RESUMEN
AIM: To assess and compare the flexibility and torsional resistance of PathFile, RaCe ISO 10 and Scout RaCe instruments in relation to stainless steel K-File hand instruments. METHODOLOGY: Rotary PathFile (sizes 13, 16 and 19; .02 taper), Race ISO 10 (size 10; 0.02, 0.04 and 0.06 tapers), Scout RaCe (sizes 10, 15 and 20; 0.02 taper) and hand K-File (sizes 10, 15 and 20; 0.02 taper) instruments were evaluated. Alloy chemical composition, phases present and transformation temperatures were determined for the NiTi instruments. For all instruments, diameters at each millimetre from the tip as well as cross-sectional areas at 3 mm from the tip were measured based on ANSI/ADA Specification No. 101 using image analysis software. Resistance to bending and torsional resistance were determined according to specification ISO 3630-1. Vickers microhardness measurements were also taken in all instruments to assess their strength. Data were analysed using analysis of variance (α = 0.05). RESULTS: The alloys used in the manufacture of the three types of NiTi instruments had approximately the same chemical composition, but the PathFile instruments had a higher Af transformation temperature and contained a small amount of B19' martensite. All instruments had diameter values within the standard tolerance. The bending and torsional resistance values were significantly increased relative to the instrument diameter and cross-sectional area. CONCLUSIONS: PathFile instruments were the most flexible and the least torque resistant, whilst the stainless steel instruments were the least flexible although they were more torque resistant than the NiTi instruments.
Asunto(s)
Instrumentos Dentales , Análisis de Falla de Equipo , Níquel/química , Preparación del Conducto Radicular/instrumentación , Titanio/química , Aleaciones Dentales/química , Diseño de Equipo , Ensayo de Materiales , Docilidad , Espectrometría por Rayos X , Acero Inoxidable/química , TorqueRESUMEN
AIM: To compare the flexibility, torsional resistance and structural and dimensional characteristics of instruments produced by twisting with those of a geometrically similar nickel-titanium (NiTi) system produced by a grinding process. METHODOLOGY: The mean diameters along the flute and the pitch length of size 25, .04 taper, size 25, .06 taper, and size 25, .08 taper Twisted File (TF) (SybronEndo, Orange, CA, USA), and size 25, .04 taper, and size 25, .06 taper RaCe instruments (FKG, La Chaux-de-Fonds, Switzerland) (n = 10 each) were measured according to ANSI/ADA specification No. 101. Two pairs of instruments were found to have similar diameters at 3 mm from the tip: TF size 25, .06 taper and RaCe size 25, .04 taper, and TF size 25, .08 taper and RaCe size 25, .06 taper. The cross-sectional areas at 3 mm from the tip were determined. These instruments were then submitted to energy-dispersive X-ray spectroscopy, X-ray diffraction, differential scanning calorimetry (DSC), and Vickers microhardness measurements. Bending moment at 45° and maximum torque at fracture were measured (n = 10) according to specification ISO 3630-1. Data were analysed using analysis of variance (α = 0.05). RESULTS: The two types of instruments had approximately the same chemical composition, phase constitution, and austenite finishing temperatures. TF instruments had significantly (P ≤ 0.001) lower Vickers microhardness values and were more flexible than RaCe instruments (P = 0.016), but had similar (TF size 25, .08 taper and RaCe size 25, .06 taper, P = 0.916) or significantly higher (TF size 25, .06 taper and RaCe size 25, .04 taper, P ≤ 0.001) torsional resistance. CONCLUSIONS: Comparison of TF and RaCe instruments of similar measured dimensions revealed that the different manufacturing methods employed for producing these instruments gave rise to different mechanical behaviours.
Asunto(s)
Aleaciones Dentales/química , Níquel/química , Preparación del Conducto Radicular/instrumentación , Titanio/química , Rastreo Diferencial de Calorimetría , Elasticidad , Diseño de Equipo , Dureza , Humanos , Ensayo de Materiales , Fenómenos Mecánicos , Fenómenos Físicos , Docilidad , Espectrometría por Rayos X , Propiedades de Superficie , Torque , Torsión Mecánica , Difracción de Rayos XRESUMEN
AIM: To assess the influence of multiple clinical uses on the torsional behaviour of ProTaper Universal rotary NiTi instruments. METHODOLOGY: Root canal treatments were performed on patients using the ProTaper Universal rotary system to prepare canals. Ten sets of instruments were used by an experienced endodontist, each set being used in five molar teeth. After clinical use, S1, S2, F1 and F2 instruments were analysed for damage by optical and scanning electron microscopy. The used sets, along with a control group of 10 sets of new instruments, were then torsion tested based on the ISO 3630-1 specification. Data obtained were subjected to a one-way analysis of variance (anova) with alpha = 0.05. RESULTS: The use of the ProTaper Universal rotary instruments by an experienced endodontist allowed for the cleaning and shaping of the root canal system of five molar teeth without fracture. The maximum torque for instruments S2, F1 and F2, and the angular deflection at fracture for instruments S2 and F1 were significantly lower following clinical use. The largest decrease in maximum torque was 18.6% (P = 0.014) for S2 instruments. The same maximum percent decrease was found for angular deflection at fracture for F1 instruments (P = 0.009). CONCLUSIONS: Torsional resistance and angular deflection of used instruments, as compared to that of new instruments, were reduced following clinical use.