Nanostructured calcium phosphate coatings on magnesium alloys: characterization and cytocompatibility with mesenchymal stem cells.

This article reports the deposition and characterization of nanostructured calcium phosphate (nCaP) on magnesium-yttrium alloy substrates and their cytocompatibility with bone marrow derived mesenchymal stem cells (BMSCs). The nCaP coatings were deposited on magnesium and magnesium-yttrium alloy substrates using proprietary transonic particle acceleration process for the dual purposes of modulating substrate degradation and BMSC adhesion. Surface morphology and feature size were analyzed using scanning electron microscopy and quantitative image analysis tools. Surface elemental compositions and phases were analyzed using energy dispersive X-ray spectroscopy and X-ray diffraction, respectively. The deposited nCaP coatings showed a homogeneous particulate surface with the dominant feature size of 200-500 nm in the long axis and 100-300 nm in the short axis, and a Ca/P atomic ratio of 1.5-1.6. Hydroxyapatite was the major phase identified in the nCaP coatings. The modulatory effects of nCaP coatings on the sample degradation and BMSC behaviors were dependent on the substrate composition and surface conditions. The direct culture of BMSCs in vitro indicated that multiple factors, including surface composition and topography, and the degradation-induced changes in media composition, influenced cell adhesion directly on the sample surface, and indirect adhesion surrounding the sample in the same culture. The alkaline pH, the indicator of Mg degradation, played a role in BMSC adhesion and morphology, but not the sole factor. Additional studies are necessary to elucidate BMSC responses to each contributing factor.

The effects of nanostructured hydroxyapatite coating on the biodegradation and cytocompatibility of magnesium implants.

Magnesium (Mg) alloys, a novel class of degradable, metallic biomaterials, have attracted growing interest as a promising alternative for medical implant and device applications due to their advantageous mechanical and biological properties. Although its biodegradability is an attractive property, rapid degradation of Mg in the physiological environments imposes a major obstacle that limits the translation of Mg-based implants to clinical applications. Therefore, the objective of this study was to develop a nanostructured hydroxyapatite (nHA) coating on polished Mg substrates to mediate the rapid degradation of Mg while improving its integration with bone tissue for orthopedic applications. The nHA coatings were deposited on polished Mg using the patented transonic particle acceleration (Spire Biomedical) process. Surface morphology, elemental compositions, and crystal structures were characterized using scanning electron microscopy, energy dispersive X-ray spectroscopy, and X-ray diffraction (XRD) analysis, respectively. The degradation of nHA-coated and non-coated Mg samples was investigated by incubating the samples in phosphate buffered saline and revised simulated body fluid, under standard cell culture conditions. Rat bone marrow stromal cells (BMSCs) were harvested and cultured with nHA-coated and non-coated Mg samples to determine cytocompatibility. The degradation results suggested that the nHA coatings decreased Mg degradation. Improved BMSC adhesion was observed on the surfaces of the nHA-coated and non-coated Mg samples, in comparison with the cells on the culture plate surrounding the Mg samples. In conclusion, nHA coatings showed promise for improving the biodegradation and cytocompatibility properties of Mg-based orthopedic implants and should be further studied.