Elaboration of Nanomagnet Arrays: Organization and Magnetic Properties of Mass-Selected FePt Nanoparticles Deposited on Epitaxially Grown Graphene on Ir(111).

The moiré pattern created by the epitaxy of a graphene sheet on an iridium substrate can be used as a template for the growth of 2D atomic or cluster arrays. We observed for the first time a coherent organization of hard magnetic preformed FePt nanoparticles on the 2D lattice of graphene on Ir(111). Nanoparticles of 2 nm diameter have been mass selected in a gas phase and deposited with low energy on the hexagonal moiré pattern. Their morphology and organization have been investigated using grazing incidence small angle x-ray scattering, while their magnetic properties have been studied by x-ray magnetic circular dichroism, both pointing to a FePt cluster-graphene surface specific interaction. The spatial coherence of the nanoparticles is preserved upon annealing up to 700 °C where the hard magnetic phase of FePt is obtained.

Finite size effects on the metamagnetic phase transition in a thick B2 FeRh nanocluster film.

FeRh alloys in the CsCl-type (B2) chemically ordered phase present an antiferromagnetic to ferromagnetic order transition around 370 K observed in bulk and continuous films but absent in nanoclusters. In this study, we investigate the thermal magnetic behavior of a thick film composed of assembled FeRh nanoclusters preformed in the gas phase. This work reveals a broad and asymmetric metamagnetic transition with a consequent residual magnetization at low temperature. Due to the coexistence of different grain sizes in the sample, we confront the results with a description that involves two populations of B2-FeRh particles, and the existence of a discriminating size below which the magnetic order transition does not take place.

Self-Assembled Permanent Micro-Magnets in a Polymer-Based Microfluidic Device for Magnetic Cell Sorting.

Magnetophoresis-based microfluidic devices offer simple and reliable manipulation of micro-scale objects and provide a large panel of applications, from selective trapping to high-throughput sorting. However, the fabrication and integration of micro-scale magnets in microsystems involve complex and expensive processes. Here we report on an inexpensive and easy-to-handle fabrication process of micrometer-scale permanent magnets, based on the self-organization of NdFeB particles in a polymer matrix (polydimethylsiloxane, PDMS). A study of the inner structure by X-ray tomography revealed a chain-like organization of the particles leading to an array of hard magnetic microstructures with a mean diameter of 4 µm. The magnetic performance of the self-assembled micro-magnets was first estimated by COMSOL simulations. The micro-magnets were then integrated into a microfluidic device where they act as micro-traps. The magnetic forces exerted by the micro-magnets on superparamagnetic beads were measured by colloidal probe atomic force microscopy (AFM) and in operando in the microfluidic system. Forces as high as several nanonewtons were reached. Adding an external millimeter-sized magnet allowed target magnetization and the interaction range to be increased. Then, the integrated micro-magnets were used to study the magnetophoretic trapping efficiency of magnetic beads, providing efficiencies of 100% at 0.5 mL/h and 75% at 1 mL/h. Finally, the micro-magnets were implemented for cell sorting by performing white blood cell depletion.

Cubic chemically ordered FeRh and FeCo nanomagnets prepared by mass-selected low-energy cluster-beam deposition: a comparative study.

Near the point of equiatomic composition, both FeRh and FeCo bulk alloys exhibit a CsCl-type (B2) chemically ordered phase that is related to specific magnetic properties, namely a metamagnetic anti-ferromagnetic/ferromagnetic transition near room temperature for FeRh and a huge magnetic moment for the FeCo soft alloy. In this paper, we present the magnetic and structural properties of nanoparticles of less than 5 nm diameter embedded in an inert carbon matrix prepared by mass-selected low-energy cluster-beam deposition technique. We obtained a CsCl-type (B2) chemically ordered phase for annealed nanoalloys. Using different experimental measurements, we show how decreasing the size affects the magnetic properties. FeRh nanoparticles keep the ferromagnetic order at low temperature due to surface relaxation affecting the cell parameter. In the case of FeCo clusters, the environment drastically affects the intrinsic properties of this system by reducing the magnetization in comparison to the bulk.

Moiré induced organization of size-selected Pt clusters soft landed on epitaxial graphene.

Two-dimensional hexagonal arrays of Pt nanoparticles (1.5 nm diameter) have been obtained by deposition of preformed and size selected Pt nanoparticles on graphene. This original self-organization is induced, at room temperature, by the 2D periodic undulation (the moiré pattern) of graphene epitaxially grown on the Ir(111) surface. By means of complementary techniques (scanning tunneling microscopy, grazing incidence X ray scattering), the Pt clusters shapes and organization are characterized and the structural evolution during annealing is investigated. The soft-landed clusters remain quasi-spherical and a large proportion appears to be pinned on specific moiré sites. The quantitative determination of the proportion of organized clusters reveals that the obtained hexagonal array of the almost spherical nanoparticles is stable up to 650 K, which is an indication of a strong cluster-surface interaction.