In-Plane Chemical Ordering (Mo2/3 R1/3 )2 AlB2 (R = Tb, Dy, Ho, Er, Tm, and Lu) i-MAB Phases and their Two-Dimensional Derivatives (MBene): Synthesis, Structure, Magnetic, and Supercapacitor Performance.

A family of hexagonal in-plane chemical ordering (Mo2/3 R1/3 )2 AlB2 (R = Tb, Dy, Ho, Er, Tm, and Lu) i-MAB phases are synthesized with R-3m hexagonal structure. The i-MAB phases with R = Tb to Tm are considered to have a nonlinear ferromagnetic-like coupling magnetic ground state with gradually weakened magnetocrystalline anisotropy due to variant R-R distances and 4f electrons. Their 2D derivatives (2D-MBene) with rare-earth (R) atom vacancies are obtained by chemical etching. The delamination solvent, surface functional terminations, and chemical bond of 2D-MBene can be modified by one-step nitridation in environment-friendly nitrogen instead of ammonia. A phase conversion is caused by nitridation at 973 K from 2D-MBene to Mo2 N, leading to the optimized specific capacitance of 229 F g-1 . Besides exploring more rare-earth-containing laminated boride systems, this work also demonstrates the promising application of their 2D derivatives with R vacancies in supercapacitors.