RESUMEN
The effect of Al2O3/LiF dual coatings on the electrochemical performance of over-lithiated layered oxide (OLO) has been investigated. A uniform coating of Al2O3 and LiF is obtained on the surface of the layered pristine material. The OLO with a dual Al2O3/LiF coating with a ratio of 1 : 1.5 exhibits excellent electrochemical performance. An initial discharge capacity of 265.66 mA h g(-1) is obtained at a C-rate of 0.1C. This capacity is approximately 15 mA h g(-1) higher than that of pristine OLO. The capacity retention (92.8% at the 50th cycle) is also comparable to that of pristine OLO (91.4% at the 50th cycle). Coating the cathode with a dual layer comprising Al2O3 and LiF leads to improved charging and discharging kinetics, and prevents direct contact between the cathode and the electrolyte.
RESUMEN
The effect of bi-functional coatings consisting of Zr and phosphate (P) on the electrochemical performance of Li1.0Ni0.8Co0.15Mn0.05O2 (NCM) has been investigated. The presence of various types of Zr and P compounds such as oxides (ZrO2 and Li2ZrO3) and phosphates (Zr2P2O9, ZrP2O7 and LiZr2(PO4)3) in the coating was confirmed by experiments as well as density functional theory (DFT) calculations. When the NCM samples were coated with the Zr/P hybrid material, the cycle retention and the amount of removed Li residuals (LiOH, Li2CO3) were enhanced by the synergistic effect from Zr and P. The NCM sample coated with a Zr/P layer with a Zr/P ratio of 1 : 1 exhibited an increase in the initial capacity (209.3 mA h g-1) compared to the pristine sample (207.4 mA h g-1) at 0.1C, owing to the formation of the coating layer. The capacity retention of the Zr/P coated sample (92.4% at the 50th cycle) was also improved compared to that of the pristine NCM sample (90.6% at the 50th cycle). Moreover, the amount of Li residuals in the Zr/P coated NCM sample was greatly reduced from 3693 ppm (pristine NCM) to 2525 ppm (Zr/P = 5 : 5).
RESUMEN
The solvent evaporation method on the structural changes and surface chemistry of the cathode and the effect of electrochemical performance of Li1.0Ni0.8Co0.15Mn0.05O2 (NCM) has been investigated. After dissolving of Li residuals using minimum content of solvent in order to minimize the damage of pristine material and the evaporation time, the solvent was evaporated without filtering and remaining powder was re-heated at 700 °C in oxygen environment. Two kinds of solvent, de-ionized water and diluted nitric acid, were used as a solvent. The almost 40% of Li residuals were removed using solvent evaporation method. The NCM sample after solvent evaporation process exhibited an increase in the initial capacity (214.3 mAh/g) compared to the pristine sample (207.4 mAh/g) at 0.1C because of enhancement of electric conductivity caused by decline of Li residuals. The capacity retention of NCM sample after solvent evaporation process (96.0% at the 50th cycle) was also improved compared to that of the pristine NCM sample (90.6% at the 50th cycle). The uniform Li residual layer after solvent treated and heat treatment acted like a coating layer, leading to enhance the cycle performance. The NCM sample using diluted nitric acid showed better performance than that using de-ionized water.
RESUMEN
The real time detection of quantitative oxygen release from the cathode is performed by in-situ Gas Chromatography as a tool to not only determine the amount of oxygen release from a lithium-ion cell but also to address the safety concerns. This in-situ gas chromatography technique monitoring the gas evolution during electrochemical reaction presents opportunities to clearly understand the effect of surface modification and predict on the cathode stability. The oxide cathode, 0.5Li2MnO3â0.5LiNi0.4Co0.2Mn0.4O2, surface modified by amorphous cobalt-phosphate nanoparticles (a-CoPO4) is prepared by a simple co-precipitation reaction followed by a mild heat treatment. The presence of a 40 nm thick a-CoPO4 coating layer wrapping the oxide powders is confirmed by electron microscopy. The electrochemical measurements reveal that the a-CoPO4 coated overlithiated layered oxide cathode shows better performances than the pristine counterpart. The enhanced performance of the surface modified oxide is attributed to the uniformly coated Co-P-O layer facilitating the suppression of O2 evolution and offering potential lithium host sites. Further, the formation of a stable SEI layer protecting electrolyte decomposition also contributes to enhanced stabilities with lesser voltage decay. The in-situ gas chromatography technique to study electrode safety offers opportunities to investigate the safety issues of a variety of nanostructured electrodes.