offer fast and high-resolution 3D printing, and are degradable and cell compatible. They offer a straightforward approach to tailoring properties of PCL-based biomaterials and devices.
ABSTRACT
Transparent nanocomposite films made of surface-modified titanium dioxide nanoparticles and thermoplastic polyurethane are prepared via film casting approach showing enhanced refractive indexes and mechanical properties. Two different sets of composites were prepared up to 37.5 wt % of inorganic nanoparticles with a diameter <15 nm, one set using particles capped only with oleic acid and a second one with a bimodal system layer made of oleic acid and mPEO-5000 as coating agents. All of the composites show significantly enhanced refractive index and mechanical properties than the neat polymeric matrix. The transparency of nanocomposite films shows the excellent dispersion of the inorganic nanoparticles in the polymeric matrix avoiding aggregation and precipitation phenomena. Our study provides a facile and feasible route to produce transparent nanocomposite films with tunable mechanical properties and high refractive indices for various applications.