Emission ellipsometry used to probe aggregation of the luminescent 2,1,3-benzothiadiazole dyes and ordering in an E7 liquid crystal matrix.

The incorporation of dyes in liquid crystal matrices has been exploited to produce enhanced displays, but it can also be used to probe ordering in liquid crystals and to assess intermolecular interactions and dye aggregation. In this study, we investigated polarized absorption and emission of the luminescent dyes 4,7-bis(2-(4-(decyloxy)phenyl)ethynyl)-[2,1,3]-benzothiadiazole (1A) and 4,7-bis{2-[4-(4-decylpiperazin-1-yl)phenyl]ethynyl}-[2,1,3]-benzothiadiazole (5A) in the E7® liquid crystal. The electronic structures of both 1A and 5A dyes were affected by the matrix and by the analysis of the line shape of emission we could determine that the dyes form J aggregates. This achievement is significant because obtaining this type of information for small molecules requires ordered matrices, which is difficult to obtain for these dyes. Using emission ellipsometry we were able to determine the ordering of the E7 molecules, but this was possible only with the larger 5A dye. The smaller 1A was not entirely ordered in the E7 matrix and this calls for caution in other types of work where dopants are used as probes to infer the properties of the matrix. The emission ellipsometry data for the dyes allowed us to detect the enhanced birefringence in the matrix, thus confirming the theoretical prediction.

Induced secondary structure in nanostructured films of poly(p-phenylene vinylene).

The control of emission properties in luminescent polymers such as poly(p-phenylene vinylene) (PPV) is important for various applications, and may be achieved with suitable molecular architectures in nanostructured films. This paper reports on optical properties of PPV films, using ellipsometry measurements for emitted light in the scope of the Stokes' theory. Organized PPV films obtained with the Langmuir-Blodgett (LB) method exhibited high degree of polarization for the emitted light, while cast films emitted mainly non-polarized light. From ellipsometry data, a secondary structure was inferred for poly(xylylidene tetrahydrothiophenium) chloride (PTHT), a PPV precursor, in solution, which is retained only to a small extent in the PPV cast film as thermal conversion was performed close to the glass transition temperature of PPV. On the other hand, a higher intensity of emitted light with circular polarization was observed for the LB film, which is attributed to PPV molecular secondary structure that was enhanced during the LB film deposition. Circular dichroism experiments were performed to corroborate this hypothesis. It is suggested that such a secondary structure has not been predicted in theoretical models for PPV because possible conformational changes induced in the processing steps are not taken into account.