We report on the heteroepitaxial growth of ferroelectric (FE)-antiferromagnetic (AFM) BiFeO3 (BFO) on ferromagnetic La0.7Sr0.3MnO3 (LSMO), integrated on Si(100) using pulsed laser deposition via the domain matching epitaxy paradigm. The BFO/LSMO films were epitaxially grown on Si(100) by introducing epitaxial layers of SrTiO3/MgO/TiN. X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, X-ray photo absorption spectroscopy, and atomic force microscopy were employed to fully characterize the samples. Furthermore, we have investigated the magnetic behavior of this five layer heterostructure, in which a d(5) system (Fe(3+)) manifested in FE-AFM BFO is epitaxially conjoined at the interface to a multivalent transition metal ion such as Mn(3+)/Mn(4+) in LSMO. The temperature- and magnetic field-dependent magnetization measurements reveal an unexpected enhancement in magnetic moment and improved magnetic hysteresis squareness originating from the BFO/LSMO interface. We observe a stronger temperature dependence of HEB when the polarity of field cooling is negative as compared to positive field cooling. We believe such an enhancement in magnetic moment and magnetic coupling is likely directly related to an electronic orbital reconstruction at the interface and complex interplay between orbital and spin degrees of freedom, similar to what has previously been reported in the literature. Future work will involve the linearly polarized X-ray absorption measurements to prove this hypothesis. This work represents a starting step toward the realization of magneto-electronic devices integrated with Si(100).
Asunto(s)
Lantano/química , Imanes/química , Óxidos/química , Estroncio/química , Titanio/química , Electrónica , Nanoestructuras/química , Difracción de Rayos XRESUMEN
We report a comprehensive study of the defects in room-temperature ferromagnetic (RTFM) Cu-doped ZnO thin films using x-ray absorption spectroscopy. The films are doped with 2 at.% Cu, and are prepared by reactive magnetron sputtering (RMS) and pulsed laser deposition (PLD), respectively. The results reveal unambiguously that atomic point defects exist in these RTFM thin films. The valence states of the Cu ions in both films are 2(+). In the film prepared by PLD, the oxygen vacancies (V(O)) form around both Zn ions and Cu ions in the hexagonal wurtzite structure. Upon annealing of the film in O(2), the V(O) population reduces and so does the RTFM. In the film prepared by RMS, the V(O)s around Cu ions are not detected, and the V(O) population around Zn ions is also smaller than in the PLD-prepared film. However, zinc vacancies (V(Zn)) are evidenced. Given the low doping level of spin-carrying Cu ions, these results provide strong support for defect-mediated ferromagnetism in Cu-doped ZnO thin films.