RESUMEN
Binary metal hydrides can act as low-temperature reducing agents for complex oxides in the solid state, facilitating the synthesis of anion-deficient oxide or oxyhydride phases. The reaction of LaSrCoRuO6, with CaH2 in a sealed tube yields the face-centered cubic phase LaSrCoRuO3.2H1.9. The reaction with LiH under similar conditions converts LaSrCoRuO6 to a mixture of tetragonal LaSrCoRuO4.8H1.2 and cubic LaSrCoRuO3.3H2.13. The formation of the LaSrCoRuOxHy oxyhydride phases proceeds directly from the parent oxide, with no evidence for anion-deficient LaSrCoRuO6-x intermediates, in contrast with many other topochemically synthesized transition-metal oxyhydrides. However, the reaction between LaSrCoRuO6 and LiH under flowing argon yields a mixture of LaSrCoRuO5 and the infinite layer phase LaSrCoRuO4. The change to all-oxide products when reactions are performed under flowing argon is attributed to the lower hydrogen partial pressure under these conditions. The implications for the reaction mechanism of these topochemical transformations is discussed along with the role of the hydrogen partial pressure in oxyhydride synthesis. Magnetization measurements indicate the LaSrCoRuOxHy phases exhibit local moments on Co and Ru centers, which are coupled antiferromagnetically. In contrast, LaSrCoRuO4 exhibits ferromagnetic behavior with a Curie temperature above 350 K, which can be rationalized on the basis of superexchange coupling between the Co1+ and Ru2+ centers.
RESUMEN
Complex transition-metal oxides exhibit a wide variety of chemical and physical properties which are a strong function the local electronic states of the transition-metal centres, as determined by a combination of metal oxidation state and local coordination environment. Topochemical reduction of the double perovskite oxide, LaSrCoRuO6 , using Zr, yields LaSrCoRuO5 . This reduced phase contains an ordered array of apex-linked square-based pyramidal Ru3+ O5 , square-planar Co1+ O4 and octahedral Co3+ O6 units, consistent with the coordination-geometry driven disproportionation of Co2+ . Coordination-geometry driven disproportionation of d7 transition-metal cations (e.g. Rh2+ , Pd3+ , Pt3+ ) is common in complex oxides containing 4d and 5d metals. However, the weak ligand field experienced by a 3d transition-metal such as cobalt leads to the expectation that d7+ Co2+ should be stable to disproportionation in oxide environments, so the presence of Co1+ O4 and Co3+ O6 units in LaSrCoRuO5 is surprising. Low-temperature measurements indicate LaSrCoRuO5 adopts a ferromagnetically ordered state below 120â K due to couplings between S=1 /2 Ru3+ and S=1 Co1+ .
RESUMEN
Sr2FeO3F, an oxyfluoride compound with an n = 1 Ruddlesden-Popper structure, was identified as a potential interesting mixed ionic and electronic conductor (MIEC). The phase can be synthesized under a range of different pO2 atmospheres, leading to various degrees of fluorine for oxygen substitution and Fe4+ content. A structural investigation and thorough comparison of both argon- and air-synthesized compounds were performed by combining high-resolution X-ray and electron diffraction, high-resolution scanning transmission electron microscopy, Mössbauer spectroscopy, and DFT calculations. While the argon-synthesized phase shows a well-behaved O/F ordered structure, this study revealed that oxidation leads to averaged large-scale anionic disorder on the apical site. In the more oxidized Sr2FeO3.2F0.8 oxyfluoride, containing 20% of Fe4+, two different Fe positions can be identified with a 32%/68% occupancy (P4/nmm space group). This originates due to the presence of antiphase boundaries between ordered domains within the grains. Relations between site distortion and valence states as well as stability of apical anionic sites (O vs F) are discussed. This study paves the way for further studies on both ionic and electronic transport properties of Sr2FeO3.2F0.8 and its use in MIEC-based devices, such as solid oxide fuel cells.
RESUMEN
A novel synthetic approach is described for the targeted preparation of multivariate metal-organic frameworks (MTV-MOFs) with specific combinations of metal elements. This methodology is based on the use of molecular complexes that already comprise desired metal-atom combinations, as building units for the MTV-MOF synthesis. These units are transformed into the MOF structural constituents through a ligand/linker exchange process that involves structural modifications while preserving their originally encoded atomic combination. Thus, through the use of heterometallic ring-shaped molecules combining gallium and nickel or cobalt, we have obtained MOFs with identical combinations of the metal elements, now incorporated in the rod-shaped secondary building unit, as confirmed with a combination of X-ray and electron diffraction, electron microscopy, and X-ray absorption spectroscopy techniques.
Asunto(s)
Galio , Estructuras Metalorgánicas , Cobalto , Galio/química , Ligandos , Estructuras Metalorgánicas/química , NíquelRESUMEN
Two novel chromium oxide arsenide materials have been synthesized, Sr2CrO2Cr2OAs2 (i.e., Sr2Cr3As2O3) and Sr2CrO3CrAs (i.e., Sr2Cr2AsO3), both of which contain chromium ions in two distinct layers. Sr2CrO2Cr2OAs2 was targeted following electron microscopy measurements on a related phase. It crystallizes in the space group P4/mmm and accommodates distorted CrO4As2 octahedra containing Cr2+ and distorted CrO2As4 octahedra containing Cr3+. In contrast, Sr2CrO3CrAs incorporates Cr3+ in CrO5 square-pyramidal coordination in [Sr2CrO3]+ layers and Cr2+ ions in CrAs4 tetrahedra in [CrAs]- layers and crystallizes in the space group P4/nmm. Powder neutron diffraction data reveal antiferromagnetic ordering in both compounds. In Sr2CrO3CrAs the Cr2+ moments in the [CrAs]- layers exhibit long-range ordering, while the Cr3+ moments in the [Sr2CrO3]+ layers only exhibit short-range ordering. However, in Sr2CrO2Cr2OAs2, both the Cr2+ moments in the CrO4As2 environments and the Cr3+ moments in the CrO2As4 polyhedra are long-range-ordered below 530(10) K. Above this temperature, only the Cr3+ moments are ordered with a Néel temperature slightly in excess of 600 K. A subtle structural change is evident in Sr2CrO2Cr2OAs2 below the magnetic ordering transitions.
RESUMEN
A broad range of cationic nonstoichiometry has been demonstrated for the Li-rich layered rock-salt-type oxide Li2MoO3, which has generally been considered as a phase with a well-defined chemical composition. Li2+xMo1-xO3 (-0.037 ≤ x ≤ 0.124) solid solutions were synthesized via hydrogen reduction of Li2MoO4 in the temperature range of 650-1100 °C, with x decreasing with the increase of the reduction temperature. The solid solutions adopt a monoclinically distorted O3-type layered average structure and demonstrate a robust local ordering of the Li cations and Mo3 triangular clusters within the mixed Li/Mo cationic layers. The local structure was scrutinized in detail by electron diffraction and aberration-corrected scanning transmission electron microcopy (STEM), resulting in an ordering model comprising a uniform distribution of the Mo3 clusters compatible with local electroneutrality and chemical composition. The geometry of the triangular clusters with their oxygen environment (Mo3O13 groups) has been directly visualized using differential phase contrast STEM imaging. The established local structure was used as input for density functional theory (DFT)-based calculations; they support the proposed atomic arrangement and provide a plausible explanation for the staircase galvanostatic charge profiles upon electrochemical Li+ extraction from Li2+xMo1-xO3 in Li cells. According to DFT, all electrochemical capacity in Li2+xMo1-xO3 solely originates from the cationic Mo redox process, which proceeds via oxidation of the Mo3 triangular clusters into bent Mo3 chains where the electronic capacity of the clusters depends on the initial chemical composition and Mo oxidation state defining the width of the first charge low-voltage plateau. Further oxidation at the high-voltage plateau proceeds through decomposition of the Mo3 chains into Mo2 dimers and further into individual Mo6+ cations.
RESUMEN
The pursuit of two-dimensional (2D) borides, MBenes, has proven to be challenging, not the least because of the lack of a suitable precursor prone to the deintercalation. Here, we studied room-temperature topochemical deintercalation of lithium from the layered polymorphs of the LiNiB compound with a considerable amount of Li stored in between [NiB] layers (33 at. % Li). Deintercalation of Li leads to novel metastable borides (Liâ¼0.5NiB) with unique crystal structures. Partial removal of Li is accomplished by exposing the parent phases to air, water, or dilute HCl under ambient conditions. Scanning transmission electron microscopy and solid-state 7Li and 11B NMR spectroscopy, combined with X-ray pair distribution function (PDF) analysis and DFT calculations, were utilized to elucidate the novel structures of Liâ¼0.5NiB and the mechanism of Li-deintercalation. We have shown that the deintercalation of Li proceeds via a "zip-lock" mechanism, leading to the condensation of single [NiB] layers into double or triple layers bound via covalent bonds, resulting in structural fragments with Li[NiB]2 and Li[NiB]3 compositions. The crystal structure of Liâ¼0.5NiB is best described as an intergrowth of the ordered single [NiB], double [NiB]2, or triple [NiB]3 layers alternating with single Li layers; this explains its structural complexity. The formation of double or triple [NiB] layers induces a change in the magnetic behavior from temperature-independent paramagnets in the parent LiNiB compounds to the spin-glassiness in the deintercalated Liâ¼0.5NiB counterparts. LiNiB compounds showcase the potential to access a plethora of unique materials, including 2D MBenes (NiB).
RESUMEN
Understanding the electric dipole switching in multiferroic materials requires deep insight of the atomic-scale local structure evolution to reveal the ferroelectric mechanism, which remains unclear and lacks a solid experimental indicator in high-pressure prepared LiNbO3-type polar magnets. Here, we report the discovery of Zn-ion splitting in LiNbO3-type Zn2FeNbO6 established by multiple diffraction techniques. The coexistence of a high-temperature paraelectric-like phase in the polar Zn2FeNbO6 lattice motivated us to revisit other high-pressure prepared LiNbO3-type A2BB'O6 compounds. The A-site atomic splitting (â¼1.0-1.2 Å between the split-atom pair) in B/B'-mixed Zn2FeTaO6 and O/N-mixed ZnTaO2N is verified by both powder X-ray diffraction structural refinements and high angle annular dark field scanning transmission electron microscopy images, but is absent in single-B-site ZnSnO3. Theoretical calculations are in good agreement with experimental results and suggest that this kind of A-site splitting also exists in the B-site mixed Mn-analogues, Mn2FeMO6 (M = Nb, Ta) and anion-mixed MnTaO2N, where the smaller A-site splitting (â¼0.2 Å atomic displacement) is attributed to magnetic interactions and bonding between A and B cations. These findings reveal universal A-site splitting in LiNbO3-type structures with mixed multivalent B/B', or anionic sites, and the splitting-atomic displacement can be strongly suppressed by magnetic interactions and/or hybridization of valence bands between d electrons of the A- and B-site cations.
RESUMEN
Sr2CrO2Cr2As2 and Ba2CrO2Cr2As2 with Cr2+ ions in CrO2 sheets and in CrAs layers crystallize with the Sr2Mn3Sb2O2 structure (space group I4/mmm, Z = 2) and lattice parameters a = 4.00800(2) Å, c = 18.8214(1) Å (Sr2CrO2Cr2As2) and a = 4.05506(2) Å, c = 20.5637(1) Å (Ba2CrO2Cr2As2) at room temperature. Powder neutron diffraction reveals checkerboard-type antiferromagnetic ordering of the Cr2+ ions in the arsenide layers below TN1_Sr, of 600(10) K (Sr2CrO2Cr2As2) and TN1_Ba 465(5) K (Ba2CrO2Cr2As2) with the moments initially directed perpendicular to the layers in both compounds. Checkerboard-type antiferromagnetic ordering of the Cr2+ ions in the oxide layer below 230(5) K for Ba2CrO2Cr2As2 occurs with these moments also perpendicular to the layers, consistent with the orientation preferences of d4 moments in the two layers. In contrast, below 330(5) K in Sr2CrO2Cr2As2, the oxide layer Cr2+ moments are initially oriented in the CrO2 plane; but on further cooling, these moments rotate to become perpendicular to the CrO2 planes, while the moments in the arsenide layers rotate by 90° with the moments on the two sublattices remaining orthogonal throughout [behavior recently reported independently by Liu et al. [Liu et al. Phys. Rev. B 2018, 98, 134416]]. In Sr2CrO2Cr2As2, electron diffraction and high resolution powder X-ray diffraction data show no evidence for a structural distortion that would allow the two Cr2+ sublattices to couple, but high resolution neutron powder diffraction data suggest a small incommensurability between the magnetic structure and the crystal structure, which may account for the coupling of the two sublattices and the observed spin reorientation. The saturation values of the Cr2+ moments in the CrO2 layers (3.34(1) µB (for Sr2CrO2Cr2As2) and 3.30(1) µB (for Ba2CrO2Cr2As2)) are larger than those in the CrAs layers (2.68(1) µB for Sr2CrO2Cr2As2 and 2.298(8) µB for Ba2CrO2Cr2As2) reflecting greater covalency in the arsenide layers.
RESUMEN
The mineral Zlatogorite, CuNiSb2, was synthesized in the laboratory for the first time by annealing elements at ambient pressure (CuNiSb2-AP). Rietveld refinement of synchrotron powder X-ray diffraction data indicates that CuNiSb2-AP crystallizes in the NiAs-derived structure (P3m1, #164) with Cu and Ni ordering. The structure consists of alternate NiSb6 and CuSb6 octahedral layers via face-sharing. The formation of such structure instead of metal disordered NiAs-type structure (P63/mmc, #194) is validated by the lower energy of the ordered phase by first-principle calculations. Interatomic crystal orbital Hamilton population, electron localization function, and charge density analysis reveal strong Ni-Sb, Cu-Sb, and Cu-Ni bonding and long weak Sb-Sb interactions in CuNiSb2-AP. The magnetic measurement indicates that CuNiSb2-AP is Pauli paramagnetic. First-principle calculations and experimental electrical resistivity measurements reveal that CuNiSb2-AP is a metal. The low Seebeck coefficient and large thermal conductivity suggest that CuNiSb2 is not a potential thermoelectric material. Single crystals were grown by chemical vapor transport. The high pressure sample (CuNiSb2-8 GPa) was prepared by pressing CuNiSb2-AP at 700 °C and 8 GPa. However, the structures of single crystal and CuNiSb2-8 GPa are best fit with a disordered metal structure in the P3m1 space group, corroborated by transmission electron microscopy.
RESUMEN
Quasi phase-pure (>98 wt %) MAX phase solid solution ceramics with the (Zr,Ti)2(Al0.5,Sn0.5)C stoichiometry and variable Zr/Ti ratios were synthesized by both reactive hot pressing and pressureless sintering of ZrH2, TiH2, Al, Sn, and C powder mixtures. The influence of the different processing parameters, such as applied pressure and sintering atmosphere, on phase purity and microstructure of the produced ceramics was investigated. The addition of Sn to the (Zr,Ti)2AlC system was the key to achieve phase purity. Its effect on the crystal structure of a 211-type MAX phase was assessed by calculating the distortions of the octahedral M6C and trigonal M6A prisms due to steric effects. The M6A prismatic distortion values were found to be smaller in Sn-containing double solid solutions than in the (Zr,Ti)2AlC MAX phases. The coefficients of thermal expansion along the ⟨ a⟩ and ⟨ c⟩ directions were measured by means of Rietveld refinement of high-temperature synchrotron X-ray diffraction data of (Zr1- x,Ti x)2(Al0.5,Sn0.5)C MAX phase solid solutions with x = 0, 0.3, 0.7, and 1. The thermal expansion coefficient data of the Ti2(Al0.5,Sn0.5)C solid solution were compared with those of the Ti2AlC and Ti2SnC ternary compounds. The thermal expansion anisotropy increased in the (Zr,Ti)2(Al0.5,Sn0.5)C double solid solution MAX phases as compared to the Zr2(Al0.5,Sn0.5)C and Ti2(Al0.5,Sn0.5)C end-members.
RESUMEN
Reaction of the n = 1 Ruddlesden-Popper oxide LaSr3CoRuO8 with CaH2 yields the oxyhydride phase LaSr3CoRuO4H4 via a topochemical anion exchange. Close inspection of the X-ray and neutron powder diffraction data in combination with HAADF-STEM images reveals that the nanoparticles of SrO are exsolved from the system during the reaction, with the change in cation stoichiometry accommodated by the inclusion of n > 1 (Co/Ru)nOn+1H2n "perovskite" layers into the Ruddlesden-Popper stacking sequence. This novel pseudotopochemical process offers a new route for the formation of n > 1 Ruddlesden-Popper structured materials. Magnetization data are consistent with a LaSr3Co+Ru2+O4H4 (Co+, d8, S = 1; Ru2+, d6, S = 0) oxidation/spin state combination. Neutron diffraction and µ+SR data show no evidence for long-range magnetic order down to 2 K, suggesting the diamagnetic Ru2+ centers impede the Co-Co magnetic-exchange interactions.
RESUMEN
The chemical accessibility of the CeIV oxidation state enables redox chemistry to be performed on the naturally coinage-metal-deficient phases CeM1- xSO (M = Cu, Ag). A metastable black compound with the PbFCl structure type (space group P4/ nmm: a = 3.8396(1) Å, c = 6.607(4) Å, V = 97.40(6) Å3) and a composition approaching CeSO is obtained by deintercalation of Ag from CeAg0.8SO. High-resolution transmission electron microscopy reveals the presence of large defect-free regions in CeSO, but stacking faults are also evident which can be incorporated into a quantitative model to account for the severe peak anisotropy evident in all the high-resolution X-ray and neutron diffractograms of bulk CeSO samples; these suggest that a few percent of residual Ag remains. A straw-colored compound with the filled PbFCl (i.e., ZrSiCuAs- or HfCuSi2-type) structure (space group P4/ nmm: a = 3.98171(1) Å, c = 8.70913(5) Å, V = 138.075(1) Å3) and a composition close to LiCeSO, but with small amounts of residual Ag, is obtained by direct reductive lithiation of CeAg0.8SO or by insertion of Li into CeSO using chemical or electrochemical means. Computation of the band structure of pure, stoichiometric CeSO predicts it to be a Ce4+ compound with the 4f-states lying approximately 1 eV above the sulfide-dominated valence band maximum. Accordingly, the effective magnetic moment per Ce ion measured in the CeSO samples is much reduced from the value found for the Ce3+-containing LiCeSO, and the residual paramagnetism corresponds to the Ce3+ ions remaining due to the presence of residual Ag, which presumably reflects the difficulty of stabilizing Ce4+ in the presence of sulfide (S2-). Comparison of the behavior of CeCu0.8SO with that of CeAg0.8SO reveals much slower reaction kinetics associated with the Cu1- xS layers, and this enables intermediate CeCu1- xLi xSO phases to be isolated.
RESUMEN
We demonstrate that changes in the unit cell structure of lithium battery cathode materials during electrochemical cycling in liquid electrolyte can be determined for particles of just a few hundred nanometers in size using in situ transmission electron microscopy (TEM). The atomic coordinates, site occupancies (including lithium occupancy), and cell parameters of the materials can all be reliably quantified. This was achieved using electron diffraction tomography (EDT) in a sealed electrochemical cell with conventional liquid electrolyte (LP30) and LiFePO4 crystals, which have a well-documented charged structure to use as reference. In situ EDT in a liquid environment cell provides a viable alternative to in situ X-ray and neutron diffraction experiments due to the more local character of TEM, allowing for single crystal diffraction data to be obtained from multiphased powder samples and from submicrometer- to nanometer-sized particles. EDT is the first in situ TEM technique to provide information at the unit cell level in the liquid environment of a commercial TEM electrochemical cell. Its application to a wide range of electrochemical experiments in liquid environment cells and diverse types of crystalline materials can be envisaged.
RESUMEN
Two novel lithium nickel boride polymorphs, RT-LiNiB and HT-LiNiB, with layered crystal structures are reported. This family of compounds was theoretically predicted by using the adaptive genetic algorithm (AGA) and subsequently synthesized by a hydride route with LiH as the lithium source. Unique among the known ternary transition-metal borides, the LiNiB structures feature Li layers alternating with nearly planar [NiB] layers composed of Ni hexagonal rings with a B-B pair at the center. A comprehensive study using a combination of single crystal/synchrotron powder X-ray diffraction, solid-state 7 Li and 11 Bâ NMR spectroscopy, scanning transmission electron microscopy, quantum-chemical calculations, and magnetism has shed light on the intrinsic features of these polymorphic compounds. The unique layered structures of LiNiB compounds make them ultimate precursors for exfoliation studies, thus paving a way toward two-dimensional transition-metal borides, MBenes.
RESUMEN
A polycrystalline sample of SrLa2FeCoSbO9 has been prepared in a solid-state reaction and studied by a combination of electron microscopy, magnetometry, Mössbauer spectroscopy, X-ray diffraction, and neutron diffraction. The compound adopts a monoclinic (space group P21/ n; a = 5.6218(6), b = 5.6221(6), c = 7.9440(8) Å, ß = 90.050(7)° at 300 K) perovskite-like crystal structure with two crystallographically distinct six-coordinate sites. One of these sites is occupied by 2/3 Co2+, 1/3 Fe3+ and the other by 2/3 Sb5+, 1/3 Fe3+. This pattern of cation ordering results in a transition to a ferrimagnetic phase at 215 K. The magnetic moments on nearest-neighbor, six-coordinate cations align in an antiparallel manner, and the presence of diamagnetic Sb5+ on only one of the two sites results in a nonzero remanent magnetization of â¼1 µB per formula unit at 5 K.
RESUMEN
Sr2Fe3Se2O3 is a localized-moment iron oxide selenide in which two unusual coordinations for Fe2+ ions form two sublattices in a 2:1 ratio. In the paramagnetic region at room temperature, the compound adopts the crystal structure first reported for Sr2Co3S2O3, crystallizing in space group Pbam with a = 7.8121 Å, b = 10.2375 Å, c = 3.9939 Å, and Z = 2. The sublattice occupied by two-thirds of the iron ions (Fe2 site) is formed by a network of distorted mer-[FeSe3O3] octahedra linked via shared Se2 edges and O vertices forming layers, which connect to other layers by shared Se vertices. As shown by magnetometry, neutron powder diffraction, and Mössbauer spectroscopy measurements, these moments undergo long-range magnetic ordering below TN1 = 118 K, initially adopting a magnetic structure with a propagation vector (1/2 - δ, 0, 1/2) (0 ≤ δ ≤ 0.1) which is incommensurate with the nuclear structure and described in the Pbam1 '( a01/2)000 s magnetic superspace group, until at 92 K ( TINC) there is a first order lock-in transition to a structure in which these Fe2 moments form a magnetic structure with a propagation vector (1/2, 0, 1/2) which may be modeled using a 2 a × b × 2 c expansion of the nuclear cell in space group 36.178 B a b21 m (BNS notation). Below TN2 = 52 K the remaining third of the Fe2+ moments (Fe1 site) which are in a compressed trans-[FeSe4O2] octahedral environment undergo long-range ordering, as is evident from the magnetometry, the Mössbauer spectra, and the appearance of new magnetic Bragg peaks in the neutron diffractograms. The ordering of the second set of moments on the Fe1 sites results in a slight reorientation of the majority moments on the Fe2 sites. The magnetic structure at 1.5 K is described by a 2 a × 2 b × 2 c expansion of the nuclear cell in space group 9.40 I a b (BNS notation).
RESUMEN
The presence of secondary phases is one of the main issues that hinder the growth of pure kesterite Cu2ZnSnS4 (CZTS) based thin films with suitable electronic and junction properties for efficient solar cell devices. In this work, CZTS thin films with varied Zn and Sn content have been prepared by RF-power controlled co-sputtering deposition using Cu, ZnS and SnS targets and a subsequent sulphurization step. Detailed TEM investigations show that the film shows a layered structure with the majority of the top layer being the kesterite phase. Depending on the initial thin film composition, either about ~1 µm Cu-rich and Zn-poor kesterite or stoichiometric CZTS is formed as top layer. X-ray diffraction, Raman spectroscopy and transmission electron microscopy reveal the presence of Cu2-xS, ZnS and SnO2 minor secondary phases in the form of nanoinclusions or nanoparticles or intermediate layers.
RESUMEN
The noncentrosymmetric tungstate oxide, Ce18W10O57, was synthesized for the first time as high-quality single crystals via the molten chloride flux method and structurally characterized by single-crystal X-ray diffraction. The compound is a structural analogue to the previously reported La18W10O57, which crystallizes in the hexagonal space group P6Ì 2c. The +3 oxidation state of cerium in Ce18W10O57 was achieved via the in situ reduction of Ce(IV) to Ce(III) using Zn metal. The structure consists of both isolated and face-shared WO6 octahedra and, surprisingly, isolated WO6 trigonal prisms. A careful analysis of the packing arrangement in the structure makes it possible to explain the unusual structural architecture of Ce18W10O57, which is described in detail. The temperature-dependent magnetic susceptibility of Ce18W10O57 indicates that the cerium(III) f1 cations do not order magnetically and exhibit simple paramagnetic behavior. The SHG efficiency of Ln18W10O57 (Ln = La, Ce) was measured as a function of particle size, and both compounds were found to be SHG active with efficiency approximately equal to that of α-SiO2.
RESUMEN
This study reports on the synthesis and characterization of MAX phases in the (Zr,Ti)n+1AlCn system. The MAX phases were synthesized by reactive hot pressing and pressureless sintering in the 1350-1700 °C temperature range. The produced ceramics contained large fractions of 211 and 312 (n = 1, 2) MAX phases, while strong evidence of a 413 (n = 3) stacking was found. Moreover, (Zr,Ti)C, ZrAl2, ZrAl3, and Zr2Al3 were present as secondary phases. In general, the lattice parameters of the hexagonal 211 and 312 phases followed Vegard's law over the complete Zr-Ti solid solution range, but the 312 phase showed a non-negligible deviation from Vegard's law around the (Zr0.33,Ti0.67)3Al1.2C1.6 stoichiometry. High-resolution scanning transmission electron microscopy combined with X-ray diffraction demonstrated ordering of the Zr and Ti atoms in the 312 phase, whereby Zr atoms occupied preferentially the central position in the close-packed M6X octahedral layers. The same ordering was also observed in 413 stackings present within the 312 phase. The decomposition of the secondary (Zr,Ti)C phase was attributed to the miscibility gap in the ZrC-TiC system.