RESUMEN
This work aimed to develop and evaluate the influence of processing variables on the morphology and swelling of sulfonated poly(ether ether ketone) (SPEEK) spheres for possible applications as a biomaterial. We used the drip method to obtain spheres with the polymer starting solutions SPEEK-6 (w/v: 6%) and SPEEK-10 (w/v: 10%), drip rates (20 and 30 mL/h), and drip heights (5 and 10 cm) in experimental planning. The samples were characterized by Fourier-transform infrared spectroscopy (FTIR), optical microscopy (OM), the absorption capacity of phosphate-buffered saline (PBS) by swelling (%), and statistical analysis of data through Design of Experiments (DOE). The obtained results evidenced that the processing variables influenced the morphology and swelling. Spheres with a bigger concentration of the polymer solution presented a greater degree of sulfonation (DS). We verified that the diameter of the spheres was directly related to the variable height and the sphericity was associated with the speed and viscosity of the solution. Bigger and more pores in a greater amount were observed in the spheres with a greater DS, influencing the behavior of the swelling in PBS. The better variable combinations with a high DS, regular sphericity, a smaller diameter, and greater swelling were the samples S2-10-20-5 e S10-10-20-5. The cytotoxicity indicated that the best samples obtained in the experimental planning (S2-10-20-5 and S10-10-20-5) were not toxic. In that regard, the evaluated spheres presented cell viability and swelling capacity, suggesting their possible applications as biomaterials.
RESUMEN
Purified clay was modified with different amounts of alkyl ammonium and phosphonium salts and used as filler in the preparation of PET nanocomposites via melt intercalation. The effect of this type of filler on morphology and thermal and mechanical properties of PET nanocomposites was investigated by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetric analyses (TG), tensile properties, and transmission electron microscopy (TEM). The results showed that the mixture of alkyl ammonium and phosphonium salts favored the production of PET nanocomposites with intercalated and partially exfoliated morphologies with slight improvement in thermal stability. In addition, the incorporation of these organoclays tended to inhibit PET crystallization behavior, which is profitable in the production of transparent bottles.