RESUMEN
The synthesis of crystalline polyphenylene covalent organic frameworks (COFs) was accomplished by linking fluorinated tris(4-acetylphenyl)benzene building units using aldol cyclotrimerization. The structures of the two COFs, reported here, were confirmed by powder X-ray diffraction techniques, Fourier transform infrared, and solid-state 13C CP/MAS NMR spectroscopy. The results showed that the COFs were porous and chemically stable in corrosive, harsh environments for at least 1 week. Accordingly, postsynthetically modified derivatives of these COFs using primary amines showed CO2 uptake from air and flue gas.
RESUMEN
We synthesized two isoreticular furan-based metal-organic frameworks (MOFs), MOF-LA2-1(furan) and MOF-LA2-2(furan) with rod-like secondary building units (SBUs) featuring 1D channels, as sorbents for atmospheric water harvesting (LA = long arm). These aluminum-based MOFs demonstrated a combination of high water uptake and stability, exhibiting working capacities of 0.41 and 0.48 gwater/gMOF (under isobaric conditions of 1.70 kPa), respectively. Remarkably, both MOFs showed a negligible loss in water uptake after 165 adsorption-desorption cycles. These working capacities rival that of MOF-LA2-1(pyrazole), which has a working capacity of 0.55 gwater/gMOF. The current MOFs stand out for their high water stability, as evidenced by 165 cycles of water uptake and release. MOF-LA2-2(furan) is the first aluminum MOF to employ a double 'long arm' extension strategy, which is confirmed through single-crystal X-ray diffraction (SCXRD). The MOFs were synthesized by using a straightforward synthesis route. This study offers valuable insights into the design of durable, water-stable MOFs and underscores their potential for efficient water harvesting.
RESUMEN
We have developed two series of amine-functionalized zirconium (Zr) metal-organic framework-808 (MOF-808), which were produced by postsynthetic modifications to have either amino acids coordinated to Zr ions (MOF-808-AAs) or polyamines covalently bound to the chloro-functionalized structure (MOF-808-PAs). These MOF variants were comprehensively characterized by liquid-state 1H nuclear magnetic resonance (NMR) measurements and potentiometric acid-base titration to determine the amounts of amines, energy-dispersive X-ray spectroscopy to assess the extent of covalent substitution by polyamines, powder X-ray diffraction analysis to verify the maintenance of the MOF crystallinity and structure after postsynthetic modifications, nitrogen sorption isotherm measurements to confirm retention of the porosity, and water sorption isotherm measurements to find the water uptake in the pores of each member of the series. Evaluation and testing of these compounds in direct air capture (DAC) of CO2 showed improved CO2 capture performance for the functionalized forms, especially under humid conditions: In dry conditions, the l-lysine- and tris(3-aminopropyl)amine-functionalized variants, termed as MOF-808-Lys and MOF-808-TAPA, exhibited the highest CO2 uptakes at 400 ppm, measuring 0.612 and 0.498 mmol g-1, and further capacity enhancement was achieved by introducing 50% relative humidity, resulting in remarkable uptakes of 1.205 and 0.872 mmol g-1 corresponding to 97 and 75% increase compared to the dry uptakes, respectively. The mechanism underlying the enhanced uptake efficiency was revealed by 13C solid-state NMR and temperature-programmed desorption measurements, indicating the formation of bicarbonate species, and therefore a stoichiometry of 1:1 CO2 to each amine site.
RESUMEN
The introduction of molecularly woven three-dimensional (3D) covalent organic framework (COF) crystals into polymers of varying types invokes different forms of contact between filler and polymer. Whereas the combination of woven COFs with amorphous and brittle polymethyl methacrylate results in surface interactions, the use of the liquid-crystalline polymer polyimide induces the formation of polymer-COF junctions. These junctions are generated by the threading of polymer chains through the pores of the nanocrystals, thus allowing for spatial arrangement of polymer strands. This offers a programmable pathway for unthreading polymer strands under stress and leads to the in situ formation of high-aspect-ratio nanofibrils, which dissipate energy during the fracture. Polymer-COF junctions also strengthen the filler-matrix interfaces and lower the percolation thresholds of the composites, enhancing strength, ductility, and toughness of the composites by adding small amounts (~1 weight %) of woven COF nanocrystals. The ability of the polymer strands to closely interact with the woven framework is highlighted as the main parameter to forming these junctions, thus affecting polymer chain penetration and conformation.