TiO2 anatase nanoparticle networks: synthesis, structure, and electrochemical performance.

Nanocrystalline anatase TiO(2) materials with different specific surface areas and pore size distributions are prepared via sol-gel and miniemulsion routes in the presence of surfactants. The samples are characterized by X-ray diffraction, nitrogen sorption, transmission electron microscopy, and electrochemical measurements. The materials show a pure anatase phase with average crystallite size of about 10 nm. The nitrogen sorption analysis reveals specific surface areas ranging from 25 to 150 m(2) g(-1) . It is demonstrated that the electrochemical performance of this material strongly depends on morphology. The mesoporous TiO(2) samples exhibit excellent high rate capabilities and good cycling stability.

Mesoporous CeO2 nanoparticles synthesized by an inverse miniemulsion technique and their catalytic properties in methane oxidation.

Cerium(IV) oxide nanoparticles were synthesized using an inverse miniemulsion technique with cerium nitrate hexahydrate as precursor. The resulting nanocrystallites are as small as 5 nm with a specific surface area of 158 m² g⁻¹ after calcination at 400 °C. With the addition of cetyltrimethylammonium bromide (CTAB) or (poly(ethylene oxide)-b-poly(propylene oxide)-b-poly(ethylene oxide)) triblock copolymers (PEO-PPO-PEO) as template in the miniemulsion droplets, the specific surface area can be increased up to 255 m² g⁻¹. The miniemulsions were characterized by dynamic light scattering (DLS) and the obtained oxides were examined by x-ray diffraction (XRD), nitrogen sorption (BET and BJH), and transmission electron microscopy (TEM). The catalytic activity of the resulting ceria was investigated for the temperature-programmed oxidation (TPO) of methane.

Phase stability and photocatalytic activity of Zr-doped anatase synthesized in miniemulsion.

A series of mesoporous anatase-type TiO(2) doped with zirconium (0-50 mol% Zr) was synthesized by combining the sol-gel process with the inverse miniemulsion technique. Nanoparticles between 100 and 300 nm were directly prepared from acidic precursor solutions of titanium glycolate (EGMT) and zirconium isopropoxide. The miniemulsion technique is a simple and convenient method to synthesize nanoparticles of homogeneous size because the reactions (here hydrolysis and condensation) take place in the confined space of nanodroplets (several hundreds of nanometres) and therefore in a highly controlled manner. For low doping levels (0-7.1 mol% Zr), Zr(x)Ti(1 - x)O(2) solid solutions were formed where Zr was uniformly dispersed into the anatase framework. For higher amounts of zirconium (Zr >or= 7.1 mol%), the crystallization of zirconium titanate (ZrTiO(4)) occurred at a low temperature of 650 degrees C and it was obtained as a pure material for 47.4 mol%