OBJECTIVE: The safety and feasibility of retrograde laparoscopic resection of the left side of the liver. METHODS: Ninety-three laparoscopic left hepatic lobe cases were selected between August 2010 and August 2014 from our institution. A retrospective cohort study was performed between the antegrade partial hepatectomy group (47 cases; dissection from the first porta hepatis to the second) and the retrograde partial hepatectomy group (46 cases; dissection from the second porta hepatis to the first), to compare the length of time needed for resection, the amount of bleeding, post-operative time in the hospital, and the incidence of major complications, such as bile leakage, abdominal abscess, and post-hepatectomy hemorrhage. RESULTS: All of the cases had a successful laparoscopic partial hepatectomy without the need for an intraoperative blood transfusion. Patients were able to ambulate on post-operative day 1 and tolerated a liquid diet on post-operative day 1 or 2. There were no statistical differences of post-operative hospital length of stay or incidence of major complications between the two groups. Both duration of resection and the amount of bleeding were less in the retrograde group than of those in the antegrade group, due to the lower incidence of hepatic vein injury in the retrograde group. CONCLUSION: Occlusion of both the inflow and outflow hepatic vessels combined with retrograde hepatectomy from the second porta hepatis to the first, demonstrated less hemorrhage and lower incidence of hepatic veins injury during laparoscopic partial hepatectomy.

Humidity-sensitive irreversible phase transformation of open-framework zinc phosphate and its water-assisted high proton conduction properties.

Open-framework zinc phosphate (NMe4)(ZnP2O8H3) undergoes irreversible phase transformation. Structural transformation with α (NMe4·Zn[HPO4][H2PO4] the low-temperature phase) and ß (NMe4·ZnH3[PO4]2 the high-temperature phase) (Tc = 149 °C) and conduction properties were investigated by single-crystal X-ray diffraction, differential scanning calorimetry, and alternating current (ac) impedance. The open-framework material was sensitive to humidity and ß proton conductivity was higher than 10-2 S cm-1 at room temperature and 98% relative humidity (RH). Given that the high proton conductivity of the open-framework material can compete with that of many advanced proton conductors based on metal-organic frameworks (MOFs), it has broad application prospects in various electrochemical devices.