RESUMEN
OBJECTIVE: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites. MATERIALS AND METHODS: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis. RESULTS: The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups. CONCLUSION: The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material. CLINICAL RELEVANCE: The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.
Asunto(s)
Recubrimiento Dental Adhesivo , Metacrilatos , Recubrimiento Dental Adhesivo/métodos , Propiedades de Superficie , Ensayo de Materiales , Resinas Compuestas/química , Circonio/química , Cerámica/química , Resistencia al Corte , Itrio/química , Cementos de Resina/química , Análisis del Estrés DentalRESUMEN
This study aimed to compare the effect of sodium hypochlorite (NaOCl) and calcium hypochlorite [Ca(OCl)2 ] on the bond strength to pulp chamber dentin when followed or not by the use of sodium thiosulfate (Na2 S2 O3 ). The pulp chamber of fifty human molars were divided into five groups (n = 10) according to the immersion protocol: 2.5% NaOCl; 2.5% NaOCl + 5% Na2 S2 O3 ; 2.5% Ca(OCl)2 ; 2.5% Ca(OCl)2 + 5% Na2 S2 O3 ; and 0.9% sodium chloride (NaCl; control). Subsequently, the samples were restored with resin composite. Three sticks each were obtained and subjected to microtensile testing. SEM/EDS analyses of the pulp chamber roof (n = 8) were carried out for mineral quantification. Elemental analysis data were investigated via one-way ANOVA and Tukey's post hoc, and bond strength data by post hoc pairwise comparisons using the Kruskal-Wallis test. Use of 2.5% NaOCl was associated with the lowest value of bond strength, while 2.5% Ca(OCl)2 had similar bond strength to that of the 0.9% NaCl control. Using 5% Na2 S2 O3 was able to increase the bond strength after 2.5% NaOCl, but not after 2.5% Ca(OCl)2 . The group treated only with 2.5% Ca(OCl)2 had a higher Ca/P ratio on the dentin surface. Dentin treated with Ca(OCl)2 was not affected by Na2 S2 O3 and showed bond strength similar to the 0.9% NaCl.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Humanos , Recubrimientos Dentinarios/química , Cavidad Pulpar , Solución Salina/farmacología , Dentina , Ensayo de Materiales , Irrigantes del Conducto Radicular/farmacología , Irrigantes del Conducto Radicular/químicaRESUMEN
STATEMENT OF PROBLEM: Zirconia has been reported to be suitable for multiunit monolithic restorations. However, as the connector region is the weakest part of the system, studies are needed to determine the optimal connector geometry. PURPOSE: The purpose of this in vitro study was to evaluate the load-bearing capacity under fatigue of implant-supported fixed partial prostheses made of monolithic zirconia with different connector cross-sectional geometries. MATERIAL AND METHODS: Three-unit monolithic fixed partial prostheses (from mandibular second premolar to the second molar) were fabricated in zirconia (Zenostar T) by computer-aided design and computer-aided manufacture (CAD-CAM). Different connector cross-sectional geometries, with an area of 9 mm2, were tested (n=10): round, square with rounded angles, or trapezoid with rounded angles. The prostheses were screwed over 2 implants and inserted into acrylic resin bases. The specimens were submitted to a mechanical fatigue test until failure, with load applied to the pontic using the stepwise stress methodology (initial load of 100 N for 5000 cycles, followed by an increase to 200 N for 20 000 cycles, with a subsequent increase of 50 N each step). For data analysis, fatigue failure load (FFL) and cycles for fatigue failure (CFF) were recorded. Failed structures were analyzed by fractography. The Kaplan-Meier test followed by a log-rank Mantel-Cox post hoc test was used to analyze FFL and CFF (α=.05). Weibull analysis was also performed. RESULTS: The round (1065 N) and trapezoid (1010 N) groups presented higher FFL values than the square one (870 N) (P≤.05). For CFF, the round connector (358 777) was better than the square (280 310) (P=.006), and the trapezoid (337 773) was statistically similar to both (P>.05). No difference among groups was observed in Weibull modulus either for CFF or FFL data. All failures were catastrophic, originating at the base of the connector and propagating toward the occlusal surface of the pontic (region under loading). CONCLUSIONS: The connector cross-sectional geometry significantly influenced the mechanical fatigue performance of implant-supported fixed partial prostheses made of monolithic zirconia.
Asunto(s)
Cerámica , Implantes Dentales , Cerámica/química , Análisis del Estrés Dental , Ensayo de Materiales , Propiedades de Superficie , Circonio/química , Diseño Asistido por Computadora , Soporte de Peso , Fracaso de la Restauración Dental , Porcelana Dental/químicaRESUMEN
PURPOSE: To examine the influence of phosphoric acid containing chlorhexidine on the dentin bond stability of a universal and a 2-step etch-and-rinse adhesive. MATERIALS AND METHODS: Eighty sound bovine incisors were randomly assigned to 8 groups (n = 10) according to: phosphoric acid (37% phosphoric acid [CTR] or 37% phosphoric acid with 2% chlorhexidine [CHX]); adhesive (Scotchbond Universal Adhesive [SBU]or Adper Single Bond 2 [SB2]); and water storage time (24 h and 6 months). Both acids and adhesives were applied to flat dentin surfaces (following manufacturer's instructions) upon which composite cylinders were built up (0.72 mm2). After storage in distilled water at 37°C for 24 h or 6 months, the composite cylinders were submitted to microshear bond strength (µSBS) testing. Bond strength data (MPa) were analyzed using three-way ANOVA and post-hoc Tukey's test (α = 5%). RESULTS: The interaction among factors was significant (p = 0.012). Both adhesives showed similar 24-h bond strengths regardless of the phosphoric acid. After 6 months, similar values were found for both materials when control phosphoric acid was used, but CHX phosphoric acid produced statistically significantly lower bond strengths for SBU. SB2 bond strength was not affected by acid type. CONCLUSION: Phosphoric acid containing chlorhexidine induced premature bond strength degradation of Scotchbond Universal Adhesive.
Asunto(s)
Clorhexidina , Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Ácidos Fosfóricos , Grabado Ácido Dental , Animales , Bovinos , Dentina , Ensayo de Materiales , Distribución Aleatoria , Resistencia a la TracciónRESUMEN
Trichomoniasis is a common sexually transmitted infection that poses significant complications for women. Challenges in treatment include adverse effects and resistance to standard antimicrobial agents. Given this context, a sesame seed oil nanoemulsion (SONE) was developed and showed anti-Trichomonas vaginalis activity. To facilitate the local application of SONE, a polysaccharide film was developed using xanthan gum (XG) and κ-carrageenan gum (CG). A blend of XG and CG (at 2 %, ratio 1:3) plasticized with glycerol produced a more promising film (XCF) than using the gums individually. The film containing SONE (SONE-XCF) was successfully obtained by replacing the aqueous solvent with SONE via solvent evaporation technique. The hydrophilic SONE-XCF exhibited homogeneity and suitable mechanical properties for vaginal application. Furthermore, SONE-XCF demonstrated mucoadhesive properties and high absorption capacity for excessive vaginal fluids produced in vaginitis. It also had a disintegration time of over 8 h, indicating long retention at the intended site of action. Hemolysis and chorioallantoic membrane tests confirmed the safety of the film. Therefore, SONE-XCF is a biocompatible film with a natural composition and inherent activity against T. vaginalis, possessing exceptional characteristics that make it appropriate for vaginal application, offering an interesting alternative for trichomoniasis treatment.
Asunto(s)
Nanocompuestos , Sesamum , Tricomoniasis , Femenino , Humanos , Carragenina , Prednisona , Polisacáridos Bacterianos , Solventes , Preparaciones Farmacéuticas , Aceites de Plantas/farmacologíaRESUMEN
The present study aimed to evaluate the impact of the existence of an abutment screw-access hole and the filling effects on the fatigue mechanical behavior of a luted lithium-disilicate glass-ceramic. Seventy-two discs (Ø = 10 mm, 1.0 mm in thickness) of lithium disilicate (IPS e.max CAD, Ivoclar AG) were obtained from prefabricated blocks. Thirty-six abutment specimens of an opaque zirconia (Yz - IPS e.max ZirCAD, Ivoclar AG) and titanium (Ti - Luminesse Ti-Cam discs, Talladium Inc.) were confectioned, and allocated according to 6 groups: Yz and Ti rigid (without screw access hole); Yz unfilled, Yz filled, Ti unfilled and Ti filled (with the screw access (Ø = 2.5 mm) in the center). For the unfilled groups, only a polytetrafluoroethylene tape was used. Resin composite (Tetric N-Ceram, Ivoclar AG) was applied to the screw access hole for the filled groups (Yz and Ti). A cyclic fatigue test was carried out (load of 200 N, 10,000 cycles each; 20 Hz of frequency, step size of 100 N until failure detection (radial/cone crack). The fatigue failure load (FFL) and number of cycles until failure (CFF) were recorded for statistical purposes. The stress distribution (MPa) was evaluated by finite element analysis. A statistically positive effect of the abutment material and the presence of the screw access hole was observed (p ≤ 0.05). The rigid groups (without screw access holes) depicted almost 100% of survival after the fatigue tests. Among the other groups, the Yz-filled group showed the best performance (p ≤ 0.05), followed by the Yz unfilled group. The Ti groups depicted lower values of FFL and CFF, with the Ti unfilled group showing the most unfavorable fatigue behavior (p ≤ 0.05). The lowest tensile stress concentration in the restorative material was observed with the use of rigid abutments, the filled groups depicted intermediate values, while unfilled groups showed the highest stress concentration (Yz rigid = 306.3 MPa; Ti rigid = 310.4 MPa < Yz filled = 490.7 MPa; Ti filled = 498.9 MPa < Yz unfilled = 707.6 MPa; Ti unfilled = 719.7 MPa). Therefore, the presence of a screw-access hole decreases the mechanical performance of a lithium disilicate ceramic regardless of the abutment material. In the presence of a screw-access hole, zirconia abutments depicted a higher fatigue failure load when compared with titanium. The filling of the abutment screw-access hole with resin composite increased the mechanical performance of the simulated restoration.
Asunto(s)
Cerámica , Litio , Titanio , Propiedades de Superficie , Ensayo de Materiales , Análisis del Estrés Dental , Porcelana Dental , Circonio , Tornillos Óseos , Diseño Asistido por Computadora , Fracaso de la Restauración DentalRESUMEN
Despite the advancements in indirect monolithic restorations, technical complications may occur during function. To overcome this issues, intraoral repair using resin composite is a practical and low-cost procedure, being able to increase the restoration's longevity. This review aimed to evaluate the need for repair and suggest a standardized repair protocol to the main indirect restorative materials. For this, studies were surveyed from PubMed with no language or date restriction, to investigate the scientific evidence of indirect monolithic restoration repair with direct resin composite. A classification to guide clinical decisions was made based on the FDI World Dental Federation criteria about defective indirect restorations considering esthetic and functional standards, along with the patient's view, to decide when polishing, repairing or replacing a defective restoration. Based on 38 surveyed studies, different resin composite intraoral repair protocols, that included mechanical and chemical aspects, were defined depending on the substrate considering resin-based, glass-ceramic or zirconia restorations. The presented criteria and protocols were developed to guide the clinician's decision-making process regarding defective indirect monolithic restorations, prolonging longevity and increasing clinical success.
Asunto(s)
Resinas Compuestas , Diseño Asistido por Computadora , Humanos , Resinas Compuestas/uso terapéutico , Resinas de Plantas , Encuestas y CuestionariosRESUMEN
The aim of this in vitro study was to evaluate the effect of the combinations of two different intraoral scanners (IOS), two milling machines, and two restorative materials on the marginal/internal fit and fatigue behavior of endocrowns produced by CAD-CAM. Eight groups (n= 10) were considered through the combination of TRIOS 3 (TR) or Primescan (PS) IOS; 4-axes (CR; CEREC MC XL) or 5-axes (PM; PrograMill PM7) milling machines; and lithium disilicate (LD; IPS e.max CAD) or resin composite (RC; Tetric CAD) restorative materials. Specific surface treatments were applied to each material, and the bonding to its corresponding Endocrown-shaped fiberglass-reinforced epoxy resin preparations was performed (Variolink Esthetic DC). Computed microtomography (µCT) was performed to assess the marginal/internal fit, as well as a mechanical fatigue test (20 Hz, initial load = 100 N/5000 cycles; step-size = 50 N/10,000 cycles until a threshold of 1500 N, then, the step-size was increased if needed to 100 N/10,000 cycles until failure or a threshold of 2800 N) to evaluate the restorations long-term behavior. Complementary analysis of the fracture features and surface topography in scanning electron microscopy was performed. Three-way ANOVA and Kaplan-Meier test (α = 0.05) were performed for marginal/internal fit, and fatigue behavior data, respectively. PS scanner, CR milling machine, and RC endocrowns resulted in a better marginal fit compared to their counterparts. Still, the PM machine resulted in a better pulpal space fit compared to the CR milling machine. Regardless of the scanner and milling machine, RC endocrowns exhibited superior fatigue behavior than LD ones. LD endocrowns presented margin chipping regardless of the milling machine used. Despite minor differences in terms of fit, the 'IOS' and 'milling machine' factors did not impair the fatigue behavior of endocrowns. Resin-composite restorations resulted in a higher survival rate compared to glass-ceramic ones, independently of the digital devices used in the workflow.
Asunto(s)
Resinas Compuestas , Diseño Asistido por Computadora , Porcelana Dental , Ensayo de Materiales , Resinas Compuestas/química , Porcelana Dental/química , Fenómenos Mecánicos , Propiedades de Superficie , Pruebas Mecánicas , Estrés MecánicoRESUMEN
Objective: To evaluate the effect of different surface treatments on the morphology, shear bond, and flexural fatigue strength of a repaired translucent zirconia. Methods: Monolithic disc-shaped specimens of translucent zirconia were prepared and ground to simulate repair areas. Four groups underwent different treatments: Air-MDP (air-abrasion with alumina particles and 10-MDP primer), Si-Sil (silica-coated alumina particles with MDP-containing silane), Si-MDP (silica coating with 10-MDP primer), and Uni adhe (universal adhesive). After roughness measurements and treatments, repairs were done using resin composite. Shear bond and flexural (n = 15) fatigue tests were performed. Surface topography, interfacial analysis, fractographic, and finite element analysis were conducted. Results: The zirconia roughness was similar between the groups, however, the surface topography was modified according to the surface treatments. Si-Sil generated higher and more stable bond strength values (20.69 MPa) between translucent zirconia and resin composite when compared to Uni adhe (15.75 MPa) considering the fatigue bond strength scenario, while it was similar to Si-MDP (17.70 MPa) and Air-MDP (18.97 MPa). Regarding the mechanical behavior, Si-Sil (680.83 MPa) also showed higher and significantly different fatigue strength when compared to Uni adhe (584.55 MPa), while both were similar to Si-MDP (634.22 MPa) and Air-MDP (641.86 MPa). Conclusion: The association of mechanical and chemical approaches is essential for long-term bond strength and optimized mechanical behavior, being air-abrasion protocols and the use of silane and/or MDP-based primers suitable for zirconia repair protocols. It was found that relying solely on a universal adhesive was not as effective as other options available. Clinical significance: The surface treatment of repair protocols affects translucent zirconia's morphology. To enhance fatigue behavior in repaired monolithic zirconia, air abrasion is crucial. Exclusive use of a universal adhesive is less effective than other choices. A primer containing silane/MDP holds the potential for stable bond strength and optimized mechanical performance.
RESUMEN
Ketoprofen (KET), commonly used for inflammation in clinical settings, leads to systemic adverse effects with prolonged use, mitigated by topical administration. Nanotechnology-based cutaneous forms, like films, may enhance KET efficacy. Therefore, this study aimed to prepare and characterize films containing KET nanoemulsions (F-NK) regarding mechanical properties, chemical composition and interactions, occlusive potential, bioadhesion, drug permeation in human skin, and safety. The films were prepared using a κ-carrageenan and xanthan gum blend (2 % w/w, ratio 3: 1) plasticized with glycerol through the solvent casting method. Non-nanoemulsioned KET films (F-K) were prepared for comparative purposes. F-NK was flexible and hydrophilic, exhibited higher drug content and better uniformity (94.40 ± 3.61 %), maintained the NK droplet size (157 ± 12 nm), and was thinner and lighter than the F-K. This film also showed increased tensile strength and Young's modulus values, enhanced bioadhesion and occlusive potential, and resulted in more of the drug in the human skin layers. Data also suggested that nano-based formulations are homogeneous and more stable than F-KET. Hemolysis and chorioallantoic membrane tests suggested the formulations' safety. Thus, the nano-based film is suitable for cutaneous KET delivery, which may improve the drug's efficacy in managing inflammatory conditions.
Asunto(s)
Cetoprofeno , Nanocompuestos , Polisacáridos Bacterianos , Humanos , Cetoprofeno/farmacología , Cetoprofeno/química , Carragenina/química , Piel , Nanocompuestos/químicaRESUMEN
OBJECTIVE: To evaluate the fatigue behavior of lithium disilicate crowns with a simplified anatomy against progressive cement/ceramic debonding scenarios. MATERIALS AND METHODS: Lithium disilicate crowns were fabricated via CAD/CAM and luted onto a dentin analogue material using resin cement following the manufacturer's instructions. Then, the different crown regions were isolated with paraffin oil for the absence of chemical adhesion according to four experimental groups (n = 15): Shoulder; Shoulder + Axial; Fully isolated; and Control (no insulation/fully bonded). Load to failure tests (n = 3) were run to determine cyclic fatigue parameters, and the specimens were subsequently submitted to a cyclic fatigue test (n = 12) (initial load 200 N for 5000 cycles, step 100 N, 15,000 cycles/step, frequency 20 Hz) until cracks were observed, and later fracture. The data were analyzed by Kaplan-Meier + Mantel-Cox post-hoc tests for both outcomes (cracks and fracture). Fractographic, cross-sectional surface, and finite element (FEA) analyzes were performed. RESULTS: When it comes to crack occurrence when the chemical adhesion to the occlusal surface is compromised, there is worsening (p < 0.05) in fatigue behavior compared to groups where the occlusal portion of the crown is still bonded. Considering fracture occurrence, there was no difference (p > 0.05) among the tested groups. All cracks occurred in the occlusal portion, first as a radial crack at the ceramic intaglio surface, and posteriorly unleashing a Hertzian cone crack at the top surface, resulting in fractures on the frontal walls. The interface analysis showed no interference of the insulating agent. FEA showed that as the isolated areas increased, there was also an increase in both tensile and shear stresses concentration in the crown and in the cement layer. CONCLUSION: The chemical adhesion between cement and ceramic is essential for better fatigue behavior of lithium disilicate crowns with a simplified anatomy, especially in the occlusal portion, but the restoration performance is impaired when such adhesion is compromised. There is an increase in crown and cement stress concentration with the progressive loss of chemical bonding of the crown's walls.
Asunto(s)
Porcelana Dental , Cementos de Resina , Estudios Transversales , Cerámica , Soporte de Peso , Ensayo de Materiales , Análisis del Estrés Dental , Diseño Asistido por Computadora , Fracaso de la Restauración Dental , Propiedades de SuperficieRESUMEN
OBJECTIVE: To characterize the effect of the occlusal contact region on the mechanical fatigue performance and on the fracture region of monolithic lithium disilicate ceramic crowns. MATERIALS AND METHODS: Monolithic lithium disilicate ceramic crowns were machined in a CAD/CAM system and adhesively luted onto glass-fiber reinforced epoxy resin preparations with resin cement. The crowns were divided into three groups (n = 16) according to load application region (cusp tip: restricted to cusp tips; cusp plane: restricted to cuspal inclined plane; or mixed: associating tip cusp and cuspal inclined plane). The specimens were submitted to a cyclic fatigue test (initial load: 200 N; step-size: 100 N; cycles/step: 20,000; loading frequency: 20 Hz; load applicator: 6 mm or 40 mm diameter stainless steel) until observing cracks (1st outcome) and fracture (2nd outcome). The data were analyzed by the Kaplan-Meier + Mantel-Cox post-hoc tests for both outcomes (cracks and fracture). Finite element analysis (FEA), occlusal contact region, contact radii measurements, and fractographic analyzes were performed. RESULTS: The mixed group presented worse fatigue mechanical behavior (550 N / 85.000 cycles) compared to the cuspal inclined plane group (656 N / 111,250 cycles) (p < 0.05) for the first crack outcome, while the cusp tip group was similar to both groups (588 N / 97,500 cycles) (p > 0.05). The mixed group had the worst fatigue behavior (1413 N / 253,029 cycles) in relation to the other groups (Cusp tip: 1644 N / 293,312 cycles; Cuspal inclined plane: 1631 N / 295,174 cycles) considering the crown fracture outcome (p < 0.05). FEA showed higher tensile stress concentration areas just below the load application region. In addition, loading on the cuspal inclined plane induced a higher tensile stress concentration in the groove region. The most prevalent type of crown fracture was the wall fracture. Groove fracture was observed in 50% of the loading specimens exclusively on the cuspal inclined plane. CONCLUSION: Load application on distinct occlusal contact regions affects the stress distribution pattern and consequently the mechanical fatigue performance and fracture region of the monolithic lithium disilicate ceramic crowns. A combination of loading at distinct regions is recommended to promote better evaluation of the fatigue behavior of a restored set.
Asunto(s)
Fracturas Óseas , Fracturas de los Dientes , Humanos , Cerámica , Ensayo de Materiales , Porcelana Dental , Coronas , Diseño Asistido por Computadora , Análisis del Estrés Dental , Fracaso de la Restauración Dental , Propiedades de SuperficieRESUMEN
The present systematic review and meta-analysis aimed to assess the characteristics and consequences of post-processing methods after grinding procedures in YSZ ceramics on its surface roughness and flexural strength. The protocol of this review was made prospectively and is available online in the PROSPERO database (link). Literature searches on PubMed/MEDLINE, EMBASE, Lilacs, Web of Science and Scopus were conducted on December 2022 to select in vitro studies written in English, without publishing-date restrictions, that considered surface characteristics and mechanical properties of YSZ ceramics submitted to grinding and subsequent post-processing surface treatments as an attempt to revert the effect induced by grinding. Two authors independently selected the studies, extracted the data and assessed the risk of bias. Mean differences (Rev-Man 5.1, random effects model, α= 0.05) were obtained by comparing flexural strength and surface roughness values of ground surfaces with at least one post-processing surface treatment (global analysis). Subgroup analyses were performed considering the most prevalent categories of post-processing methods. A total of 33 (out of 4032) studies were eligible and included in the analysis. In the global analysis, ground surfaces showed higher flexural strength than when post-processing methodologies were employed (p< 0.0001). The subgroup analysis showed that only polishing was able to enhance the flexural strength after grinding (p= 0.001); however, when other protocols were used, the ground surface was always superior in terms of flexural strength (p< 0.0001). Post-processing techniques in both the global and sub-group analyses were able to reduce the surface roughness after grinding in YSZ ceramics (p< 0.00001). High heterogeneity was found in all the meta-analyses. Concerning the risk of bias analysis, the included studies had mixed scores for the considered factors. In conclusion, in terms of improving flexural strength and restoring surface roughness after grinding, polishing protocols can be considered the best indication as post-processing treatment after YSZ ceramics adjustments/grinding.
Asunto(s)
Itrio , Circonio , Humanos , Ensayo de Materiales , Propiedades de Superficie , Circonio/análisis , Itrio/análisis , Cerámica , Pulido Dental , Porcelana DentalRESUMEN
When partial and/or non-retentive preparation, such as those for occlusal veneers, is indicated, a proper and stable adhesion is essential. Therefore, the aim of this in vitro study was to evaluate the effect of loss of adhesion in different regions of the bonding interface on the fatigue behavior of simplified lithium disilicate restorations. For this, lithium disilicate (IPS e.max CAD) discs (1 mm thick and Ø = 10 mm) were fabricated, polished with #400-, #600-, #1200-grit silicon carbide (SiC) papers, and crystallized. As substrate, fiber-reinforced resin epoxy discs (2.5 mm thick and Ø = 10 mm) were fabricated and polished with #600-grit SiC paper. The ceramic bonding surface was treated with 5% hydrofluoric acid and a silane-containing primer (Monobond N), while the substrate was etched with 10% hydrofluoric acid followed by the application of the bonding system primers (Primer A + B). A lacquer (nail polish) was used to simulate the loss of adhesion in specific areas according to the study design to compose the testing groups: bonded (control; did not received nail polish application); - non-bonded (loss of adhesion in the whole specimen area); - margin (loss of adhesion in the ceramic margin); - center (loss of adhesion in the ceramic central area). The adhesive area of partially bonded groups was 50% of the adhesive surface. Then, the discs (n = 12) were bonded to the respective substrate using a resin cement (Multilink N), light-cured, water-stored for 90 days, and subjected to thermocycling (25,000 cycles, 5° to 55 °C) before testing. A cyclic fatigue test was run (20 Hz, initial load of 200 N for 5000 cycles, 50 N step size for 10,000 cycles each until specimen failure), and the fatigue failure load and number of cycles for failure were recorded. As complementary analysis, finite element analysis (FEA) and scanning electron microscopy analysis were performed. Kaplan-Meier log-rank (Mantel-Cox) was conducted for survival analysis. The results showed that as the loss of adhesion reaches the central area, the worse is the fatigue behavior and the higher is the stress peak concentration in the ceramic bonding surface. The bonded specimens presented better fatigue behavior and stress distribution compared to the others. In conclusion in a non-retentive preparation situation, proper adhesion is a must for the restoration fatigue behavior even after aging; while the loss of adhesion reaches central areas the mechanical functioning is compromised.
Asunto(s)
Cerámica , Cementos de Resina , Cerámica/química , Cementos de Resina/química , Ácido Fluorhídrico/química , Propiedades de Superficie , Ensayo de Materiales , Análisis del Estrés Dental , Porcelana DentalRESUMEN
This study aimed to evaluate the influence of ceramic surface treatments, resin cement viscosities, and storage regimens on the fatigue performance of bonded glass-ceramics (lithium disilicate, LD; feldspathic, FEL). Ceramic discs (Ø = 10 mm; thickness = 1.5 mm) were allocated into eight groups per ceramic (n = 15), considering three factors: "ceramic surface treatment" in two levels - 5% hydrofluoric acid etching and silane-based coupling agent application (HF), or self-etching ceramic primer (E&P); "resin cement viscosity" in two levels - in high or low viscosity; and "storage regimen" in two levels - baseline, 24 h to 5 days; or aging, 180 days + 25,000 thermal cycles. Adhesive luting was performed onto glass fiber-reinforced epoxy resin discs (Ø = 10 mm; thickness = 2 mm) and the bonded assemblies were subjected to cyclic fatigue tests: initial load = 200 N; step-size = 25 N (FEL) and 50 N (LD); 10,000 cycles/step; 20 Hz. Scanning electron microscopy (SEM) inspections were performed. Regarding the LD ceramic, the fatigue behavior was reduced after aging for HF_HIGH and E&P_LOW conditions, while stable performance was observed for HF_LOW and E&P_HIGH. Regarding the FEL results, aging negatively affected HF_HIGH, E&P_HIGH, and E&P_LOW, being that only the HF_LOW condition presented a stable behavior. The failure initiated from defects on the etched surface of the ceramics, where the cross-sectional analysis commonly revealed unfilled areas. Long-term aging might induce a decrease in mechanical behavior. The 'ceramic microstructure/surface conditioning/resin cement viscosity relationships' modulate the fatigue performance of lithium disilicate and feldspathic glass-ceramics.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Propiedades de Superficie , Viscosidad , Estudios Transversales , Ensayo de Materiales , Grabado Ácido Dental/métodos , Ácido Fluorhídrico , Cerámica , Porcelana Dental , Análisis del Estrés DentalRESUMEN
This study aimed to incorporate nanocapsules containing 3,3'-diindolylmethane (DIM) with antitumor activity into a bilayer film of karaya and gellan gums for use in topical melanoma therapy. Nanocarriers and films were prepared by interfacial deposition of the preformed polymer and solvent casting methods, respectively. Incorporating DIM into nanocapsules increased its antitumor potential against human melanoma cells (A-375) (IC50 > 24.00 µg/mL free DIM × 2.89 µg/mL nanocapsules). The films were transparent, hydrophilic (θ < 90°), had homogeneous thickness and weight, and had a DIM content of 106 µg/cm2. Radical ABTS+ scavenger assay showed that the DIM films presented promising antioxidant action. Remarkably, the films showed selective bioadhesive potential on the karaya gum side. Considering the mechanical analyses, the nanotechnology-based films presented appropriate behavior for cutaneous application and controlled DIM release profile, which could increase the residence time on the application site. Furthermore, the nanofilms were found to increase the permeation of DIM into the epidermis, where melanoma develops. Lastly, the films were non-hemolytic (hemolysis test) and non-irritant (HET-CAM assay). In summary, the combination of karaya and gellan gum in bilayer films that contain nanoencapsulated DIM has demonstrated potential in the topical treatment of melanoma and could serve as a viable option for administering DIM for cutaneous melanoma therapy.
RESUMEN
This study evaluated the mechanical behavior and risk of failure of three CAD-CAM crowns repaired with different resin composites through a three-dimensional (3D) finite element analysis. Three-dimensional models of different cusp-repaired (conventional nanohybrid, bulk-fill, and flowable resin composites) crowns made of zirconia, lithium disilicate, and CAD-CAM resin composite were designed, fixed at the cervical level, and loaded in 100 N at the working cusps, including the repaired one. The models were analyzed to determine the Maximum Principal and Maximum Shear stresses (MPa). Complementary, an in vitro shear bond strength test (n = 10) was performed to calculate the risk of failure for each experimental group. The stress distribution among the models was similar when considering the same restorative material. The crown material affected the stress concentration, which was higher for the ceramic models (±9 MPa for shear stress; ±3 MPa for tensile stress) than for the CAD-CAM composite (±7 MPa for shear stress; ±2 MPa for tensile stress). The shear bond strength was higher for the repaired CAD-CAM resin composite (±17 MPa) when compared to the ceramics (below 12 MPa for all groups), while the repair materials showed similar behavior for each substrate. The stress distribution is more homogenous for repaired resin composite crowns, and a flowable direct resin composite seems suitable to repair ceramic crowns with less risk of failure.
RESUMEN
OBJECTIVE: To explore and characterize the effect of the discrepancy between crestal bone height (CB) and pulp chamber floor (PCF) in the fatigue performance of endodontically-treated teeth rehabilitated with an endocrown restoration. MATERIALS AND METHODS: A total of 75 human molars free of defects, caries history or cracks were selected, then endodontically treated and randomly allocated into 5 groups (N = 15) according to the difference between PCF and CB, as follows: PCF 2 mm above, PCF 1 mm above, PCF leveled, PCF 1 mm below and PCF 2 mm below. Endocrown restorations were made with composite resin (Tetric N-Ceram, shade B3, Ivoclar) in 1.5 mm thickness and luted with a resin cement (Multilink N, Ivoclar) onto the dental elements. Monotonic testing was performed to define the fatigue parameters, and a cyclic fatigue test was used until failure of the assembly. The collected data were submitted to statistical survival analysis (Kaplan-Meier followed by Mantel-Cox and Weibull), fractographic analysis and finite element analysis (FEA) were performed as complementary analyzes. RESULTS: The PCF 2 mm below and PCF 1 mm below groups presented the best results regarding fatigue failure load (FFL) and number of cycles for failure (CFF) (p < 0.05), but presented no difference between each other (p > 0.05). The PCF leveled and PCF 1 mm above groups presented no statistical difference between them (p > 0.05), but performed better than the PCF 2 mm above group (p < 0.05). The rate of favorable failures of PCF 2 mm above, PCF 1 mm above, PCF leveled, PCF 1 mm below and PCF 2 mm below groups were 91.7%, 100%, 75%, 66.7% and 41.7%, respectively. FEA showed different stress magnitudes according to the pulp-chamber design. CONCLUSION: The insertion level of the dental element to be rehabilitated with an endocrown interferes in the mechanical fatigue performance of the set. The discrepancy between the CB height and the PCF has a direct effect, where the higher the PCF in relation to the CB, the greater the risk of mechanical failure of the restored dental element.
Asunto(s)
Cavidad Pulpar , Diente no Vital , Humanos , Cerámica , Resinas Compuestas , Diseño Asistido por Computadora , Coronas , Porcelana Dental , Fracaso de la Restauración Dental , Análisis del Estrés Dental , Ensayo de Materiales , Propiedades de Superficie , Diente MolarRESUMEN
OBJECTIVE: To evaluate whether an adhesive application after surface treatment on a lithium disilicate ceramic (LD) has an influence on its load-bearing capacity under fatigue. METHODS: LD discs (Ø= 10 mm; thickness= 1 mm) were allocated into 8 groups (n= 15), considering 3 factors: "ceramic surface treatment" - HF: hydrofluoric acid + universal primer application; or MEP: single-component ceramic primer; "adhesive application" - with or without; and "aging protocol" - baseline: 24 h to 7 days; or aging: 180 days of storage + 25,000 thermal cycles. The LD discs were adhesively bonded to glass fiber-reinforced epoxy resin discs (Ø= 10 mm; thickness= 2 mm) and stored according to the condition and each group. Cyclic fatigue testing (initial load= 100 N; step size= 100 N until600 N and after step size= 25 N to failure; 10,000 cycles/step; 20 Hz frequency) was performed. Fractographic and adhesive interface analyzes were also performed. The collected data were then analyzed by Kaplan Meier and Mantel-Cox tests and One-way ANOVA. RESULTS: The adhesive application in the baseline condition had no influence on the load-bearing capacity under fatigue when the HF surface treatment was performed, however, adhesive application for the MEP treatment led to worse results than without it. The adhesive application in the aged condition showed worse fatigue outcomes for both treatments. All specimens presented radial cracks. MEP treatment followed by adhesive application presented the thickest luting layer. CONCLUSION: The adhesive application after surface treatments of a lithium disilicate glass-ceramic is detrimental to its load-bearing capacity under fatigue when adhesively luted onto a supporting substrate.
Asunto(s)
Recubrimiento Dental Adhesivo , Ácido Fluorhídrico , Adhesivos , Cerámica , Porcelana Dental , Análisis del Estrés Dental , Resinas Epoxi , Ensayo de Materiales , Cementos de Resina , Propiedades de Superficie , Soporte de PesoRESUMEN
The present study aimed to determine the influence of adhesive luting on the fatigue mechanical properties of simplified lithium disilicate crowns luted to dentin analogues preparations, and to compare two different approaches of simulation of a non-adhesive luting procedure. To this end, 30 prosthetic preparations of glass fiber-filled epoxy resin used as dentin analogues were milled and lithium disilicate crowns were pressed (1.5 mm thickness), which were allocated into three different groups: resin cement (RC), resin cement isolated by paraffin oil (RCI) and zinc phosphate cement (ZP). For luting procedures, the ceramic crowns of the RC and RCI groups had their internal surface treated with 5% hydrofluoric acid and universal primer. Afterwards, a thin layer of paraffin oil was applied onto the ceramic crown intaglio surface in the RCI group. The dentin analogues were treated with 10% hydrofluoric acid, followed by primer application and luting as recommended by the manufacturer. No previous surface treatments were performed for the ZP group, and the cement was applied as recommended. The fatigue test was run under cyclic fatigue (load 400-2000 N, step-size 100 N, 15,000 cycles/step, frequency 20 Hz) until failure detection (radial crack) by transillumination. The fatigue failure load (FFL), number of cycles until failure (CFF), and survival rate in each testing step were recorded. The RC group presented a higher FFL, CFF and survival rate compared to the other groups (p < 0.001), which were statistically equal to each other (p > 0.05). Weibull analysis detected no difference between groups for the Weibull module. Therefore, loss of adhesion between the evaluated substrates induces a significant reduction in load-bearing capacity under fatigue of the lithium disilicate crowns, strengthening the strong-importance of long-lasting adhesion for crown's survival. In addition, different methods for the simulation of non-adhesive conditions induce the same performance in the explored outcomes, confirming that both are valid approaches for laboratory studies.