RESUMO
Electrochemical transformation of CO2 into energy-dense liquid fuels provides a viable solution to challenges regarding climate change and nonrenewable resource dependence. Here, we report on the modification of a Cr-Ga oxide electrocatalyst through the introduction of nickel to generate a catalyst that generates 1-butanol at unprecedented faradaic efficiencies (ξ = 42%). This faradaic efficiency occurs at -1.48 V vs Ag/AgCl, with 1-butanol production commencing at an overpotential of 320 mV. At this potential, minor products include formate, methanol, acetic acid, acetone, and 3-hydroxybutanal. At -1.0 and -1.4 V, 3-hydroxybutanal becomes the primary product. This is in contrast to the nickel-free (Cr2O3)3(Ga2O3) system, where neither 3-hydroxybutanal nor 1-butanol was detected. Mechanistic studies show that formate is the initial CO2 reduction product and identify acetaldehyde as the key intermediate. Nickel is found responsible for the coupling and reduction of acetaldehyde to generate the higher molecular weight carbon products observed. To the best of our knowledge, this is the first electrocatalyst to generate 1-butanol with high faradaic efficiency.
RESUMO
We report a new HxCrS2-based crystalline/amorphous layered material synthesized by soft chemical methods. We study the structural nature and composition of this material with atomic resolution scanning transmission electron microscopy (STEM), revealing a complex structure consisting of alternating layers of amorphous and crystalline lamellae. Furthermore, the magnetic properties show evidence for increased magnetic frustration compared to the parent compound NaCrS2. Finally, we show that this material can be exfoliated, thus providing a facile synthesis method for chromium-sulfide-based ultrathin layers. The material reported herein can not only be a source of new thin TMD-related sheets for potential application in catalysis but also be of interest for realizing new 2D magnetic materials.