Tunable Release of Ions from Graphene Oxide Laminates for Sustained Antibacterial Activity in a Biomimetic Environment.

Silver has long been recognized for its potent antimicrobial properties, but achieving a slow and longer-term delivery of silver ions presents significant challenges. Previous efforts to control silver ion dosages have struggled to sustain release for extended periods in biomimetic environments, especially in the presence of complex proteins. This challenge is underscored by the absence of technology for sustaining antimicrobial activity, especially in the context of orthopedic implants where long-term efficacy, extending beyond 7 days, is essential. In this study, the tunable, slow, and longer-term release of silver ions from the two-dimensional (2D) nanocapillaries of graphene oxide (GO) laminates incorporated with silver ions (Ag-GO) for antimicrobial applications are successfully demonstrated. To closely mimic a physiologically relevant serum-based environment, a novel in vitro study model using 100% fetal bovine serum (FBS) is introduced as the test medium for microbiology, biocompatibility, and bioactivity studies. To emulate fluid circulation in a physiological environment, the in vitro studies are challenged with serum exchange protocols on different days. The findings show that the Ag-GO coating can sustainably release silver ions at a minimum dosage of 10 µg cm-2 day-1, providing an effective and sustained antimicrobial barrier for over ten days.

Active Sensor for Microwave Tissue Imaging with Bias-Switched Arrays.

A prototype of a bias-switched active sensor was developed and measured to establish the achievable dynamic range in a new generation of active arrays for microwave tissue imaging. The sensor integrates a printed slot antenna, a low-noise amplifier (LNA) and an active mixer in a single unit, which is sufficiently small to enable inter-sensor separation distance as small as 12 mm. The sensor’s input covers the bandwidth from 3 GHz to 7.5 GHz. Its output intermediate frequency (IF) is 30 MHz. The sensor is controlled by a simple bias-switching circuit, which switches ON and OFF the bias of the LNA and the mixer simultaneously. It was demonstrated experimentally that the dynamic range of the sensor, as determined by its ON and OFF states, is 109 dB and 118 dB at resolution bandwidths of 1 kHz and 100 Hz, respectively.

Highly porous phosphate-based glasses for controlled delivery of antibacterial Cu ions prepared via sol-gel chemistry.

Mesoporous glasses are a promising class of bioresorbable biomaterials characterized by high surface area and extended porosity in the range of 2 to 50 nm. These peculiar properties make them ideal materials for the controlled release of therapeutic ions and molecules. Whilst mesoporous silicate-based glasses (MSG) have been widely investigated, much less work has been done on mesoporous phosphate-based glasses (MPG). In the present study, MPG in the P2O5-CaO-Na2O system, undoped and doped with 1, 3, and 5 mol% of Cu ions were synthesized via a combination of the sol-gel method and supramolecular templating. The non-ionic triblock copolymer Pluronic P123 was used as a templating agent. The porous structure was studied via a combination of Scanning Electron Microscopy (SEM), Small-Angle X-ray Scattering (SAXS), and N2 adsorption-desorption analysis at 77 K. The structure of the phosphate network was investigated via solid state 31P Magic Angle Spinning Nuclear Magnetic Resonance (31P MAS-NMR) and Fourier Transform Infrared (FTIR) spectroscopy. Degradation studies, performed in water via Inductively Coupled Plasma-Optical Emission Spectroscopy (ICP-OES), showed that phosphates, Ca2+, Na+ and Cu ions are released in a controlled manner over a 7 days period. The controlled release of Cu, proportional to the copper loading, imbues antibacterial properties to MPG. A significant statistical reduction of Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) bacterial viability was observed over a 3 days period. E. coli appeared to be more resistant than S. aureus to the antibacterial effect of copper. This study shows that copper doped MPG have great potential as bioresorbable materials for controlled delivery of antibacterial ions.

Preparation and characterization of 58S bioactive glass based scaffold with Kaempferol-containing Zein coating for bone tissue engineering.

The aim of this study was to prepare a porous scaffold out of 58S bioactive glass as the bare and coated with Zein to improve mechanical properties and acting as a carrier for Kaempferol controlled delivery. Porosity and morphology, mechanical properties, drug release behavior, bioactivity, cell attachment, and biodegradation of the scaffolds were evaluated accordingly. Obtained results indicated that the scaffolds coated by (7wt/v %) Zein solution, showed the highest mechanical strength (3.06 ± 0.4 MPa) and desirable porous morphology. These scaffolds could support bioactivity, cell attachment, and provide sustained drug release in the safe range of Kaempferol concentration confirmed via 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide analysis. Overall, this study showed that the Zein-coated scaffold possesses superior properties rather than bare scaffold, and the scaffolds coated with 7wt/v % Zein solution could be considered as appropriate scaffolds for bone regeneration.

Mesoporous Phosphate-Based Glasses Prepared via Sol-Gel.

In the present study, a mesoporous phosphate-based glass (MPG) in the P2O5-CaO-Na2O system was synthesized, for the first time, using a combination of sol-gel chemistry and supramolecular templating. A comparison between the structural properties, bioactivity, and biocompatibility of the MPG with a non-porous phosphate-based glass (PG) of analogous composition prepared via the same sol-gel synthesis method but in the absence of a templating surfactant is also presented. Results indicate that the MPG has enhanced bioactivity and biocompatibility compared to the PG, despite having a similar local structure and dissolution properties. In contrast to the PG, the MPG shows formation of hydroxycarbonate apatite (HCA) on its surface after 24 h of immersion in simulated body fluid. Moreover, MPG shows enhanced viability of Saos-2 osteosarcoma cells after 7 days of culturing. This suggests that textural properties (porosity and surface area) play a crucial role in the kinetics of HCA formation and in interaction with cells. Increased efficiency of drug loading and release over non-porous PG systems was proved using the antibiotic tetracycline hydrochloride as a drug model. This study represents a significant advance in the field of mesoporous materials for drug delivery and bone tissue regeneration as it reports, for the first time, the synthesis, structural characterization, and biocompatibility of mesoporous calcium phosphate glasses.

Mesoporous Strontium-Doped Phosphate-Based Sol-Gel Glasses for Biomedical Applications.

Mesoporous phosphate-based glasses have great potential as biomedical materials being able to simultaneously induce tissue regeneration and controlled release of therapeutic molecules. In the present study, a series of mesoporous phosphate-based glasses in the P2O5-CaO-Na2O system, doped with 1, 3, and 5 mol% of Sr2+, were prepared using the sol-gel method combined with supramolecular templating. A sample without strontium addition was prepared for comparison. The non-ionic triblock copolymer EO20PO70EO20 (P123) was used as a templating agent. Scanning electron microscopy (SEM) images revealed that all synthesized glasses have an extended porous structure. This was confirmed by N2 adsorption-desorption analysis at 77 K that shows a porosity typical of mesoporous materials. 31P magic angle spinning nuclear magnetic resonance (31P MAS-NMR) and Fourier transform infrared (FTIR) spectroscopies have shown that the glasses are mainly formed by Q1 and Q2 phosphate groups. Degradation of the glasses in deionized water assessed over a 7-day period shows that phosphate, Ca2+, Na+, and Sr2+ ions can be released in a controlled manner over time. In particular, a direct correlation between strontium content and degradation rate was observed. This study shows that Sr-doped mesoporous phosphate-based glasses have great potential in bone tissue regeneration as materials for controlled delivery of therapeutic ions.

Antibacterial silver-doped phosphate-based glasses prepared by coacervation.

Phosphate-based glasses are materials of great interest for the regeneration and repair of damaged hard or soft tissues. They have the desirable property of slowly dissolving in the physiological environment, eventually being totally replaced by regenerated tissue. Being bioresorbable, they can simultaneously induce tissue regeneration and deliver therapeutic agents (e.g. antibacterial ions) in a controlled way. In this work, we have synthesised a series of glasses in the P2O5-CaO-Na2O system doped with Ag2O using the coacervation method. The addition of silver is known to provide the glass with antibacterial properties due to the release of Ag+ ions into the body fluid. The coacervation method is a facile, water-based technique which offers significant advantages over the conventional melt-quench route for preparing phosphate-based glasses which requires melting of metal oxide powders at high temperatures (1000-1200 °C). The properties of the initial colloidal polyphosphate systems (coacervates) as a function of the Ag2O content were characterised using rheology and liquid state 31P NMR. The effect of Ag+ addition on the final dried glasses was investigated using thermal analysis, Raman spectroscopy and X-ray diffraction. The antibacterial activity was assessed against Staphylococcus aureus (S. aureus), a bacterial strain commonly found in post-surgery infections. A dose-dependent antimicrobial effect was seen with an increasing silver content.

Antibacterial Copper-Doped Calcium Phosphate Glasses for Bone Tissue Regeneration.

Calcium phosphate glasses are a promising new generation of biomaterials that can simultaneously induce tissue regeneration and controlled release of therapeutic molecules. In this work, novel calcium phosphate glasses containing 0, 2, 4, and 6 mol % Cu2+ were synthesized via room temperature precipitation reaction in aqueous solution. The effect of Cu2+ addition on the glass properties and structure was investigated using thermal analysis, 31P solid-state MAS NMR, Raman spectroscopy, and X-ray diffraction. All glasses crystallize at temperature >500 °C and are mainly formed by Q1 groups. The release of P, Ca, and Cu in solution over time was monitored via inductively coupled plasma-optical emission spectroscopy. It was found that with increasing Cu content, the amount of P and Ca released decreases whereas the amount of Cu released increases. The effect of Cu2+ release on the antibacterial activity against S. aureus, a bacterial strain commonly found in postsurgery infections, has been investigated. The addition of copper has been shown to infer the glasses antibacterial properties. As expected, the antibacterial activity of the glasses increases with increasing Cu2+ content. Cytocompatibility was assessed by seeding human osteoblast-like osteosarcoma cells Saos-2 (HTB85) on the glass particles. A significant increase in cell number was observed in all the glasses investigated. The copper-doped calcium phosphate glasses have proven to be multifunctional, as they combine bone regenerative properties with antibacterial activity. Therefore, they have great potential as antibacterial bioresorbable materials for hard tissue regeneration.

Sol-gel synthesis and electrospraying of biodegradable (P2O5)55-(CaO)30-(Na2O)15 glass nanospheres as a transient contrast agent for ultrasound stem cell imaging.

Ultrasound imaging is a powerful tool in medicine because of the millisecond temporal resolution and submillimeter spatial resolution of acoustic imaging. However, the current generation of acoustic contrast agents is primarily limited to vascular targets due to their large size. Nanosize particles have the potential to be used as a contrast agent for ultrasound molecular imaging. Silica-based nanoparticles have shown promise here; however, their slow degradation rate may limit their applications as a contrast agent. Phosphate-based glasses are an attractive alternative with controllable degradation rate and easily metabolized degradation components in the body. In this study, biodegradable P2O5-CaO-Na2O phosphate-based glass nanospheres (PGNs) were synthesized and characterized as contrast agents for ultrasound imaging. The structure of the PGNs was characterized using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), (31)P magic angle spinning nuclear magnetic resonance ((31)P MAS NMR), and Fourier transform infrared (FTIR) spectroscopy. The SEM images indicated a spherical shape with a diameter size range of 200-500 nm. The XRD, (31)P NMR, and FTIR results revealed the amorphous and glassy nature of PGNs that consisted of mainly Q(1) and Q(2) phosphate units. We used this contrast to label mesenchymal stem cells and determined in vitro and in vivo detection limits of 5 and 9 µg/mL, respectively. Cell counts down to 4000 could be measured with ultrasound imaging with no cytoxicity at doses needed for imaging. Importantly, ion-release studies confirmed these PGNs biodegrade into aqueous media with degradation products that can be easily metabolized in the body.

Sol-gel synthesis of quaternary (P2O5)55-(CaO)25-(Na2O)(20-x)-(TiO2) x bioresorbable glasses for bone tissue engineering applications (x = 0, 5, 10, or 15).

In the present study, we report a new and facile sol-gel synthesis of phosphate-based glasses with the general formula of (P2O5)55-(CaO)25-(Na2O)(20-x)-(TiO2) x , where x = 0, 5, 10 or 15, for bone tissue engineering applications. The sol-gel synthesis method allows greater control over glass morphology at relatively low processing temperature (200 °C) in comparison with phosphate-based melt-derived glasses (~1000 °C). The glasses were analyzed using several characterization techniques, including x-ray diffraction (XRD), (31)P magic angle spinning nuclear magnetic resonance ((31)P MAS-NMR), Fourier transform infrared (FTIR) spectroscopy and energy-dispersive x-ray (EDX) spectroscopy, which confirmed the amorphous and glassy nature of the prepared samples. Degradation was assessed by measuring the ion release and pH change of the storage medium. Cytocompatibility was also confirmed by culturing osteoblast-like osteosarcoma cell line MG-63 on the glass microparticles over a seven-day period. Cell attachment to the particles was imaged using scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). The results revealed the potential of phosphate-based sol-gel derived glasses containing 5 or 10 mol% TiO2, with high surface area, ideal dissolution rate for cell attachment and easily metabolized dissolution products, for bone tissue engineering applications.

Strontium- and calcium-containing, titanium-stabilised phosphate-based glasses with prolonged degradation for orthopaedic tissue engineering.

Strontium- and calcium-releasing, titanium-stabilised phosphate-based glasses with a controlled degradation rate are currently under development for orthopaedic tissue engineering applications. Ca and/or Sr were incorporated at varying concentrations in quaternary phosphate-based glasses, in order to promote osteoinduction. Ti was incorporated at a fixed concentration in order to prolong degradation. Glasses of the general formula (P2O5)-(Na2O)-(TiO2)-(CaO)-(SrO) were prepared via the melt-quench technique. The materials were characterised by energy-dispersive X-ray spectroscopy, X-ray diffraction, (31)P magic angle spinning nuclear magnetic resonance, Fourier transform infrared spectroscopy, differential thermal analysis and density determination. The dissolution rate in distilled water was determined by measuring mass loss, ion release and pH change over a two-week period. In addition, the cytocompatibility and alkaline phosphatase activity of an osteoblast-like cell line cultured on the surface of glass discs was assessed. The glasses were shown to be amorphous and contained Q(1), Q(2) and Q(3) species. Fourier transform infrared spectroscopy revealed small changes in the glass structure as Ca was substituted with Sr and differential thermal analysis confirmed a decrease in crystallisation temperature with increasing Sr content. Degradation and ion release studies also showed that mass loss was positively correlated with Sr content. These results were attributed to the lower electronegativity of Sr in comparison to Ca favouring the formation of phosphate-based mineral phases. All compositions supported cell proliferation and survival and induced at least 2.3-fold alkaline phosphatase activity relative to the control. Glass containing 17.5 mol% Sr had 3.6-fold greater alkaline phosphatase activity than the control. The gradual release of Ca and Sr supported osteoinduction, indicating their potential suitability in orthopaedic tissue engineering applications.