Valorization of Fly Ashes and Sands Wastes from Biomass Boilers in One-Part Geopolymers.

Fly ash (FA) and exhausted bed sands (sands wastes) that are generated in biomass burners for energy production are two of the wastes generated in the pulp and paper industry. The worldwide production of FA biomass is estimated at 10 million tons/year and is expected to increase. In this context, the present work aims to develop one-part alkali-activated materials with biomass FA (0-100 wt.% of the binder) and sands wastes (100 wt.% of the aggregate). FA from two different boilers, CA and CT, was characterized and the mortar's properties, in the fresh and hardened conditions, were evaluated. Overall, the incorporation of FA decreases the compressive strength of the specimens. However, values higher than 30 MPa are reached with 50 wt.% of FA incorporation. For CA and CT, the compressive strength of mortars with 28 days of curing was 59.2 MPa (0 wt.%), 56.9 and 57.0 MPa (25 wt.%), 34.9 and 46.8 MPa (50 wt.%), 20.5 and 13.5 MPa (75 wt.%), and 9.2 and 0.2 MPa (100 wt.%), respectively. The other evaluated characteristics (density, water absorption, leached components and freeze-thaw resistance) showed no significant differences, except for the specimen with 100 wt.% of CA. Therefore, this work proved that one-part geopolymeric materials with up to 90 wt.% of pulp and paper industrial residues (FA and sand) can be produced, thus reducing the carbon footprint associated with the construction sector.

Waste-Based Pigments for Application in Ceramic Glazes and Stoneware Bodies.

The use of wastes, some of them hazards, as raw materials of ceramic pigments has been a way to diminish their environmental impact, to economically valorize them, and to face the depletion of virgin raw materials. In this work were prepared pigments having in their composition only industrial wastes: Cr/Ni electroplating (ES), and sludges from the cutting of natural stones-marble (MS) and granite (GS). The prepared mixtures were calcined at three temperatures (1100, 1200, and 1300 °C) and the obtained powders were characterized by XRD and UV-vis. Their coloring strength and thermal stability were assessed by adding them to different ceramic substrates: glazes (transparent bright and opaque matte) and a stoneware paste. The CIEL*a*b* coordinates of the fired materials were measured. The developed pigments are thermally stable and exhibit good tinting power, originating nicely colored and defect-free ceramic materials.