Compared with a single semiconductor, the heterojunction formed by two different semiconductors usually has higher light utilization and better photoelectric performance. By using stable TiO2 nanotubes as the main subject, CdSe/TiO2NTs heterojunctions were synthesized by a hydrothermal method. XRD, TEM, SEM, PL, UV-vis, and EIS were used to characterize the fabricated CdSe/TiO2NTs. Under visible light irradiation, CdSe/TiO2NTs heterojunctions exhibited a higher absorption intensity and lower degree of photogenerated carrier recombination than TiO2. The electrons and holes were proven to be effectively separated in this heterojunction via theoretical calculation. Under CdSe/TiO2NTs' optimal conditions, the glucose concentrations (10-90 µM) had a linear relationship with the photocurrent value, and the detection limit was 3.1 µM. Moreover, the CdSe/TiO2NTs sensor exhibited good selectivity and stability. Based on the experimental data and theoretical calculations, its PEC sensing mechanism was also illuminated.
Asunto(s)
Compuestos de Cadmio , Compuestos de Selenio , Compuestos de Cadmio/química , Compuestos de Selenio/química , Titanio/química , GlucosaRESUMEN
The formation of heterojunction structures can effectively prevent the recombination of photogenerated electron-hole pairs in semiconductors and result in the enhancement of photoelectric properties. Using TiO2 nanotubes (prepared using the hydrothermal-impregnation method) as carriers, CdS-TiO2NTs were fabricated as a photoelectrochemical (PEC) sensor, which can be used under visible light and can exhibit good PEC performance due to the existence of the heterojunction structure. The experimental results show that the prepared CdS-TiO2NTs electrode had a linear response to 2-16 mM glutathione (GSH). The sensor's sensitivity and detection limit (LOD) were 102.9 µA·mM-1 cm-2 and 27.7 µM, respectively. Moreover, the biosensor had good stability, indicating the potential application of this kind of heterojunction PEC biosensor.