Nitrogen-Doped Biochar for Enhanced Peroxymonosulfate Activation to Degrade Phenol through Both Free Radical and Direct Oxidation Based on Electron Transfer Pathways.

Nowadays, super nitrogen-doped biochar (SNBC) material has become one of the most promising metal-free catalysts for activating peroxymonosulfate (PMS) to degrade organic pollutants. To understand the evolution of SNBC properties with fabrication conditions, a variety of SNBC materials were prepared and characterized by elemental analysis, N2 adsorption-desorption, scanning electron microscopy, Fourier transform infrared spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, and X-ray diffraction. We systematically investigated the activation potential of these SNBC materials for PMS to degrade phenol. SN1BC-800 with the best catalytic performance was obtained by changing the activation temperatures and the ratio of biochar to melamine. The effects of catalyst dosage, the PMS concentration, pH, and reaction temperature on phenol degradation were studied in detail. In the presence of 0.3 g/L SN1BC-800 and 1 g/L PMS, the removal rate of 20 mg/L phenol could reach 100% within 5 min. According to electron paramagnetic resonance spectra and free radical quenching experiments, a nonfree radical pathway of phenol degradation dominated by 1O2 and electron transfer was proposed. More interestingly, the excellent catalytic performance of the SN1BC-800/PMS system is universally applicable in the degradation of other typical organic pollutants. In addition, the degradation rate of phenol is still over 80% after five reuses, which shows that the SN1BC-800 catalyst has high stability and good application prospects in environmental remediation.

Efficient activation of persulfate by Nickel-supported cherry core biochar composite for removal of bisphenol A.

In this study, low-cost and easily obtained biochar was chosen to prepare nickel-modified biochar materials (Ni/BC) through a one-step activation pyrolysis method. Characterization with X-ray diffraction, X-ray photoelectron spectroscopy and high-resolution transmission electron microscopy proved the existence of Ni0 and NiO nanocrystals in Ni/BC catalyst. The optimal Ni0.5/BC exhibited excellent peroxymonosulfate (PMS) and peroxydisulfate (PDS) activation efficiency toward bisphenol A (BPA) degradation. The Ni0.5/BC (0.03 g) reacted with 1.0 g L-1 PMS or PDS could completely remove 20 mg L-1 BPA in 10 min with the first-order kinetic constants (k1) of 0.322 min-1 (PMS) and 0.336 min-1 (PDS). More importantly, the composite has better structural and functional attributes for the BPA degradation with universal applicability at wide pH and temperature range, proving as a better degradation mediator with high adaptation for numerous organic pollutants. Catalytic activity decreased slightly even after 4 cycles. Based on the quenching experiment and electron paramagnetic resonance, it was found that SO4•-, •OH and 1O2 were the dominant active species in BPA degradation process. Therefore, this work not only supplies a promising catalyst for the removal of organic contaminants, but also is beneficial for the further development of alternative catalysts for sulfate radical based advanced oxidation processes.

Preparation of N-doped porous biochar with high specific surface area and its efficient adsorption for mercury ion from aqueous solution.

Herein, a new type of super active nitrogen-doped biochar sheet (SNBC) was prepared by two-step pyrolysis and KOH chemical activation with melamine and cherry kernel powder as precursors of nitrogen and carbon source for removing Hg2+ from wastewater. The N2 adsorption/desorption and scanning electron microscope characterization revealed that the resulted SNBC under 600 °C calcination owned huge specific surface area of 2828 m2/g and plenty of well-developed micropores, and X-ray photoelectron spectroscopy and Fourier transform-infrared spectroscopy analysis testified the existence of functional groups containing N and O, which could provide adsorption sites for Hg2+. The SNBC-600 showed high adsorption capacity for Hg2+ even at low pH, and interfering cations had little effect on the adsorption. The adsorption process was rapid and dynamic data fit the pseudo-second-order dynamic model well. The maximum adsorption capacity of Hg2+ on SNBC-600 calculated by Langmuir model was 230 mg/g. After six times of reuse, the adsorption capacity still exceeded 200 mg/g, exhibiting good reusability. The designed microfiltration membrane device base on SNBC-600 could remove low concentration of Hg2+ effectively from solution. This study provided a simple and environment-friendly method for manufacturing nitrogen-doped biochar sheet, which was of great significance in the practical application of Hg2+ pollution treatment.